Properties
General
| Property | Value |
|---|---|
Relative density | 8.89 [-] Show Supplier Material materials with Relative density of 8.89 [-] |
Mechanical
| Property | Value | Comment |
|---|---|---|
Bendability 90°, bw | 0 [-] Show Supplier Material materials with Bendability 90°, bw of 0 [-] | O Temper | Ts=280 N/mm2 |
0 [-] Show Supplier Material materials with Bendability 90°, bw of 0 [-] | 1/4H Temper | Ts=298 N/mm2 | |
1 [-] Show Supplier Material materials with Bendability 90°, bw of 1 [-] | 1/2H Temper | Ts=354 N/mm2 | |
1.5 [-] Show Supplier Material materials with Bendability 90°, bw of 1.5 [-] | H Temper | Ts=409 N/mm2 | |
2 [-] Show Supplier Material materials with Bendability 90°, bw of 2 [-] | EH Temper | Ts=484 N/mm2 | |
Bendability 90°, gw | 0 [-] Show Supplier Material materials with Bendability 90°, gw of 0 [-] | O Temper | Ts=280 N/mm2 |
0 [-] Show Supplier Material materials with Bendability 90°, gw of 0 [-] | 1/4H Temper | Ts=298 N/mm2 | |
0 [-] Show Supplier Material materials with Bendability 90°, gw of 0 [-] | 1/2H Temper | Ts=354 N/mm2 | |
0 [-] Show Supplier Material materials with Bendability 90°, gw of 0 [-] | H Temper | Ts=409 N/mm2 | |
1.3 [-] Show Supplier Material materials with Bendability 90°, gw of 1.3 [-] | EH Temper | Ts=484 N/mm2 | |
Elastic modulus | 110 GPa Show Supplier Material materials with Elastic modulus of 110 GPa | |
Elongation | 3 % Show Supplier Material materials with Elongation of 3 % | min. | H Temper | for thickness 0.1-5 mm |
10 % Show Supplier Material materials with Elongation of 10 % | min. | 1/2H Temper | for thickness 0.1-5 mm | |
30 % Show Supplier Material materials with Elongation of 30 % | min. | 1/4H Temper | for thickness 0.1-5 mm | |
40 % Show Supplier Material materials with Elongation of 40 % | min. | O Temper | for thickness 0.1-5 mm | |
Flexural modulus | 100 GPa Show Supplier Material materials with Flexural modulus of 100 GPa | |
Hardness, Vickers | 60 - 120 [-] Show Supplier Material materials with Hardness, Vickers of 60 - 120 [-] | 1/4H Temper | for thickness 0.15-5 mm |
90 - 155 [-] Show Supplier Material materials with Hardness, Vickers of 90 - 155 [-] | 1/2H Temper | for thickness 0.1-5 mm | |
120 - 165 [-] Show Supplier Material materials with Hardness, Vickers of 120 - 165 [-] | H Temper | for thickness 0.1-5 mm | |
140 [-] Show Supplier Material materials with Hardness, Vickers of 140 [-] | min. | EH Temper | for thickness 0.05-5 mm | |
Tensile strength | 240 MPa Show Supplier Material materials with Tensile strength of 240 MPa | min. | O Temper | for thickness 0.1-5 mm |
240 - 330 MPa Show Supplier Material materials with Tensile strength of 240 - 330 MPa | 1/4H Temper | for thickness 0.1-5 mm | |
330 - 450 MPa Show Supplier Material materials with Tensile strength of 330 - 450 MPa | 1/2H Temper | for thickness 0.1-5 mm | |
390 - 500 MPa Show Supplier Material materials with Tensile strength of 390 - 500 MPa | H Temper | for thickness 0.1-5 mm | |
460 MPa Show Supplier Material materials with Tensile strength of 460 MPa | min. | EH Temper | for thickness 0.1-5 mm |
Thermal
| Property | Value |
|---|---|
Coefficient of thermal expansion | 1.78e-05 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.78e-05 1/K |
Melting point | 1075 °C Show Supplier Material materials with Melting point of 1075 °C |
Thermal conductivity | 205 W/(m·K) Show Supplier Material materials with Thermal conductivity of 205 W/(m·K) |
Electrical
| Property | Value |
|---|---|
Specific Electrical conductivity | 40 % IACS Show Supplier Material materials with Specific Electrical conductivity of 40 % IACS |
Chemical properties
| Property | Value | Comment |
|---|---|---|
Iron | 0.1 % Show Supplier Material materials with Iron of 0.1 % | max. |
Lead | 0.02 % Show Supplier Material materials with Lead of 0.02 % | max. |
Other | 99.5 % Show Supplier Material materials with Other of 99.5 % | min. | Cu+Sn+P |
Phosphorus | 0.15 % Show Supplier Material materials with Phosphorus of 0.15 % | max. |
Tin | 1 - 1.7 % Show Supplier Material materials with Tin of 1 - 1.7 % | |
Zinc | 0.2 % Show Supplier Material materials with Zinc of 0.2 % | max. |
Technological properties
| Property | ||
|---|---|---|
| Application areas | The grade is particularly suitable for electronics (connectors, lead frames, lead terminals, transistor terminals, etc.), electrical (relay and switch contacts, rotary switch slides and contacts, fuse clips, etc.), automotive (bearing frames, hydraulic equipment caps, packing, bearings, clutch disks, electrical parts, etc.) and others (bellows, slides, blades, plate springs, corrosion-proof machinery equipment, diaphragms, etc.) | |
| Coating | Standard product specification of a HOT-DIP-tinned strip. *Width means the slit width after plating. *Different plating thickness for each side is possible. * We can accommodate our products to individual specifications other than the above standard specifications. Please feel free to call us. | |
| Other | Hardness Vickers note: Minimum test force is 1.961 N | |
| Tolerances | ||