General
Property | Temperature | Value | Condition | Related Standards |
---|---|---|---|---|
Density | 20.0 °C | 2.7 g/cm³ Show Material materials with Density of 2.7 g/cm³ | T5 | DIN 1725-2, EN 1676, EN 1706 |
Mechanical
Property | Temperature | Value | Condition | Related Standards | Comment |
---|---|---|---|---|---|
Elastic modulus | 20.0 °C | 73.0 GPa Show Material materials with Elastic modulus of 73.0 GPa | T5 | DIN 1725-2, EN 1676, EN 1706 | |
Elongation | -196.0 °C | 1.4 % Show Material materials with Elongation of 1.4 % | T5 | DIN 1725-2, EN 1676, EN 1706 | |
-196.0 °C | 1.6 % Show Material materials with Elongation of 1.6 % | T5 | DIN 1725-2, EN 1676, EN 1706 | ||
-120.0 °C | 1.2 % Show Material materials with Elongation of 1.2 % | T5 | DIN 1725-2, EN 1676, EN 1706 | ||
-120.0 °C | 1.6 % Show Material materials with Elongation of 1.6 % | T5 | DIN 1725-2, EN 1676, EN 1706 | ||
-50.0 °C | 1.4 % Show Material materials with Elongation of 1.4 % | T5 | DIN 1725-2, EN 1676, EN 1706 | ||
20.0 °C | 0.5 % Show Material materials with Elongation of 0.5 % | T5 | DIN 1725-2, EN 1676, EN 1706 | ||
20.0 °C | 0.7 % Show Material materials with Elongation of 0.7 % | T5 | DIN 1725-2, EN 1676, EN 1706 | ||
20.0 °C | 1.0 - 3.0 % Show Material materials with Elongation of 1.0 - 3.0 % | T5 | DIN 1725-2, EN 1676, EN 1706 | ||
20.0 °C | 2.2 % Show Material materials with Elongation of 2.2 % | T5 | DIN 1725-2, EN 1676, EN 1706 | ||
Hardness, Brinell | 20.0 °C | 90.0 [-] Show Material materials with Hardness, Brinell of 90.0 [-] | T5 | DIN 1725-2, EN 1676, EN 1706 | |
20.0 °C | 90.0 - 110.0 [-] Show Material materials with Hardness, Brinell of 90.0 - 110.0 [-] | T5 | DIN 1725-2, EN 1676, EN 1706 | ||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Cast 3xx.x Series Aluminium | |||
Shear modulus | 2.8 GPa Show Material materials with Shear modulus of 2.8 GPa | Typical for Cast 3xx.x Series Aluminium | |||
Shear strength | 20.0 °C | 181.0 MPa Show Material materials with Shear strength of 181.0 MPa | T5 | DIN 1725-2, EN 1676, EN 1706 | |
Tensile strength | -196.0 °C | 278.0 MPa Show Material materials with Tensile strength of 278.0 MPa | T5 | DIN 1725-2, EN 1676, EN 1706 | |
-196.0 °C | 312.0 MPa Show Material materials with Tensile strength of 312.0 MPa | T5 | DIN 1725-2, EN 1676, EN 1706 | ||
-120.0 °C | 266.0 MPa Show Material materials with Tensile strength of 266.0 MPa | T5 | DIN 1725-2, EN 1676, EN 1706 | ||
-120.0 °C | 287.0 MPa Show Material materials with Tensile strength of 287.0 MPa | T5 | DIN 1725-2, EN 1676, EN 1706 | ||
-50.0 °C | 258.0 MPa Show Material materials with Tensile strength of 258.0 MPa | T5 | DIN 1725-2, EN 1676, EN 1706 | ||
-50.0 °C | 276.0 MPa Show Material materials with Tensile strength of 276.0 MPa | T5 | DIN 1725-2, EN 1676, EN 1706 | ||
20.0 °C | 190.0 MPa Show Material materials with Tensile strength of 190.0 MPa | T5 | DIN 1725-2, EN 1676, EN 1706 | ||
20.0 °C | 242.0 MPa Show Material materials with Tensile strength of 242.0 MPa | T5 | DIN 1725-2, EN 1676, EN 1706 | ||
20.0 °C | 249.0 MPa Show Material materials with Tensile strength of 249.0 MPa | T5 | DIN 1725-2, EN 1676, EN 1706 | ||
20.0 °C | 260.0 - 320.0 MPa Show Material materials with Tensile strength of 260.0 - 320.0 MPa | T5 | DIN 1725-2, EN 1676, EN 1706 |
Thermal
Property | Temperature | Value | Condition | Related Standards | Comment |
---|---|---|---|---|---|
Coefficient of thermal expansion | 200.0 °C | 2.3e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3e-05 1/K | T5 | DIN 1725-2, EN 1676, EN 1706 | |
Melting point | 505.0 - 770.0 °C Show Material materials with Melting point of 505.0 - 770.0 °C | Typical for Cast 3xx.x Series Aluminium | |||
Specific heat capacity | 20.0 °C | 920.0 J/(kg·K) Show Material materials with Specific heat capacity of 920.0 J/(kg·K) | T5 | DIN 1725-2, EN 1676, EN 1706 | |
Thermal conductivity | 20.0 °C | 150.0 - 190.0 W/(m·K) Show Material materials with Thermal conductivity of 150.0 - 190.0 W/(m·K) | T5 | DIN 1725-2, EN 1676, EN 1706 |
Electrical
Property | Temperature | Value | Condition | Related Standards |
---|---|---|---|---|
Electrical conductivity | 20.0 °C | 21000000.0 - 29000000.0 S/m Show Material materials with Electrical conductivity of 21000000.0 - 29000000.0 S/m | T5 | DIN 1725-2, EN 1676, EN 1706 |
Chemical properties
Property | Value | Condition | Related Standards |
---|---|---|---|
Aluminium | 91.8 % Show Material materials with Aluminium of 91.8 % | T5 | DIN 1725-2, EN 1676, EN 1706 |
Copper | 0.05 Show Material materials with Copper of 0.05 | T5 | DIN 1725-2, EN 1676, EN 1706 |
Iron | 0.5 Show Material materials with Iron of 0.5 | T5 | DIN 1725-2, EN 1676, EN 1706 |
Magnesium | 0.4 - 0.8 % Show Material materials with Magnesium of 0.4 - 0.8 % | T5 | DIN 1725-2, EN 1676, EN 1706 |
Manganese | 0.001 - 0.4 % Show Material materials with Manganese of 0.001 - 0.4 % | T5 | DIN 1725-2, EN 1676, EN 1706 |
Silicon | 5.0 - 6.0 % Show Material materials with Silicon of 5.0 - 6.0 % | T5 | DIN 1725-2, EN 1676, EN 1706 |
Titanium | 0.001 - 0.2 % Show Material materials with Titanium of 0.001 - 0.2 % | T5 | DIN 1725-2, EN 1676, EN 1706 |
Zinc | 0.1 Show Material materials with Zinc of 0.1 | T5 | DIN 1725-2, EN 1676, EN 1706 |
Technological properties
Property | ||
---|---|---|
Processing methods | permanent mould casting |