EN 12165 Grade CuAl10Fe3Mn2 M

Want to keep this datasheet? Save it now in your required format

Description

CuAl10Fe3Mn2 (CW306G) is a wrought alloy of high strength, also at increased temperatures. The strength properties of cold formable wrought alloys are primarily dependent on the deformation grade. Tensile strength, yield strength and hardness rise according to the increasing cold forming grade. Elongation after fracture and contraction at fracture are decreasing. Thermal conductivity is reduced by the Al-content, electrical conductivity decreases according to the increasing AL-content. CuAl10Fe3Mn2 has a high strength at high temperatures up to approx. 300°C and a high endurance strength also at corrosion strain. The alloy is scaling resistant , shows a high wear resistance and a high corrosion resistance to saltwater, sulfite bases and mineral acids. Processing properties: warm forming: good cold forming: unfavorable machinability: moderately soft soldering: unfavorable hard soldering: moderately gas-shielded welding: good burnishing: good CuAl10Fe3Mn2 is a construction material for chemical apparatus engineering. It is particularly suitable for impact, dynamic or wear loaded components in engine and transmission engineering, for scaling resistant parts, for bolts, high-strength screws and nuts, for shafts, spindles, worm and gear wheels and rims as well as for control system parts in hydraulics, for bearings and sliding elements.

Related Standards

Equivalent Materials

This material data has been provided by WIAM.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.6 g/cm³

Show Material materials with Density of 7.6 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

20.0 °C

120 GPa

Show Material materials with Elastic modulus of 120 GPa

Poisson's ratio

23.0 °C

0.33 [-]

Show Material materials with Poisson's ratio of 0.33 [-]

Typical for Leaded Phosphor Bronze

Shear modulus

20.0 °C

43 GPa

Show Material materials with Shear modulus of 43 GPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

1.5E-5 - 1.9E-5 1/K

Show Material materials with Coefficient of thermal expansion of 1.5E-5 - 1.9E-5 1/K

Typical for Leaded Phosphor Bronze

Specific heat capacity

20.0 °C

377 - 418 J/(kg·K)

Show Material materials with Specific heat capacity of 377 - 418 J/(kg·K)

Thermal conductivity

20.0 °C

57 W/(m·K)

Show Material materials with Thermal conductivity of 57 W/(m·K)

Electrical

PropertyTemperatureValue

Electrical conductivity

20.0 °C

7.00E+6 S/m

Show Material materials with Electrical conductivity of 7.00E+6 S/m

Specific Electrical conductivity

12.1 % IACS

Show Material materials with Specific Electrical conductivity of 12.1 % IACS

Chemical properties

PropertyValue

Aluminium

9 - 11 %

Show Material materials with Aluminium of 9 - 11 %

Copper

79.45 %

Show Material materials with Copper of 79.45 %

Iron

2 - 4 %

Show Material materials with Iron of 2 - 4 %

Lead

0.05 %

Show Material materials with Lead of 0.05 %

Manganese

1.5 - 3.5 %

Show Material materials with Manganese of 1.5 - 3.5 %

Nickel

1 %

Show Material materials with Nickel of 1 %

Silicon

0.2 %

Show Material materials with Silicon of 0.2 %

Tin

0.1 %

Show Material materials with Tin of 0.1 %

Zinc

0.5 %

Show Material materials with Zinc of 0.5 %