NBR/PVC Delas 175

Alternative and trade names
Delas 175
Want to keep this datasheet? Save it now in your required format

Description

Delas is NBR/PVC thermoplastic elastomer, with excellent grease resistance, weather resistance, Delas could replace NBR, Neoprene and PVC.

This material data has been provided by Lingen Plastic Rubber Co..

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.27 g/cm³

Show Supplier Material materials with Density of 1.27 g/cm³

ASTM D792

Mechanical

PropertyTemperatureValueComment

Compression set

70.0 °C

66 [-]

Show Supplier Material materials with Compression set of 66 [-]

ASTM D395

Elongation

23.0 °C

430 %

Show Supplier Material materials with Elongation of 430 %

ASTM D412

Hardness, Shore A

23.0 °C

75 [-]

Show Supplier Material materials with Hardness, Shore A of 75 [-]

ASTM D2240

Tear strength

23.0 °C

36 kN/m

Show Supplier Material materials with Tear strength of 36 kN/m

ASTM D624

Tensile strength

23.0 °C

12 MPa

Show Supplier Material materials with Tensile strength of 12 MPa

ASTM D412

Thermal

PropertyValueComment

Max service temperature

80 °C

Show Supplier Material materials with Max service temperature of 80 °C

ASTM D746

Min service temperature

-26 °C

Show Supplier Material materials with Min service temperature of -26 °C

ASTM D746

Technological properties

Property
Processing methods

Pre-drying: 60°C for 6-8 hr, Extrusion: Hopper Temperature: 130-140°C, Middle Temperature: 140-150°C, Measurment Temperature: 140-150°C, Front Temperature: 150-170°C, Mold Temperature: 150-170°C, Melt Temperature: 160°C, Comp. Ratio: 2.5:1, Screen: 20-60 Mesh - Injection: Rear Temperature: 130-140°C, Middle Temperature: 140-160°C, Front Temperature: 160-190°C, Nozzle Temperature: 170-190°C, Melt Temperature:170°C, Mold Temperature: 30-80°C, Speed: 100-200rpm, Back Pressure 0.05-05 Mpa