Properties
General
| Property | Value |
|---|---|
Relative density | 8.78 [-] Show Supplier Material materials with Relative density of 8.78 [-] |
Mechanical
| Property | Value | Comment |
|---|---|---|
Elastic modulus | 105 GPa Show Supplier Material materials with Elastic modulus of 105 GPa | |
Elongation | 5 % Show Supplier Material materials with Elongation of 5 % | min. | SH Temper | for thickness 0.1-0.4 mm |
9 % Show Supplier Material materials with Elongation of 9 % | min. | EH Temper | for thickness 0.1-0.8 mm | |
11 % Show Supplier Material materials with Elongation of 11 % | min. | H Temper | for thickness 0.1-1.6 mm | |
Flexural modulus | 100 GPa Show Supplier Material materials with Flexural modulus of 100 GPa | |
Hardness, Vickers | 200 - 240 [-] Show Supplier Material materials with Hardness, Vickers of 200 - 240 [-] | H Temper | for thickness 0.1-1.6 mm |
230 - 270 [-] Show Supplier Material materials with Hardness, Vickers of 230 - 270 [-] | EH Temper | for thickness 0.1-0.8 mm | |
250 - 300 [-] Show Supplier Material materials with Hardness, Vickers of 250 - 300 [-] | SH Temper | for thickness 0.1-0.4 mm | |
270 [-] Show Supplier Material materials with Hardness, Vickers of 270 [-] | min. | ESH Temper | for thickness 0.1-0.4 mm | |
290 [-] Show Supplier Material materials with Hardness, Vickers of 290 [-] | min. | XSH Temper | for thickness 0.1-0.4 mm | |
Tensile strength | 650 - 750 MPa Show Supplier Material materials with Tensile strength of 650 - 750 MPa | H Temper | for thickness 0.1-1.6 mm |
750 - 850 MPa Show Supplier Material materials with Tensile strength of 750 - 850 MPa | EH Temper | for thickness 0.1-0.8 mm | |
850 - 950 MPa Show Supplier Material materials with Tensile strength of 850 - 950 MPa | SH Temper | for thickness 0.1-0.4 mm | |
950 MPa Show Supplier Material materials with Tensile strength of 950 MPa | min. | ESH Temper | for thickness 0.1-0.4 mm | |
1000 MPa Show Supplier Material materials with Tensile strength of 1000 MPa | min. | XSH Temper | for thickness 0.1-0.4 mm | |
Yield strength | 430 MPa Show Supplier Material materials with Yield strength of 430 MPa | min. | H Temper | for spring material (Kb0.1) | for thickness 0.15-1.6 mm |
510 MPa Show Supplier Material materials with Yield strength of 510 MPa | min. | EH Temper | for spring material (Kb0.1) | for thickness 0.15-1.6 mm | |
510 MPa Show Supplier Material materials with Yield strength of 510 MPa | min. | H Temper | for thickness 0.1-1.6 mm, RP02 | |
570 MPa Show Supplier Material materials with Yield strength of 570 MPa | min. | SH Temper | for spring material (Kb0.1) | for thickness 0.15-1.6 mm | |
630 MPa Show Supplier Material materials with Yield strength of 630 MPa | min. | ESH Temper | for spring material (Kb0.1) | for thickness 0.15-1.6 mm | |
630 MPa Show Supplier Material materials with Yield strength of 630 MPa | min. | EH Temper | for thickness 0.1-0.8 mm, RP02 | |
700 MPa Show Supplier Material materials with Yield strength of 700 MPa | min. | XSH Temper | for spring material (Kb0.1) | for thickness 0.15-1.6 mm | |
750 MPa Show Supplier Material materials with Yield strength of 750 MPa | min. | SH Temper | for thickness 0.1-0.4 mm, RP02 | |
870 MPa Show Supplier Material materials with Yield strength of 870 MPa | min. | ESH Temper | for thickness 0.1-0.4 mm, RP02 | |
930 MPa Show Supplier Material materials with Yield strength of 930 MPa | min. | XSH Temper | for thickness 0.1-0.4 mm, RP02 |
Thermal
| Property | Value |
|---|---|
Coefficient of thermal expansion | 1.84e-05 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.84e-05 1/K |
Melting point | 845 - 1000 °C Show Supplier Material materials with Melting point of 845 - 1000 °C |
Specific heat capacity | 375 J/(kg·K) Show Supplier Material materials with Specific heat capacity of 375 J/(kg·K) |
Thermal conductivity | 50 W/(m·K) Show Supplier Material materials with Thermal conductivity of 50 W/(m·K) |
Electrical
| Property | Value |
|---|---|
Specific Electrical conductivity | 10 % IACS Show Supplier Material materials with Specific Electrical conductivity of 10 % IACS |
Chemical properties
| Property | Value | Comment |
|---|---|---|
Iron | 0.1 % Show Supplier Material materials with Iron of 0.1 % | max. |
Lead | 0.02 % Show Supplier Material materials with Lead of 0.02 % | max. |
Other | 99.5 % Show Supplier Material materials with Other of 99.5 % | min. | Cu+Sn+P |
Phosphorus | 0.03 - 0.35 % Show Supplier Material materials with Phosphorus of 0.03 - 0.35 % | |
Tin | 9 - 11 % Show Supplier Material materials with Tin of 9 - 11 % | |
Zinc | 0.2 % Show Supplier Material materials with Zinc of 0.2 % | max. |
Technological properties
| Property | ||
|---|---|---|
| Application areas | The grade is particularly suitable for electronics (connectors, lead frames, lead terminals, transistor terminals, etc.), electrical (relay and switch contacts, rotary switch slides and contacts, fuse clips, etc.), automotive (bearing frames, hydraulic equipment caps, packing, bearings, clutch disks, electrical parts, etc.) and others (bellows, slides, blades, plate springs, corrosion-proof machinery equipment, diaphragms, etc.) | |
| Coating | Standard product specification of a HOT-DIP-tinned strip. *Width means the slit width after plating. *Different plating thickness for each side is possible. * We can accommodate our products to individual specifications other than the above standard specifications. Please feel free to call us. | |
| Other | Hardness Vickers note: Minimum test force is 1.961 N | |
| Tolerances | ||