DIN 1725-2 Grade 3.3241 T5

Want to keep this datasheet? Save it now in your required format

Description

The alloy G-AlMg3Si solidified in a wide temperature range, is sufficiently castable and poses excellent weather and corrosion resistance. G-AlMg3Si is especially applicable for mechanically high loaded cast pieces. It is excellent polishable and able for anodic oxdising for decorative purpose. Application: ship, automotive and aircraft construction, chemical and fodd industry, fittings and claddings

Related Standards

Equivalent Materials

This material data has been provided by WIAM.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueConditionRelated Standards

Density

20.0 °C

2.7 g/cm³

Show Material materials with Density of 2.7 g/cm³

T5

DIN 1725-2, EN 1676, EN 1706

Mechanical

PropertyTemperatureValueConditionRelated StandardsComment

Elastic modulus

20.0 °C

70.0 GPa

Show Material materials with Elastic modulus of 70.0 GPa

T5

DIN 1725-2, EN 1676, EN 1706

Elongation

20.0 °C

2.0 %

Show Material materials with Elongation of 2.0 %

T5

DIN 1725-2, EN 1676, EN 1706

20.0 °C

2.0 - 8.0 %

Show Material materials with Elongation of 2.0 - 8.0 %

T5

DIN 1725-2, EN 1676, EN 1706

20.0 °C

3.0 %

Show Material materials with Elongation of 3.0 %

T5

DIN 1725-2, EN 1676, EN 1706

20.0 °C

3.0 - 10.0 %

Show Material materials with Elongation of 3.0 - 10.0 %

T5

DIN 1725-2, EN 1676, EN 1706

Hardness, Brinell

20.0 °C

55.0 [-]

Show Material materials with Hardness, Brinell of 55.0 [-]

T5

DIN 1725-2, EN 1676, EN 1706

20.0 °C

60.0 - 80.0 [-]

Show Material materials with Hardness, Brinell of 60.0 - 80.0 [-]

T5

DIN 1725-2, EN 1676, EN 1706

20.0 °C

60.0 [-]

Show Material materials with Hardness, Brinell of 60.0 [-]

T5

DIN 1725-2, EN 1676, EN 1706

20.0 °C

65.0 [-]

Show Material materials with Hardness, Brinell of 65.0 [-]

T5

DIN 1725-2, EN 1676, EN 1706

20.0 °C

65.0 - 90.0 [-]

Show Material materials with Hardness, Brinell of 65.0 - 90.0 [-]

T5

DIN 1725-2, EN 1676, EN 1706

Unlock all property charts

Poisson's ratio

0.33 [-]

Show Material materials with Poisson's ratio of 0.33 [-]

Typical for Cast 5xx.x Series Aluminium

Tensile strength

20.0 °C

180.0 MPa

Show Material materials with Tensile strength of 180.0 MPa

T5

DIN 1725-2, EN 1676, EN 1706

20.0 °C

200.0 - 280.0 MPa

Show Material materials with Tensile strength of 200.0 - 280.0 MPa

T5

DIN 1725-2, EN 1676, EN 1706

20.0 °C

220.0 MPa

Show Material materials with Tensile strength of 220.0 MPa

T5

DIN 1725-2, EN 1676, EN 1706

20.0 °C

220.0 - 300.0 MPa

Show Material materials with Tensile strength of 220.0 - 300.0 MPa

T5

DIN 1725-2, EN 1676, EN 1706

Unlock all property charts

Thermal

PropertyTemperatureValueConditionRelated StandardsComment

Coefficient of thermal expansion

200.0 °C

2.4e-05 1/K

Show Material materials with Coefficient of thermal expansion of 2.4e-05 1/K

T5

DIN 1725-2, EN 1676, EN 1706

Melting point

450.0 - 640.0 °C

Show Material materials with Melting point of 450.0 - 640.0 °C

Typical for Cast 5xx.x Series Aluminium

Specific heat capacity

20.0 °C

930.0 J/(kg·K)

Show Material materials with Specific heat capacity of 930.0 J/(kg·K)

T5

DIN 1725-2, EN 1676, EN 1706

Thermal conductivity

20.0 °C

110.0 - 140.0 W/(m·K)

Show Material materials with Thermal conductivity of 110.0 - 140.0 W/(m·K)

T5

DIN 1725-2, EN 1676, EN 1706

Electrical

PropertyTemperatureValueConditionRelated Standards

Electrical conductivity

20.0 °C

15000000.0 - 21000000.0 S/m

Show Material materials with Electrical conductivity of 15000000.0 - 21000000.0 S/m

T5

DIN 1725-2, EN 1676, EN 1706

Chemical properties

PropertyValueConditionRelated Standards

Aluminium

93.8 %

Show Material materials with Aluminium of 93.8 %

T5

DIN 1725-2, EN 1676, EN 1706

Copper

0.05

Show Material materials with Copper of 0.05

T5

DIN 1725-2, EN 1676, EN 1706

Iron

0.5

Show Material materials with Iron of 0.5

T5

DIN 1725-2, EN 1676, EN 1706

Magnesium

2.5 - 3.5 %

Show Material materials with Magnesium of 2.5 - 3.5 %

T5

DIN 1725-2, EN 1676, EN 1706

Manganese

0.001 - 0.4 %

Show Material materials with Manganese of 0.001 - 0.4 %

T5

DIN 1725-2, EN 1676, EN 1706

Silicon

0.9 - 1.3 %

Show Material materials with Silicon of 0.9 - 1.3 %

T5

DIN 1725-2, EN 1676, EN 1706

Titanium

0.001 - 0.2 %

Show Material materials with Titanium of 0.001 - 0.2 %

T5

DIN 1725-2, EN 1676, EN 1706

Zinc

0.1

Show Material materials with Zinc of 0.1

T5

DIN 1725-2, EN 1676, EN 1706

Technological properties

Property
Processing methods

investment casting, sample taken from casting