Polyphthalamide (PPA) HT02 GFR 45 BK Q1E501

Alternative and trade names
PA6T/66-GF45
Want to keep this datasheet? Save it now in your required format

Description

Partially Aromatic copolyamide with a combination of semi-crystalline polyamide reinforced with 45% Glass fiber, heat stabilized and lubricated for injection molding process.

Eplamid HT02 grades offer the following unique properties in general conditions, and even after moisture absorption: Good Surface Finish, Good Dimensional Stability, Good High Temperature Properties, Good Chemical Resistance to Glycols and Oils and Excellent Creep Resistance. Eplamid HT02 grades are used for molding technical parts where higher operating temperatures and higher stiffness in moist environments are required.

This material data has been provided by Epsan.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.56 g/cm³

Show Supplier Material materials with Density of 1.56 g/cm³

ISO 1183

Water content

23.0 °C

0.1 %

Show Supplier Material materials with Water content of 0.1 %

ISO 15512

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

17.3 GPa

Show Supplier Material materials with Elastic modulus of 17.3 GPa

ISO 527-2 (1mm/min)

Elongation

23.0 °C

2.5 %

Show Supplier Material materials with Elongation of 2.5 %

ISO 527-2 (5mm/min)

Hardness, Ball Indentation

23.0 °C

260 MPa

Show Supplier Material materials with Hardness, Ball Indentation of 260 MPa

ISO 2039-1

Impact strength, Charpy notched

-30.0 °C

11 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 11 kJ/m²

ISO 179/1eA

23.0 °C

12 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 12 kJ/m²

ISO 179/1eA

Impact strength, Charpy unnotched

23.0 °C

90 kJ/m²

Show Supplier Material materials with Impact strength, Charpy unnotched of 90 kJ/m²

ISO 179/1eU

Tensile strength

23.0 °C

235 MPa

Show Supplier Material materials with Tensile strength of 235 MPa

ISO 527-2 (5mm/min)

Thermal

PropertyTemperatureValueComment

Ash content

23.0 °C

45 %

Show Supplier Material materials with Ash content of 45 %

ISO 3451-4

Heat deflection temperature, 1.80 MPa

295 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 295 °C

ISO 75-2/A

Heat deflection temperature, 8.0 MPa

150 °C

Show Supplier Material materials with Heat deflection temperature, 8.0 MPa of 150 °C

ISO 75-2/B

Max service temperature, long

140 °C

Show Supplier Material materials with Max service temperature, long of 140 °C

ISO 2578

Max service temperature, short

250 °C

Show Supplier Material materials with Max service temperature, short of 250 °C

ISO 2578

Melting point

310 °C

Show Supplier Material materials with Melting point of 310 °C

ISO 3146

Flammability

UL94 (0.8mm) HB

Electrical

PropertyTemperatureValueComment

Comparative tracking index

23.0 °C

600 V

Show Supplier Material materials with Comparative tracking index of 600 V

EN 60112

Dielectric strength

23.0 °C

40 kV/mm

Show Supplier Material materials with Dielectric strength of 40 kV/mm

IEC 60243-1

Rheological Properties

PropertyTemperatureValueComment

Shrinkage

23.0 °C

0.1 %

Show Supplier Material materials with Shrinkage of 0.1 %

ISO 294-4 (3mm)

Shrinkage, transverse

23.0 °C

0.6 %

Show Supplier Material materials with Shrinkage, transverse of 0.6 %

ISO 294-4 (3mm)

Technological properties

Property
Application areas

Eplamid HT02 grades are used for molding technical parts where higher operating temperatures and higher stiffness in moist environments are required.

Fillers

45% Glass Fiber

Other

Laboratory conditions are 23 ±2°C and 45-55 % RH.