VESTALITE® S 102 (for neat resin)

Alternative and trade names
VESTALITE® S 102 (for neat resin)
Want to keep this datasheet? Save it now in your required format

Description

VESTALITE® S 102 is a curing agent for epoxy resin matrix designed for SMC applications. Systems using VESTALITE® S 102 have a low initial viscosity during compounding, allowing excellent fiber wetting, high fiber volume fraction and efficient processing. The high reactivity of the hardener allows fast curing in about 3 min at 150 °C.

This material data has been provided by Evonik Industries AG.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueTemperatureComment

Density

1.14 g/cm³

Show Supplier Material materials with Density of 1.14 g/cm³ at 23.0 °C

23.0 °C

OECD 109 (neat resin)

Viscosity

0.5 Pa·s

Show Supplier Material materials with Viscosity of 0.5 Pa·s at 23.0 °C

23.0 °C

(neat resin)

Mechanical

PropertyValueTemperatureComment

Elastic modulus

2.93 GPa

Show Supplier Material materials with Elastic modulus of 2.93 GPa at 23.0 °C

23.0 °C

DIN EN ISO 527-2 (neat resin)

Elongation

6 %

Show Supplier Material materials with Elongation of 6 % at 23.0 °C

23.0 °C

DIN EN ISO 527-2 (neat resin)

Flexural modulus

2.91 GPa

Show Supplier Material materials with Flexural modulus of 2.91 GPa at 23.0 °C

23.0 °C

DIN EN ISO 178 (neat resin)

Flexural strain

7 %

Show Supplier Material materials with Flexural strain of 7 % at 23.0 °C

23.0 °C

DIN EN ISO 178 (neat resin)

Flexural strength

120 MPa

Show Supplier Material materials with Flexural strength of 120 MPa at 23.0 °C

23.0 °C

DIN EN ISO 178 (neat resin)

Tensile strength

80 MPa

Show Supplier Material materials with Tensile strength of 80 MPa at 23.0 °C

23.0 °C

DIN EN ISO 527-2 (neat resin)

Thermal

PropertyValueComment

Glass transition temperature

120 °C

Show Supplier Material materials with Glass transition temperature of 120 °C

DIN EN ISO 11357-2 (neat resin)

Technological properties

Property
Application areas

Semi-structural parts, Supporting structures, structural lightweight applications, Exterior / Interior parts