Property | Value |
---|---|
Relative density | 8.86 [-] Show Supplier Material materials with Relative density of 8.86 [-] |
Mechanical
Property | Value | Comment |
---|---|---|
Elastic modulus | 115 GPa Show Supplier Material materials with Elastic modulus of 115 GPa | |
Elongation | 4 % Show Supplier Material materials with Elongation of 4 % | min. | EH Temper | for thickness 0.2-5 mm |
7 % Show Supplier Material materials with Elongation of 7 % | min. | H Temper | for thickness 0.1-5 mm | |
15 % Show Supplier Material materials with Elongation of 15 % | min. | 1/2H Temper | for thickness 0.1-5 mm | |
28 % Show Supplier Material materials with Elongation of 28 % | min. | 1/4H Temper | for thickness 0.1-5 mm | |
40 % Show Supplier Material materials with Elongation of 40 % | min. | O Temper | for thickness 0.1-5 mm | |
Flexural modulus | 110 GPa Show Supplier Material materials with Flexural modulus of 110 GPa | |
Hardness, Vickers | 90 - 160 [-] Show Supplier Material materials with Hardness, Vickers of 90 - 160 [-] | 1/4H Temper | for thickness 0.1-5 mm |
130 - 190 [-] Show Supplier Material materials with Hardness, Vickers of 130 - 190 [-] | 1/2H Temper | for thickness 0.1-5 mm | |
170 - 220 [-] Show Supplier Material materials with Hardness, Vickers of 170 - 220 [-] | H Temper | for thickness 0.1-5 mm | |
190 - 230 [-] Show Supplier Material materials with Hardness, Vickers of 190 - 230 [-] | EH Temper | for thickness 0.05-5 mm | |
200 [-] Show Supplier Material materials with Hardness, Vickers of 200 [-] | min. | SH Temper | for thickness 0.05-5 mm | |
Tensile strength | 305 MPa Show Supplier Material materials with Tensile strength of 305 MPa | min. | O Temper | for thickness 0.1-5 mm |
375 - 470 MPa Show Supplier Material materials with Tensile strength of 375 - 470 MPa | 1/4H Temper | for thickness 0.1-5 mm | |
470 - 570 MPa Show Supplier Material materials with Tensile strength of 470 - 570 MPa | 1/2H Temper | for thickness 0.1-5 mm | |
570 - 665 MPa Show Supplier Material materials with Tensile strength of 570 - 665 MPa | H Temper | for thickness 0.1-5 mm | |
620 - 710 MPa Show Supplier Material materials with Tensile strength of 620 - 710 MPa | EH Temper | for thickness 0.1-5 mm | |
660 MPa Show Supplier Material materials with Tensile strength of 660 MPa | min. | SH Temper | for thickness 0.1-5 mm |
Thermal
Property | Value |
---|---|
Coefficient of thermal expansion | 1.78e-05 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.78e-05 1/K |
Melting point | 950 - 1050 °C Show Supplier Material materials with Melting point of 950 - 1050 °C |
Specific heat capacity | 377 J/(kg·K) Show Supplier Material materials with Specific heat capacity of 377 J/(kg·K) |
Thermal conductivity | 71 W/(m·K) Show Supplier Material materials with Thermal conductivity of 71 W/(m·K) |
Electrical
Property | Value |
---|---|
Specific Electrical conductivity | 17 % IACS Show Supplier Material materials with Specific Electrical conductivity of 17 % IACS |
Chemical properties
Property | Value | Comment |
---|---|---|
Iron | 0.1 % Show Supplier Material materials with Iron of 0.1 % | max. |
Lead | 0.02 % Show Supplier Material materials with Lead of 0.02 % | max. |
Other | 99.5 % Show Supplier Material materials with Other of 99.5 % | min. | Cu+Sn+P |
Phosphorus | 0.03 - 0.35 % Show Supplier Material materials with Phosphorus of 0.03 - 0.35 % | |
Tin | 4.5 - 5.5 % Show Supplier Material materials with Tin of 4.5 - 5.5 % | |
Zinc | 0.2 % Show Supplier Material materials with Zinc of 0.2 % | max. |
Technological properties
Property | ||
---|---|---|
Application areas | The grade is particularly suitable for electronics (connectors, lead frames, lead terminals, transistor terminals, etc.), electrical (relay and switch contacts, rotary switch slides and contacts, fuse clips, etc.), automotive (bearing frames, hydraulic equipment caps, packing, bearings, clutch disks, electrical parts, etc.) and others (bellows, slides, blades, plate springs, corrosion-proof machinery equipment, diaphragms, etc.) | |
Coating | Standard product specification of a HOT-DIP-tinned strip. *Width means the slit width after plating. *Different plating thickness for each side is possible. * We can accommodate our products to individual specifications other than the above standard specifications. Please feel free to call us. | |
Other | Hardness Vickers note: Minimum test force is 1.961 N | |
Tolerances |