Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.42 g/cm³ Show Supplier Material materials with Density of 1.42 g/cm³ | ISO 1183 |
Water content | 23.0 °C | 0.1 % Show Supplier Material materials with Water content of 0.1 % | ISO 15512 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 11.4 GPa Show Supplier Material materials with Elastic modulus of 11.4 GPa | ISO 527-2 (1mm/min) |
Elongation | 23.0 °C | 3 % Show Supplier Material materials with Elongation of 3 % | ISO 527-2 (5mm/min) |
Hardness, Ball Indentation | 23.0 °C | 240 MPa Show Supplier Material materials with Hardness, Ball Indentation of 240 MPa | ISO 2039-1 |
Impact strength, Charpy notched | -30.0 °C | 7 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 7 kJ/m² | ISO 179/1eA |
23.0 °C | 8 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 8 kJ/m² | ISO 179/1eA | |
Impact strength, Charpy unnotched | 23.0 °C | 85 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 85 kJ/m² | ISO 179/1eU |
Tensile strength | 23.0 °C | 190 MPa Show Supplier Material materials with Tensile strength of 190 MPa | ISO 527-2 (5mm/min) |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Ash content | 23.0 °C | 30 % Show Supplier Material materials with Ash content of 30 % | ISO 3451-4 | ||
Heat deflection temperature, 1.80 MPa | 280 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 280 °C | ISO 75-2/A | |||
Heat deflection temperature, 8.0 MPa | 150 °C Show Supplier Material materials with Heat deflection temperature, 8.0 MPa of 150 °C | ISO 75-2/B | |||
Max service temperature, long | 140 °C Show Supplier Material materials with Max service temperature, long of 140 °C | ISO 2578 | |||
Max service temperature, short | 250 °C Show Supplier Material materials with Max service temperature, short of 250 °C | ISO 2578 | |||
Melting point | 310 °C Show Supplier Material materials with Melting point of 310 °C | ISO 3146 | |||
Flammability | UL94 (0.8mm) HB |
Electrical
Rheological Properties
Technological properties
Property | ||
---|---|---|
Application areas | Eplamid HT02 grades are used for molding technical parts where higher operating temperatures and higher stiffness in moist environments are required. | |
Fillers | 30% Glass Fiber | |
Other | Laboratory conditions are 23 ±2°C and 45-55 % RH. |