EPLAMID 6 CBR 40 NC Q1E001 (PA6)

Alternative and trade names
PA6-GB40
Want to keep this datasheet? Save it now in your required format

Description

Polyamide 6 reinforced with 40 % of glass spheres, heat stabilized and lubricated for injection moulding.

Eplamid 6 glass sphere reinforced grades offer a good surface finish, low warpage and good dimensional stability which are used in many sectors of industry.

This material data has been provided by Epsan.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.44 g/cm³

Show Supplier Material materials with Density of 1.44 g/cm³

ISO 1183

Water content

23.0 °C

0.2 %

Show Supplier Material materials with Water content of 0.2 %

ISO 15512

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

4.8 GPa

Show Supplier Material materials with Elastic modulus of 4.8 GPa

ISO 527-2 (1mm/min)

Elongation

23.0 °C

4 %

Show Supplier Material materials with Elongation of 4 %

ISO 527-2 (5mm/min)

Flexural modulus

23.0 °C

4.2 GPa

Show Supplier Material materials with Flexural modulus of 4.2 GPa

ISO 178 (2mm/min)

Flexural strength

23.0 °C

120 MPa

Show Supplier Material materials with Flexural strength of 120 MPa

ISO 178 (2mm/min)

Impact strength, Charpy notched

23.0 °C

7 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 7 kJ/m²

ISO 179/1eA

Impact strength, Charpy unnotched

23.0 °C

60 kJ/m²

Show Supplier Material materials with Impact strength, Charpy unnotched of 60 kJ/m²

ISO 179/1eU

Impact strength, Izod notched

23.0 °C

6 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 6 kJ/m²

ISO 180/1A

Impact strength, Izod unnotched

23.0 °C

45 kJ/m²

Show Supplier Material materials with Impact strength, Izod unnotched of 45 kJ/m²

ISO 180/1U

Tensile strength

23.0 °C

80 MPa

Show Supplier Material materials with Tensile strength of 80 MPa

ISO 527-2 (5mm/min)

Thermal

PropertyTemperatureValueComment

Ash content

23.0 °C

40 %

Show Supplier Material materials with Ash content of 40 %

ISO 3451-4

Heat deflection temperature, 0.45 MPa

215 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 215 °C

ISO 75-2/B

Heat deflection temperature, 1.80 MPa

90 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 90 °C

ISO 75-2/A

Melting point

215 °C

Show Supplier Material materials with Melting point of 215 °C

ISO 3146

Flammability

UL94 (0.8mm) HB, EN 60695-11-10

Electrical

PropertyTemperatureValueComment

Comparative tracking index

23.0 °C

550 V

Show Supplier Material materials with Comparative tracking index of 550 V

EN 60112

Surface resistivity

23.0 °C

1.00E+13 Ω/sq

Show Supplier Material materials with Surface resistivity of 1.00E+13 Ω/sq

ASTM D257

Rheological Properties

PropertyTemperatureValueComment

Shrinkage

23.0 °C

0.6 %

Show Supplier Material materials with Shrinkage of 0.6 %

ISO 294-4 (3mm)

Shrinkage, transverse

23.0 °C

0.9 %

Show Supplier Material materials with Shrinkage, transverse of 0.9 %

ISO 294-4 (3mm)

Technological properties

Property
Application areas

Eplamid 6 glass sphere reinforced grades offer a good surface finish, low warpage and good dimensional stability which are used in many sectors of industry.

Fillers

40% Glass Bead

Other

Laboratory conditions are 23 ±2°C and 45-55 % RH.