General
Property | Value |
---|---|
Relative density | 8.8 [-] Show Supplier Material materials with Relative density of 8.8 [-] |
Mechanical
Property | Value | Comment |
---|---|---|
Elastic modulus | 110 GPa Show Supplier Material materials with Elastic modulus of 110 GPa | |
Elongation | 5 % Show Supplier Material materials with Elongation of 5 % | min. | ESH Temper | for thickness 0.1-0.4 mm |
9 % Show Supplier Material materials with Elongation of 9 % | min. | SH Temper | for thickness 0.1-1.2 mm | |
11 % Show Supplier Material materials with Elongation of 11 % | min. | EH Temper | for thickness 0.1-1.2 mm | |
20 % Show Supplier Material materials with Elongation of 20 % | min. | H Temper | for thickness 0.1-1.6 mm | |
27 % Show Supplier Material materials with Elongation of 27 % | min. | 1/2H Temper | for thickness 0.1-1.6 mm | |
Flexural modulus | 100 GPa Show Supplier Material materials with Flexural modulus of 100 GPa | |
Hardness, Vickers | 140 - 205 [-] Show Supplier Material materials with Hardness, Vickers of 140 - 205 [-] | 1/2H Temper | for thickness 0.1-1.6 mm |
185 - 235 [-] Show Supplier Material materials with Hardness, Vickers of 185 - 235 [-] | H Temper | for thickness 0.1-1.6 mm | |
210 - 260 [-] Show Supplier Material materials with Hardness, Vickers of 210 - 260 [-] | EH Temper | for thickness 0.1-1.2 mm | |
230 - 270 [-] Show Supplier Material materials with Hardness, Vickers of 230 - 270 [-] | SH Temper | for thickness 0.1-1.2 mm | |
245 - 285 [-] Show Supplier Material materials with Hardness, Vickers of 245 - 285 [-] | ESH Temper | for thickness 0.1-0.4 mm | |
Tensile strength | 470 - 610 MPa Show Supplier Material materials with Tensile strength of 470 - 610 MPa | 1/2H Temper | for thickness 0.1-1.6 mm |
590 - 705 MPa Show Supplier Material materials with Tensile strength of 590 - 705 MPa | H Temper | for thickness 0.1-1.6 mm | |
685 - 785 MPa Show Supplier Material materials with Tensile strength of 685 - 785 MPa | EH Temper | for thickness 0.1-1.2 mm | |
735 - 835 MPa Show Supplier Material materials with Tensile strength of 735 - 835 MPa | SH Temper | for thickness 0.1-1.2 mm | |
770 - 885 MPa Show Supplier Material materials with Tensile strength of 770 - 885 MPa | ESH Temper | for thickness 0.1-0.4 mm | |
Yield strength | 245 MPa Show Supplier Material materials with Yield strength of 245 MPa | min. | 1/2H Temper | for spring material (Kb0.1) | for thickness 0.15-1.6 mm |
260 MPa Show Supplier Material materials with Yield strength of 260 MPa | min. | 1/2H Temper | for thickness 0.1-1.6 mm, RP02 | |
390 MPa Show Supplier Material materials with Yield strength of 390 MPa | min. | H Temper | for spring material (Kb0.1) | for thickness 0.15-1.6 mm | |
450 MPa Show Supplier Material materials with Yield strength of 450 MPa | min. | H Temper | for thickness 0.1-1.6 mm, RP02 | |
460 MPa Show Supplier Material materials with Yield strength of 460 MPa | min. | EH Temper | for spring material (Kb0.1) | for thickness 0.15-1.6 mm | |
510 MPa Show Supplier Material materials with Yield strength of 510 MPa | min. | SH Temper | for spring material (Kb0.1) | for thickness 0.15-1.6 mm | |
560 MPa Show Supplier Material materials with Yield strength of 560 MPa | min. | ESH Temper | for spring material (Kb0.1) | for thickness 0.15-1.6 mm | |
580 MPa Show Supplier Material materials with Yield strength of 580 MPa | min. | EH Temper | for thickness 0.1-1.2 mm, RP02 | |
640 MPa Show Supplier Material materials with Yield strength of 640 MPa | min. | SH Temper | for thickness 0.1-1.2 mm, RP02 | |
690 MPa Show Supplier Material materials with Yield strength of 690 MPa | min. | ESH Temper | for thickness 0.1-0.4 mm, RP02 |
Thermal
Property | Value |
---|---|
Coefficient of thermal expansion | 1.82e-05 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.82e-05 1/K |
Melting point | 880 - 1020 °C Show Supplier Material materials with Melting point of 880 - 1020 °C |
Specific heat capacity | 377 J/(kg·K) Show Supplier Material materials with Specific heat capacity of 377 J/(kg·K) |
Thermal conductivity | 63 W/(m·K) Show Supplier Material materials with Thermal conductivity of 63 W/(m·K) |
Electrical
Property | Value |
---|---|
Specific Electrical conductivity | 12 % IACS Show Supplier Material materials with Specific Electrical conductivity of 12 % IACS |
Chemical properties
Property | Value | Comment |
---|---|---|
Iron | 0.1 % Show Supplier Material materials with Iron of 0.1 % | max. |
Lead | 0.02 % Show Supplier Material materials with Lead of 0.02 % | max. |
Other | 99.5 % Show Supplier Material materials with Other of 99.5 % | min. | Cu+Sn+P |
Phosphorus | 0.03 - 0.35 % Show Supplier Material materials with Phosphorus of 0.03 - 0.35 % | |
Tin | 7 - 9 % Show Supplier Material materials with Tin of 7 - 9 % | |
Zinc | 0.2 % Show Supplier Material materials with Zinc of 0.2 % | max. |
Technological properties
Property | ||
---|---|---|
Application areas | The grade is particularly suitable for electronics (connectors, lead frames, lead terminals, transistor terminals, etc.), electrical (relay and switch contacts, rotary switch slides and contacts, fuse clips, etc.), automotive (bearing frames, hydraulic equipment caps, packing, bearings, clutch disks, electrical parts, etc.) and others (bellows, slides, blades, plate springs, corrosion-proof machinery equipment, diaphragms, etc.) | |
Coating | Standard product specification of a HOT-DIP-tinned strip. *Width means the slit width after plating. *Different plating thickness for each side is possible. * We can accommodate our products to individual specifications other than the above standard specifications. Please feel free to call us. | |
Other | Hardness Vickers note: Minimum test force is 1.961 N | |
Tolerances |