Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 23.0 °C | 3.1 g/cm³ Show Material materials with Density of 3.1 g/cm³ |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 23.0 °C | 71 GPa Show Material materials with Elastic modulus of 71 GPa | |
Elongation | 23.0 °C | 0.5 % Show Material materials with Elongation of 0.5 % | Sand cast, elongation in 50 mm |
Fatigue strength | 23.0 °C | 65 MPa Show Material materials with Fatigue strength of 65 MPa | for 5x10⁸ cycles, R.R. Moore type test |
Hardness, Brinell | 23.0 °C | 105 - 110 [-] Show Material materials with Hardness, Brinell of 105 - 110 [-] | 500 kg load, 10 mm b |
Poisson's ratio | 23.0 °C | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | |
Shear modulus | 23.0 °C | 26.5 GPa Show Material materials with Shear modulus of 26.5 GPa | |
Shear strength | 23.0 °C | 240 MPa Show Material materials with Shear strength of 240 MPa | |
Tensile strength | 23.0 °C | 220 - 324 MPa Show Material materials with Tensile strength of 220 - 324 MPa | Sand cast |
Yield strength | 23.0 °C | 220 MPa Show Material materials with Yield strength of 220 MPa | |
Yield strength Rp0.2 | 23.0 °C | 140 - 290 MPa Show Material materials with Yield strength Rp0.2 of 140 - 290 MPa | Sand cast |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 2.3E-5 1/K Show Material materials with Coefficient of thermal expansion of 2.3E-5 1/K | nominal value between 20°C and the mentioned temperature |
100.0 °C | 2.25E-5 1/K Show Material materials with Coefficient of thermal expansion of 2.25E-5 1/K | nominal value between 20°C and the mentioned temperature | |
300.0 °C | 2.45E-5 1/K Show Material materials with Coefficient of thermal expansion of 2.45E-5 1/K | nominal value between 20°C and the mentioned temperature | |
Melting point | 532 - 635 °C Show Material materials with Melting point of 532 - 635 °C | ||
Specific heat capacity | 23.0 °C | 960 J/(kg·K) Show Material materials with Specific heat capacity of 960 J/(kg·K) | |
Thermal conductivity | 23.0 °C | 130 W/(m·K) Show Material materials with Thermal conductivity of 130 W/(m·K) | nominal value |
25.0 °C | 134 W/(m·K) Show Material materials with Thermal conductivity of 134 W/(m·K) | nominal value | |
Electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Electrical conductivity | 23.0 °C | 1.95E+7 S/m Show Material materials with Electrical conductivity of 1.95E+7 S/m | Typical/Derived values |
Electrical resistivity | 23.0 °C | 5.22E-8 Ω·m Show Material materials with Electrical resistivity of 5.22E-8 Ω·m | Typical values |
Specific Electrical conductivity | 33 - 34 % IACS Show Material materials with Specific Electrical conductivity of 33 - 34 % IACS | Typical values |
Chemical properties
| Property | Value | Comment |
|---|---|---|
Aluminium | 88.4 - 93.6 % Show Material materials with Aluminium of 88.4 - 93.6 % | |
Chromium | 0 - 0.25 % Show Material materials with Chromium of 0 - 0.25 % | |
Copper | 3.5 - 4.5 % Show Material materials with Copper of 3.5 - 4.5 % | |
Iron | 0 - 1 % Show Material materials with Iron of 0 - 1 % | |
Magnesium | 1.2 - 1.8 % Show Material materials with Magnesium of 1.2 - 1.8 % | |
Manganese | 0 - 0.35 % Show Material materials with Manganese of 0 - 0.35 % | |
Nickel | 1.7 - 2.3 % Show Material materials with Nickel of 1.7 - 2.3 % | |
Other | 0 - 0.15 % Show Material materials with Other of 0 - 0.15 % | each 0.05, total 0.15, Rest Al |
Silicon | 0 - 0.7 % Show Material materials with Silicon of 0 - 0.7 % | |
Titanium | 0 - 0.25 % Show Material materials with Titanium of 0 - 0.25 % | |
Zinc | 0 - 0.35 % Show Material materials with Zinc of 0 - 0.35 % |