General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.26 g/cm³ Show Supplier Material materials with Density of 1.26 g/cm³ | ASTM D792 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Compression set | 70.0 °C | 65 [-] Show Supplier Material materials with Compression set of 65 [-] | ASTM D395 |
Elongation | 23.0 °C | 290 % Show Supplier Material materials with Elongation of 290 % | ASTM D412 |
Hardness, Shore A | 23.0 °C | 95 [-] Show Supplier Material materials with Hardness, Shore A of 95 [-] | ASTM D2240 |
Tear strength | 23.0 °C | 45 kN/m Show Supplier Material materials with Tear strength of 45 kN/m | ASTM D624 |
Tensile strength | 23.0 °C | 16.7 MPa Show Supplier Material materials with Tensile strength of 16.7 MPa | ASTM D412 |
Thermal
Technological properties
Property | ||
---|---|---|
Processing methods | Pre-drying: 60°C for 6-8 hr, Extrusion: Hopper Temperature: 130-140°C, Middle Temperature: 140-150°C, Measurment Temperature: 140-150°C, Front Temperature: 150-170°C, Mold Temperature: 150-170°C, Melt Temperature: 160°C, Comp. Ratio: 2.5:1, Screen: 20-60 Mesh - Injection: Rear Temperature: 130-140°C, Middle Temperature: 140-160°C, Front Temperature: 160-190°C, Nozzle Temperature: 170-190°C, Melt Temperature:170°C, Mold Temperature: 30-80°C, Speed: 100-200rpm, Back Pressure 0.05-05 Mpa |