EPLAMID 6 HSL NC Q201 (PA6)

Want to keep this datasheet? Save it now in your required format

Description

Unfilled polyamide 6, heat-aging stabilized, externally and internally lubricated for injection applications.

Eplamid 6 offers all primary properties of unreinforced polyamide 6 used with high viscosity and production of films and monofilaments in all sectors of industry, good balance of thermal and mechanical properties.

This material data has been provided by Epsan.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.14 g/cm³

Show Supplier Material materials with Density of 1.14 g/cm³

ISO 1183

Water content

23.0 °C

0.1 %

Show Supplier Material materials with Water content of 0.1 %

ISO 15512

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

3.2 GPa

Show Supplier Material materials with Elastic modulus of 3.2 GPa

ISO 527-2 (1mm/min)

Elongation

23.0 °C

20 %

Show Supplier Material materials with Elongation of 20 %

ISO 527-2 (5mm/min)

Flexural modulus

23.0 °C

2.9 GPa

Show Supplier Material materials with Flexural modulus of 2.9 GPa

ISO 178 (2mm/min)

Flexural strength

23.0 °C

110 MPa

Show Supplier Material materials with Flexural strength of 110 MPa

ISO 178 (2mm/min)

Impact strength, Charpy notched

23.0 °C

10 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 10 kJ/m²

Max; ISO 179/1eA

Impact strength, Izod notched

23.0 °C

10 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 10 kJ/m²

Max; ISO 180/1A

Tensile strength

23.0 °C

80 MPa

Show Supplier Material materials with Tensile strength of 80 MPa

ISO 527-2 (5mm/min)

Impact strength, Charpy unnotched

no break at 23°C; ISO 179/1eU

Impact strength, Izod unnotched

no break at 23°C; ISO 180/1U

Thermal

PropertyValueComment

Heat deflection temperature, 0.45 MPa

160 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 160 °C

ISO 75-2/B

Heat deflection temperature, 1.80 MPa

55 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 55 °C

ISO 75-2/A

Melting point

222 °C

Show Supplier Material materials with Melting point of 222 °C

ISO 3146

Flammability

UL94 (0.8mm) V2, EN 60695-11-10

Electrical

PropertyTemperatureValueComment

Comparative tracking index

23.0 °C

600 V

Show Supplier Material materials with Comparative tracking index of 600 V

EN 60112

Surface resistivity

23.0 °C

1.00E+13 Ω/sq

Show Supplier Material materials with Surface resistivity of 1.00E+13 Ω/sq

ASTM D257

Rheological Properties

PropertyTemperatureValueComment

Shrinkage

23.0 °C

1 %

Show Supplier Material materials with Shrinkage of 1 %

ISO 294-4 (3mm)

Shrinkage, transverse

23.0 °C

1.2 %

Show Supplier Material materials with Shrinkage, transverse of 1.2 %

ISO 294-4 (3mm)

Technological properties

Property
Application areas

Eplamid 6 offers all primary properties of unreinforced polyamide 6 used with high viscosity and production of films and monofilaments in all sectors of industry, good balance of thermal and mechanical properties.

Other

Laboratory conditions are 23 ±2°C and 45-55 % RH.