General
Property | Value |
---|---|
Relative density | 8.87 [-] Show Supplier Material materials with Relative density of 8.87 [-] |
Mechanical
Property | Value | Comment |
---|---|---|
Bendability 90°, bw | 0 [-] Show Supplier Material materials with Bendability 90°, bw of 0 [-] | O Temper | Ts=331 N/mm2 |
0.5 [-] Show Supplier Material materials with Bendability 90°, bw of 0.5 [-] | 1/2H Temper | Ts=467 N/mm2 | |
1 [-] Show Supplier Material materials with Bendability 90°, bw of 1 [-] | H Temper | Ts=515 N/mm2 | |
2.5 [-] Show Supplier Material materials with Bendability 90°, bw of 2.5 [-] | EH Temper | Ts=572 N/mm2 | |
Bendability 90°, gw | 0 [-] Show Supplier Material materials with Bendability 90°, gw of 0 [-] | O Temper | Ts=331 N/mm2 |
0 [-] Show Supplier Material materials with Bendability 90°, gw of 0 [-] | 1/2H Temper | Ts=467 N/mm2 | |
0.5 [-] Show Supplier Material materials with Bendability 90°, gw of 0.5 [-] | H Temper | Ts=515 N/mm2 | |
1 [-] Show Supplier Material materials with Bendability 90°, gw of 1 [-] | EH Temper | Ts=572 N/mm2 | |
1.5 [-] Show Supplier Material materials with Bendability 90°, gw of 1.5 [-] | SH Temper | Ts=644 N/mm2 | |
Elastic modulus | 122 GPa Show Supplier Material materials with Elastic modulus of 122 GPa | |
Elongation | 2 % Show Supplier Material materials with Elongation of 2 % | min. | EH Temper | for thickness 0.1-5 mm |
5 % Show Supplier Material materials with Elongation of 5 % | min. | H Temper | for thickness 0.1-5 mm | |
10 % Show Supplier Material materials with Elongation of 10 % | min. | 1/2H Temper | for thickness 0.1-5 mm | |
30 % Show Supplier Material materials with Elongation of 30 % | min. | O Temper | for thickness 0.1-5 mm | |
Flexural modulus | 112 GPa Show Supplier Material materials with Flexural modulus of 112 GPa | |
Hardness, Vickers | 70 - 115 [-] Show Supplier Material materials with Hardness, Vickers of 70 - 115 [-] | O Temper | for thickness 0.1-5 mm |
125 - 165 [-] Show Supplier Material materials with Hardness, Vickers of 125 - 165 [-] | 1/2H Temper | for thickness 0.1-5 mm | |
150 - 185 [-] Show Supplier Material materials with Hardness, Vickers of 150 - 185 [-] | H Temper | for thickness 0.1-5 mm | |
175 - 205 [-] Show Supplier Material materials with Hardness, Vickers of 175 - 205 [-] | EH Temper | for thickness 0.1-5 mm | |
185 - 215 [-] Show Supplier Material materials with Hardness, Vickers of 185 - 215 [-] | SH Temper | for thickness 0.1-5 mm | |
Tensile strength | 300 MPa Show Supplier Material materials with Tensile strength of 300 MPa | min. | O Temper | for thickness 0.1-5 mm |
400 - 500 MPa Show Supplier Material materials with Tensile strength of 400 - 500 MPa | 1/2H Temper | for thickness 0.1-5 mm | |
450 - 550 MPa Show Supplier Material materials with Tensile strength of 450 - 550 MPa | H Temper | for thickness 0.1-5 mm | |
500 - 600 MPa Show Supplier Material materials with Tensile strength of 500 - 600 MPa | EH Temper | for thickness 0.1-5 mm | |
600 - 700 MPa Show Supplier Material materials with Tensile strength of 600 - 700 MPa | SH Temper | for thickness 0.1-5 mm |
Thermal
Property | Value |
---|---|
Coefficient of thermal expansion | 1.65e-05 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.65e-05 1/K |
Melting point | 1065 °C Show Supplier Material materials with Melting point of 1065 °C |
Thermal conductivity | 152 W/(m·K) Show Supplier Material materials with Thermal conductivity of 152 W/(m·K) |
Electrical
Property | Value |
---|---|
Specific Electrical conductivity | 32 % IACS Show Supplier Material materials with Specific Electrical conductivity of 32 % IACS |
Chemical properties
Property | Value | Comment |
---|---|---|
Iron | 0.1 % Show Supplier Material materials with Iron of 0.1 % | max. |
Lead | 0.02 % Show Supplier Material materials with Lead of 0.02 % | max. |
Other | 99.5 % Show Supplier Material materials with Other of 99.5 % | min. | Cu+Sn+P |
Phosphorus | 0.15 % Show Supplier Material materials with Phosphorus of 0.15 % | max. |
Tin | 1.7 - 2.3 % Show Supplier Material materials with Tin of 1.7 - 2.3 % | |
Zinc | 0.2 % Show Supplier Material materials with Zinc of 0.2 % | max. |
Technological properties
Property | ||
---|---|---|
Application areas | The grade is particularly suitable for electronics (connectors, lead frames, lead terminals, transistor terminals, etc.), electrical (relay and switch contacts, rotary switch slides and contacts, fuse clips, etc.), automotive (bearing frames, hydraulic equipment caps, packing, bearings, clutch disks, electrical parts, etc.) and others (bellows, slides, blades, plate springs, corrosion-proof machinery equipment, diaphragms, etc.) | |
Coating | Standard product specification of a HOT-DIP-tinned strip. *Width means the slit width after plating. *Different plating thickness for each side is possible. * We can accommodate our products to individual specifications other than the above standard specifications. Please feel free to call us. | |
Other | Hardness Vickers note: Minimum test force is 1.961 N | |
Tolerances |