Properties
General
| Property | Value | Comment |
|---|---|---|
Density | 1.14 g/cm³ Show Supplier Material materials with Density of 1.14 g/cm³ | OECD 109 (neat resin) |
Mechanical
| Property | Value | Comment |
|---|---|---|
Elastic modulus | 2.93 GPa Show Supplier Material materials with Elastic modulus of 2.93 GPa | DIN EN ISO 527-2 (neat resin) |
Elongation | 6.0 % Show Supplier Material materials with Elongation of 6.0 % | DIN EN ISO 527-2 (neat resin) |
Flexural modulus | 2.91 GPa Show Supplier Material materials with Flexural modulus of 2.91 GPa | DIN EN ISO 178 (neat resin) |
Flexural strain | 7.0 % Show Supplier Material materials with Flexural strain of 7.0 % | DIN EN ISO 178 (neat resin) |
Flexural strength | 120.0 MPa Show Supplier Material materials with Flexural strength of 120.0 MPa | DIN EN ISO 178 (neat resin) |
Tensile strength | 80.0 MPa Show Supplier Material materials with Tensile strength of 80.0 MPa | DIN EN ISO 527-2 (neat resin) |
Thermal
| Property | Value | Comment |
|---|---|---|
Gel time | 350 sec Show Supplier Material materials with Gel time of 350 sec | Geltimer (Plate) at 140°C |
450 sec Show Supplier Material materials with Gel time of 450 sec | Geltimer (Plate) at 140°C | |
Glass transition temperature | 120.0 °C Show Supplier Material materials with Glass transition temperature of 120.0 °C | DIN EN ISO 11357-2 (neat resin) |
Rheological Properties
| Property | Value | Comment |
|---|---|---|
Viscosity | 0.5 Pa·s Show Supplier Material materials with Viscosity of 0.5 Pa·s | (neat resin) |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Semi-structural parts, Supporting structures, structural lightweight applications, Exterior / Interior parts | |