EPLAMID 66 GX0 30 NC Q1D0B801 (PA66)

Alternative and trade names
PA66-GF30 FR(40)
Want to keep this datasheet? Save it now in your required format

Description

Flame retardant polyamide 66 reinforced with 30% glass fiber, heat stabilized for injection molding.

Halogen free flame retardant grades, compliance with RoHS derivatives, with rating UL94 V0 and glow-wire at 960°C, which is used in many sectors of industy and has excellent mechanical properties.

This material data has been provided by Epsan.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueTemperatureComment

Density

1.41 g/cm³

Show Supplier Material materials with Density of 1.41 g/cm³ at 23.0 °C

23.0 °C

ISO 1183

Water content

0.2 %

Show Supplier Material materials with Water content of 0.2 % at 23.0 °C

23.0 °C

ISO 15512

Mechanical

PropertyValueTemperatureComment

Elastic modulus

10.5 GPa

Show Supplier Material materials with Elastic modulus of 10.5 GPa at 23.0 °C

23.0 °C

ISO 527-2 (1mm/min)

Elongation

2.5 %

Show Supplier Material materials with Elongation of 2.5 % at 23.0 °C

23.0 °C

ISO 527-2 (5mm/min)

Flexural modulus

9 GPa

Show Supplier Material materials with Flexural modulus of 9 GPa at 23.0 °C

23.0 °C

ISO 178 (2mm/min)

Flexural strength

190 MPa

Show Supplier Material materials with Flexural strength of 190 MPa at 23.0 °C

23.0 °C

ISO 178 (2mm/min)

Impact strength, Charpy notched

9 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 9 kJ/m² at 23.0 °C

23.0 °C

ISO 179/1eA

Impact strength, Charpy unnotched

60 kJ/m²

Show Supplier Material materials with Impact strength, Charpy unnotched of 60 kJ/m² at 23.0 °C

23.0 °C

ISO 179/1eU

Impact strength, Izod notched

8 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 8 kJ/m² at 23.0 °C

23.0 °C

ISO 180/1A

Impact strength, Izod unnotched

55 kJ/m²

Show Supplier Material materials with Impact strength, Izod unnotched of 55 kJ/m² at 23.0 °C

23.0 °C

ISO 180/1U

Tensile strength

130 MPa

Show Supplier Material materials with Tensile strength of 130 MPa at 23.0 °C

23.0 °C

ISO 527-2 (5mm/min)

Thermal

PropertyValueTemperatureComment

Ash content

30 %

Show Supplier Material materials with Ash content of 30 % at 23.0 °C

23.0 °C

ISO 3451-4

Ball Pressure Test

<2, for 125+/-2°C, EN 60695-10-2

Flammability

UL94 (0.8mm) V0

Heat deflection temperature, 0.45 MPa

250 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 250 °C

ISO 75-2/B

Heat deflection temperature, 1.80 MPa

225 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 225 °C

ISO 75-2/A

Melting point

260 °C

Show Supplier Material materials with Melting point of 260 °C

ISO 3146

Electrical

PropertyValueTemperatureComment

Comparative tracking index

600 V

Show Supplier Material materials with Comparative tracking index of 600 V at 23.0 °C

23.0 °C

EN 60112

Surface resistivity

1.00E+14 Ω/sq

Show Supplier Material materials with Surface resistivity of 1.00E+14 Ω/sq at 23.0 °C

23.0 °C

ASTM D257

Rheological Properties

PropertyValueTemperatureComment

Shrinkage

0.3 %

Show Supplier Material materials with Shrinkage of 0.3 % at 23.0 °C

23.0 °C

ISO 294-4 (3mm)

Shrinkage, transverse

0.9 %

Show Supplier Material materials with Shrinkage, transverse of 0.9 % at 23.0 °C

23.0 °C

ISO 294-4 (3mm)

Technological properties

Property
Application areas

Halogen free flame retardant grades, compliance with RoHS derivatives, with rating UL94 V0 and glow-wire at 960°C, which is used in many sectors of industy and has excellent mechanical properties.

Certifications

RoHS

Fillers

30% Glass Fiber

Other

Laboratory conditions are 23 ±2°C and 45-55 % RH.