BioBlend® XP 24875

Alternative and trade names
BioBlend® XP 24875
Want to keep this datasheet? Save it now in your required format

Description

One of the BioBlend® XP family of high performance BioPolymers designed for blown film applications. BioBlend® XP 24875 is a masterbatch that contains 50% NuPlastiQ GP BioPolymer compounded with polyethylene. Made from 50% annually renewable agricultural resources. Mechanical properties were measured on injection molded parts made directly from the 50% NuPlastiQ / 50% polyethylene masterbatch.

This material data has been provided by Feconix Pte Ltd.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueTemperatureComment

Density

1.17 g/cm³

Show Supplier Material materials with Density of 1.17 g/cm³ at 23.0 °C

23.0 °C

Calculated

Mechanical

PropertyValueTemperatureComment

Elastic modulus

0.57 GPa

Show Supplier Material materials with Elastic modulus of 0.57 GPa at 23.0 °C

23.0 °C

ASTM D638

Elongation

12 %

Show Supplier Material materials with Elongation of 12 % at 23.0 °C

23.0 °C

ASTM D638

Flexural modulus

0.71 GPa

Show Supplier Material materials with Flexural modulus of 0.71 GPa at 23.0 °C

23.0 °C

ASTM D790

Impact strength, Izod notched, ASTM

47 J/m

Show Supplier Material materials with Impact strength, Izod notched, ASTM of 47 J/m at 23.0 °C

23.0 °C

ASTM D256

Tensile strength

19 MPa

Show Supplier Material materials with Tensile strength of 19 MPa at 23.0 °C

23.0 °C

ASTM D638

Thermal

PropertyValueComment

Melting point

130 °C

Show Supplier Material materials with Melting point of 130 °C

ASTM D3418

Rheological Properties

PropertyValueComment

Melt mass-flow rate

0.56 g/10min

Show Supplier Material materials with Melt mass-flow rate of 0.56 g/10min

ASTM D1238 (190°C/5 kg)

Technological properties

Property
Application areas

Used for final products requiring strength and plasticity, such as packaging.