VESTALITE® S 102 (for cured SMC)

Alternative and trade names
VESTALITE® S 102 (for cured SMC)
Want to keep this datasheet? Save it now in your required format

Description

VESTALITE® S 102 is a curing agent for epoxy resin matrix designed for SMC applications. Systems using VESTALITE® S 102 have a low initial viscosity during compounding, allowing excellent fiber wetting, high fiber volume fraction and efficient processing. The high reactivity of the hardener allows fast curing in about 3 min at 150 °C.

This material data has been provided by Evonik Industries AG.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

Mechanical

PropertyValueConditionComment

Compressive modulus

35100.0 MPa

Show Supplier Material materials with Compressive modulus of 35100.0 MPa

The properties of cured SMC material (68.1 % carbon fiber mass fraction)

EN ISO 14126 (cured SMC material)

Compressive strength

323.0 MPa

Show Supplier Material materials with Compressive strength of 323.0 MPa

The properties of cured SMC material (68.1 % carbon fiber mass fraction)

EN ISO 14126 (cured SMC material)

Elastic modulus

44.0 GPa

Show Supplier Material materials with Elastic modulus of 44.0 GPa

The properties of cured SMC material (68.1 % carbon fiber mass fraction)

DIN EN ISO 527-4 (cured SMC material)

Elongation

0.7 %

Show Supplier Material materials with Elongation of 0.7 %

The properties of cured SMC material (68.1 % carbon fiber mass fraction)

DIN EN ISO 527-4 (cured SMC material)

Flexural modulus

39.0 GPa

Show Supplier Material materials with Flexural modulus of 39.0 GPa

The properties of cured SMC material (68.1 % carbon fiber mass fraction)

EN ISO 14125 (cured SMC material)

Flexural strain

1.8 %

Show Supplier Material materials with Flexural strain of 1.8 %

The properties of cured SMC material (68.1 % carbon fiber mass fraction)

EN ISO 14125 (cured SMC material)

Flexural strength

545.0 MPa

Show Supplier Material materials with Flexural strength of 545.0 MPa

The properties of cured SMC material (68.1 % carbon fiber mass fraction)

EN ISO 14125 (cured SMC material)

Impact strength, Charpy unnotched

107.0 kJ/m²

Show Supplier Material materials with Impact strength, Charpy unnotched of 107.0 kJ/m²

The properties of cured SMC material (68.1 % carbon fiber mass fraction)

EN ISO 179-1 (cured SMC material)

Tensile strength

263.0 MPa

Show Supplier Material materials with Tensile strength of 263.0 MPa

The properties of cured SMC material (68.1 % carbon fiber mass fraction)

DIN EN ISO 527-4 (cured SMC material)

Rheological Properties

PropertyValueConditionComment

Viscosity

0.5 Pa·s

Show Supplier Material materials with Viscosity of 0.5 Pa·s

The properties of cured SMC material (68.1 % carbon fiber mass fraction)

(neat resin)

Technological properties

Property
Application areas

Semi-structural parts, Supporting structures, structural lightweight applications, Exterior / Interior parts

Fillers

Carbon Fiber

Processing methods

The molding condition for SMC sheets: Molding pressure: 100-200 bar, Molding temperature: 150°C, Molding coverage: 50-80% and Curing time: 3-4 minutes