General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 0.93 g/cm³ Show Supplier Material materials with Density of 0.93 g/cm³ | ASTM D792 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Compression set | 23.0 °C | 22 [-] Show Supplier Material materials with Compression set of 22 [-] | ASTM D395 |
Elongation | 23.0 °C | 700 % Show Supplier Material materials with Elongation of 700 % | ASTM D412 |
Hardness, Shore A | 23.0 °C | 60 [-] Show Supplier Material materials with Hardness, Shore A of 60 [-] | ASTM D2240 |
Tensile strength | 23.0 °C | 7.4 MPa Show Supplier Material materials with Tensile strength of 7.4 MPa | ASTM D412 |
Thermal
Property | Value | Comment |
---|---|---|
Brittleness temperature | -65 °C Show Supplier Material materials with Brittleness temperature of -65 °C | D746 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 28 g/10min Show Supplier Material materials with Melt mass-flow rate of 28 g/10min | D1238, 190°C/5kg | |
Shrinkage | 23.0 °C | 1.4 % Show Supplier Material materials with Shrinkage of 1.4 % | ASTM D955 |
Technological properties
Property | ||
---|---|---|
Processing methods | Extrusion: Hopper Temperature: 140-150°C, Middle Temperature: 150-170°C, Measurment Temperature: 170-190°C, Front Temperature: 180-200°C, Mold Temperature: 170-190°C, Melt Temperature: 160-180°C, Comp. Ratio:3:1, Screen: 20-60 Mesh - Injection: Rear Temperature: 140-150°C, Middle Temperature: 150-180°C, Front Temperature: 170-200°C, Nozzle Temperature: 190-200°C, Melt Temperature:180-190°C, Mold Temperature: 30-80°C, Speed: 100-200rpm, Back Pressure 0.07 - 0.7Mpa |