General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.54 g/cm³ Show Supplier Material materials with Density of 1.54 g/cm³ | ISO 1183 |
Water content | 23.0 °C | 0.2 % Show Supplier Material materials with Water content of 0.2 % | ISO 15512 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 14 GPa Show Supplier Material materials with Elastic modulus of 14 GPa | ISO 527-2 (1mm/min) |
Elongation | 23.0 °C | 3 % Show Supplier Material materials with Elongation of 3 % | ISO 527-2 (5mm/min) |
Flexural modulus | 23.0 °C | 12.5 GPa Show Supplier Material materials with Flexural modulus of 12.5 GPa | ISO 178 (2mm/min) |
Flexural strength | 23.0 °C | 230 MPa Show Supplier Material materials with Flexural strength of 230 MPa | ISO 178 (2mm/min) |
Impact strength, Charpy notched | -30.0 °C | 12 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 12 kJ/m² | ISO 179/1eA |
23.0 °C | 22 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 22 kJ/m² | ISO 179/1eA | |
Impact strength, Charpy unnotched | 23.0 °C | 120 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 120 kJ/m² | ISO 179/1eU |
Impact strength, Izod notched | -40.0 °C | 11 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 11 kJ/m² | ISO 180/1A |
23.0 °C | 21 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 21 kJ/m² | ISO 180/1A | |
Impact strength, Izod unnotched | 23.0 °C | 115 kJ/m² Show Supplier Material materials with Impact strength, Izod unnotched of 115 kJ/m² | ISO 180/1U |
Tensile strength | 23.0 °C | 175 MPa Show Supplier Material materials with Tensile strength of 175 MPa | ISO 527-2 (5mm/min) |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Ash content | 23.0 °C | 50 % Show Supplier Material materials with Ash content of 50 % | ISO 3451-4 | ||
Heat deflection temperature, 0.45 MPa | 245 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 245 °C | ISO 75-2/B | |||
Heat deflection temperature, 1.80 MPa | 235 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 235 °C | ISO 75-2/A | |||
Melting point | 260 °C Show Supplier Material materials with Melting point of 260 °C | ISO 3146 | |||
Flammability | UL94 (0.8mm) HB |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 600 V Show Supplier Material materials with Comparative tracking index of 600 V | EN 60112 |
Surface resistivity | 23.0 °C | 1.00E+14 Ω/sq Show Supplier Material materials with Surface resistivity of 1.00E+14 Ω/sq | ASTM D257 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Application areas | Eplamid 66 glass fiber and impact modified grades are used in all sectors of industry, offering a good impact strength for mechanical properties and ensures an outstanding performance even at low temperatures (up to -40°C). | |
Fillers | 50% Glass Fiber | |
Other | Laboratory conditions are 23 ±2°C and 45-55 % RH. |