EPLAMID 6 CFR 10 BK Q1B001 (PA6)

Alternative and trade names
PA6-CF10
Want to keep this datasheet? Save it now in your required format

Description

Polyamide 6, reinforced with 10% of carbon fiber, heat stabilized, lubricated for injection moulding.

Eplamid 6 carbon fiber reinforced compounds are used in all sectors of industry, offering a good balance of thermal and mechanical properties.

This material data has been provided by Epsan.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.17 g/cm³

Show Supplier Material materials with Density of 1.17 g/cm³

ISO 1183

Water content

23.0 °C

0.1 %

Show Supplier Material materials with Water content of 0.1 %

ISO 15512

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

8.5 GPa

Show Supplier Material materials with Elastic modulus of 8.5 GPa

ISO 527-2 (1mm/min)

Elongation

23.0 °C

2 %

Show Supplier Material materials with Elongation of 2 %

ISO 527-2 (5mm/min)

Flexural modulus

23.0 °C

7 GPa

Show Supplier Material materials with Flexural modulus of 7 GPa

ISO 178 (2mm/min)

Flexural strength

23.0 °C

210 MPa

Show Supplier Material materials with Flexural strength of 210 MPa

ISO 178 (2mm/min)

Impact strength, Charpy notched

23.0 °C

6 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 6 kJ/m²

ISO 179/1eA

Impact strength, Charpy unnotched

23.0 °C

30 kJ/m²

Show Supplier Material materials with Impact strength, Charpy unnotched of 30 kJ/m²

ISO 179/1eU

Impact strength, Izod notched

23.0 °C

5 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 5 kJ/m²

ISO 180/1A

Impact strength, Izod unnotched

23.0 °C

25 kJ/m²

Show Supplier Material materials with Impact strength, Izod unnotched of 25 kJ/m²

ISO 180/1U

Tensile strength

23.0 °C

120 MPa

Show Supplier Material materials with Tensile strength of 120 MPa

ISO 527-2 (5mm/min)

Thermal

PropertyTemperatureValueComment

Ash content

23.0 °C

10 %

Show Supplier Material materials with Ash content of 10 %

ISO 3451-4

Heat deflection temperature, 0.45 MPa

210 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 210 °C

ISO 75-2/B

Heat deflection temperature, 1.80 MPa

190 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 190 °C

ISO 75-2/A

Melting point

220 °C

Show Supplier Material materials with Melting point of 220 °C

ISO 3146

Flammability

UL94 (0.8mm) HB, EN 60695-11-10

Electrical

PropertyTemperatureValueComment

Surface resistivity

23.0 °C

1000000 Ω/sq

Show Supplier Material materials with Surface resistivity of 1000000 Ω/sq

ASTM D257

Rheological Properties

PropertyTemperatureValueComment

Shrinkage

23.0 °C

0.5 %

Show Supplier Material materials with Shrinkage of 0.5 %

ISO 294-4 (3mm)

Shrinkage, transverse

23.0 °C

0.8 %

Show Supplier Material materials with Shrinkage, transverse of 0.8 %

ISO 294-4 (3mm)

Technological properties

Property
Application areas

Eplamid 6 carbon fiber reinforced compounds are used in all sectors of industry, offering a good balance of thermal and mechanical properties.

Fillers

10% Carbon Fiber

Other

Laboratory conditions are 23 ±2°C and 45-55 % RH.