Polyphthalamide (PPA) HT03 GFR 40 BK Q1E001

Alternative and trade names
PA66/6I/X-GF40
Want to keep this datasheet? Save it now in your required format

Description

Partially Aromatic copolyamide with a combination of semi-crystalline polyamide reinforced with 40% Glass fiber, heat stabilized and lubricated for injection molding process.

Eplamid HT03 grades offer the following unique properties in general conditions, and even after moisture absorption: Good Surface Finish, Good Dimensional Stability, Good High Temperature Properties, Good Chemical Resistance to Glycols and Oils and Excellent Creep Resistance. Eplamid HT03 grades are used for molding technical parts where higher operating temperatures and higher stiffness in moist environments are required.

This material data has been provided by Epsan.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueTemperatureComment

Density

1.46 g/cm³

Show Supplier Material materials with Density of 1.46 g/cm³ at 23.0 °C

23.0 °C

ISO 1183

Water content

0.1 %

Show Supplier Material materials with Water content of 0.1 % at 23.0 °C

23.0 °C

ISO 15512

Mechanical

PropertyValueTemperatureComment

Elastic modulus

14 GPa

Show Supplier Material materials with Elastic modulus of 14 GPa at 23.0 °C

23.0 °C

ISO 527-2 (1mm/min)

Elongation

3 %

Show Supplier Material materials with Elongation of 3 % at 23.0 °C

23.0 °C

ISO 527-2 (5mm/min)

Hardness, Ball Indentation

255 MPa

Show Supplier Material materials with Hardness, Ball Indentation of 255 MPa at 23.0 °C

23.0 °C

ISO 2039-1

Impact strength, Charpy notched

10 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 10 kJ/m² at -30.0 °C

-30.0 °C

ISO 179/1eA

11 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 11 kJ/m² at 23.0 °C

23.0 °C

ISO 179/1eA

Impact strength, Charpy unnotched

70 kJ/m²

Show Supplier Material materials with Impact strength, Charpy unnotched of 70 kJ/m² at 23.0 °C

23.0 °C

ISO 179/1eU

Tensile strength

210 MPa

Show Supplier Material materials with Tensile strength of 210 MPa at 23.0 °C

23.0 °C

ISO 527-2 (5mm/min)

Thermal

PropertyValueTemperatureComment

Ash content

40 %

Show Supplier Material materials with Ash content of 40 % at 23.0 °C

23.0 °C

ISO 3451-4

Flammability

UL94 (0.8mm) HB

Heat deflection temperature, 1.80 MPa

230 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 230 °C

ISO 75-2/A

Heat deflection temperature, 8.0 MPa

105 °C

Show Supplier Material materials with Heat deflection temperature, 8.0 MPa of 105 °C

ISO 75-2/B

Max service temperature, long

110 °C

Show Supplier Material materials with Max service temperature, long of 110 °C

ISO 2578

Max service temperature, short

215 °C

Show Supplier Material materials with Max service temperature, short of 215 °C

ISO 2578

Melting point

260 °C

Show Supplier Material materials with Melting point of 260 °C

ISO 3146

Electrical

PropertyValueTemperatureComment

Comparative tracking index

600 V

Show Supplier Material materials with Comparative tracking index of 600 V at 23.0 °C

23.0 °C

EN 60112

Dielectric strength

33 kV/mm

Show Supplier Material materials with Dielectric strength of 33 kV/mm at 23.0 °C

23.0 °C

IEC 60243-1

Rheological Properties

PropertyValueTemperatureComment

Shrinkage

0.1 %

Show Supplier Material materials with Shrinkage of 0.1 % at 23.0 °C

23.0 °C

ISO 294-4 (3mm)

Shrinkage, transverse

0.6 %

Show Supplier Material materials with Shrinkage, transverse of 0.6 % at 23.0 °C

23.0 °C

ISO 294-4 (3mm)

Technological properties

Property
Application areas

Eplamid HT03 grades are used for molding technical parts where higher operating temperatures and higher stiffness in moist environments are required.

Fillers

40% Glass Fiber

Other

Laboratory conditions are 23 ±2°C and 45-55 % RH.