General
Property | Value | Condition | Related Standards | Shape |
---|---|---|---|---|
Density | 2.7 g/cm³ Show Material materials with Density of 2.7 g/cm³ | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B247, ASTM B313, ASTM B316, ASTM B345, ASTM B483, ASTM B547, BS EN 573-3, BS EN 755-2 | Extrusion |
2.7 g/cm³ Show Material materials with Density of 2.7 g/cm³ | T6 |
Mechanical
Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|---|
Bending Fatigue Strength | 95.0 MPa Show Material materials with Bending Fatigue Strength of 95.0 MPa | T6 | AA Standards | |||
Compressive modulus | 69.7 MPa Show Material materials with Compressive modulus of 69.7 MPa | T6 | ||||
Elastic modulus | 69.0 GPa Show Material materials with Elastic modulus of 69.0 GPa | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B247, ASTM B313, ASTM B316, ASTM B345, ASTM B483, ASTM B547 | |||
70.0 GPa Show Material materials with Elastic modulus of 70.0 GPa | T6 | BS EN 573-3, BS EN 755-2 | Extrusion | |||
Elongation | -195 °C | 22 % Show Material materials with Elongation of 22 % | T6 | Elongation in 50 mm | ||
-80 °C | 18 % Show Material materials with Elongation of 18 % | T6 | Elongation in 50 mm | |||
4.0 % Show Material materials with Elongation of 4.0 % | T6 | AA Standards, ASTM B209 | A50 | |||
4.0 % Show Material materials with Elongation of 4.0 % | T6 | AA Standards, ASTM B247 | A100 | |||
5.0 % Show Material materials with Elongation of 5.0 % | T6 | AA Standards, ASTM B247 | A50 | |||
5.0 % Show Material materials with Elongation of 5.0 % | T6 | AA Standards, ASTM B247 | A100 | |||
6.0 % Show Material materials with Elongation of 6.0 % | T6 | AA Standards, ASTM B209 | A50 | |||
6.0 % Show Material materials with Elongation of 6.0 % | T6 | AA Standards, ASTM B247 | A100 | |||
7.0 % Show Material materials with Elongation of 7.0 % | T6 | AA Standards, ASTM B247 | A50 | |||
7.0 % Show Material materials with Elongation of 7.0 % | T6 | AA Standards, ASTM B247 | A100 | |||
8.0 % Show Material materials with Elongation of 8.0 % | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B247, ASTM B345, ASTM B483 | A50 | |||
8.0 % Show Material materials with Elongation of 8.0 % | T6 | AA Standards, ASTM B234 | A100 | |||
9.0 % Show Material materials with Elongation of 9.0 % | T6 | AA Standards, ASTM B211, ASTM B221, ASTM B241, ASTM B247, ASTM B316, ASTM B345 | A100 | |||
9.4 % Show Material materials with Elongation of 9.4 % | T6 | |||||
10.0 % Show Material materials with Elongation of 10.0 % | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B247, ASTM B313, ASTM B345, ASTM B483, ASTM B547 | A50 | |||
10.0 % Show Material materials with Elongation of 10.0 % | T6 | AA Standards, ASTM B210, ASTM B234, ASTM B483 | A100 | |||
12.0 % Show Material materials with Elongation of 12.0 % | T6 | AA Standards, ASTM B210, ASTM B234, ASTM B241, ASTM B483 | A50 | |||
15.0 % Show Material materials with Elongation of 15.0 % | T6 | AA Standards | A100 | |||
0 °C | 17 % Show Material materials with Elongation of 17 % | T6 | Elongation in 50 mm | |||
24 °C | 17 % Show Material materials with Elongation of 17 % | T6 | Elongation in 50 mm | |||
100 °C | 18 % Show Material materials with Elongation of 18 % | T6 | Elongation in 50 mm | |||
150 °C | 20 % Show Material materials with Elongation of 20 % | T6 | Elongation in 50 mm | |||
205 °C | 28 % Show Material materials with Elongation of 28 % | T6 | Elongation in 50 mm | |||
260 °C | 60 % Show Material materials with Elongation of 60 % | T6 | Elongation in 50 mm | |||
315 °C | 85 % Show Material materials with Elongation of 85 % | T6 | Elongation in 50 mm | |||
370 °C | 95 % Show Material materials with Elongation of 95 % | T6 | Elongation in 50 mm | |||
Hardness, Brinell | 95.0 [-] Show Material materials with Hardness, Brinell of 95.0 [-] | T6 | AA Standards, BS EN 573-3, BS EN 755-2 | Extrusion | ||
95.0 [-] Show Material materials with Hardness, Brinell of 95.0 [-] | T6 | 500 kg load, 10 mm ball | ||||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 6000 Series Aluminium | ||||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 6000 Series Aluminium | ||||
Shear modulus | 26.0 - 26.5 GPa Show Material materials with Shear modulus of 26.0 - 26.5 GPa | Typical for Wrought 6000 Series Aluminium | ||||
Shear strength | 207.0 MPa Show Material materials with Shear strength of 207.0 MPa | T6 | ||||
Tensile strength | -195 °C | 415 MPa Show Material materials with Tensile strength of 415 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
-80 °C | 338 MPa Show Material materials with Tensile strength of 338 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
255.0 MPa Show Material materials with Tensile strength of 255.0 MPa | T6 | AA Standards, ASTM B247 | ||||
260.0 MPa Show Material materials with Tensile strength of 260.0 MPa | T6 | AA Standards, ASTM B221, ASTM B241, ASTM B247, ASTM B345, BS EN 573-3, BS EN 755-2 | Extrusion | |||
290.0 MPa Show Material materials with Tensile strength of 290.0 MPa | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | ||||
310.0 MPa Show Material materials with Tensile strength of 310.0 MPa | T6 | AA Standards | ||||
0 °C | 325 MPa Show Material materials with Tensile strength of 325 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
24 °C | 310 MPa Show Material materials with Tensile strength of 310 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
100 °C | 290 MPa Show Material materials with Tensile strength of 290 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
150 °C | 235 MPa Show Material materials with Tensile strength of 235 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
205 °C | 130 MPa Show Material materials with Tensile strength of 130 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
260 °C | 52 MPa Show Material materials with Tensile strength of 52 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
315 °C | 32 MPa Show Material materials with Tensile strength of 32 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
370 °C | 21 MPa Show Material materials with Tensile strength of 21 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
Yield strength | -196 °C | 324 MPa Show Material materials with Yield strength of 324 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
-80 °C | 290 MPa Show Material materials with Yield strength of 290 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
-28 °C | 283 MPa Show Material materials with Yield strength of 283 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
230.0 MPa Show Material materials with Yield strength of 230.0 MPa | T6 | AA Standards, ASTM B247 | RP02 | |||
235.0 MPa Show Material materials with Yield strength of 235.0 MPa | T6 | AA Standards, ASTM B247 | RP02 | |||
240.0 MPa Show Material materials with Yield strength of 240.0 MPa | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B247, ASTM B313, ASTM B316, ASTM B345, ASTM B483, ASTM B547, BS EN 573-3, BS EN 755-2 | Extrusion | RP02 | ||
270.0 MPa Show Material materials with Yield strength of 270.0 MPa | T6 | |||||
275.0 MPa Show Material materials with Yield strength of 275.0 MPa | T6 | AA Standards | RP02 | |||
24 °C | 276 MPa Show Material materials with Yield strength of 276 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
100 °C | 262 MPa Show Material materials with Yield strength of 262 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
149 °C | 214 MPa Show Material materials with Yield strength of 214 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
204 °C | 103 MPa Show Material materials with Yield strength of 103 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
260 °C | 34 MPa Show Material materials with Yield strength of 34 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
316 °C | 19 MPa Show Material materials with Yield strength of 19 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
371 °C | 12 MPa Show Material materials with Yield strength of 12 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 |
Thermal
Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|---|
Coefficient of thermal expansion | 2.4e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.4e-05 1/K | T6 | ||||
20 °C | 2.36e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.36e-05 1/K | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B247, ASTM B313, ASTM B316, ASTM B345, ASTM B483, ASTM B547 | |||
100 °C | 2.36e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.36e-05 1/K | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B247, ASTM B313, ASTM B316, ASTM B345, ASTM B483, ASTM B547 | |||
200 °C | 0.0000243 1/K Show Material materials with Coefficient of thermal expansion of 0.0000243 1/K | T6 | derived value between 20°C and the mentioned temperature | |||
300 °C | 0.0000254 1/K Show Material materials with Coefficient of thermal expansion of 0.0000254 1/K | T6 | derived value between 20°C and the mentioned temperature | |||
Melting point | 580.0 - 650.0 °C Show Material materials with Melting point of 580.0 - 650.0 °C | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B247, ASTM B313, ASTM B316, ASTM B345, ASTM B483, ASTM B547 | |||
580.0 °C Show Material materials with Melting point of 580.0 °C | T6 | |||||
650.0 °C Show Material materials with Melting point of 650.0 °C | T6 | BS EN 573-3, BS EN 755-2 | Extrusion | |||
Specific heat capacity | 900.0 J/(kg·K) Show Material materials with Specific heat capacity of 900.0 J/(kg·K) | T6 | ||||
100 °C | 960 J/(kg·K) Show Material materials with Specific heat capacity of 960 J/(kg·K) | T6 | derived value for 23-100°C | |||
Thermal conductivity | 155.0 - 180.0 W/(m·K) Show Material materials with Thermal conductivity of 155.0 - 180.0 W/(m·K) | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B247, ASTM B313, ASTM B316, ASTM B345, ASTM B483, ASTM B547 | |||
166.0 W/(m·K) Show Material materials with Thermal conductivity of 166.0 W/(m·K) | T6 | BS EN 573-3, BS EN 755-2 | Extrusion | |||
170.0 W/(m·K) Show Material materials with Thermal conductivity of 170.0 W/(m·K) | T6 | |||||
23 °C | 167.4 W/(m·K) Show Material materials with Thermal conductivity of 167.4 W/(m·K) | T6 | derived value | |||
25 °C | 154.9 W/(m·K) Show Material materials with Thermal conductivity of 154.9 W/(m·K) | T6 | derived value |
Electrical
Property | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|
Electrical conductivity | 23000000.0 - 27000000.0 S/m Show Material materials with Electrical conductivity of 23000000.0 - 27000000.0 S/m | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B247, ASTM B313, ASTM B316, ASTM B345, ASTM B483, ASTM B547 | ||
25000000 S/m Show Material materials with Electrical conductivity of 25000000 S/m | T6 | Typical/derived value | |||
Electrical resistivity | 3.7e-08 - 4.35e-08 Ω·m Show Material materials with Electrical resistivity of 3.7e-08 - 4.35e-08 Ω·m | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B247, ASTM B313, ASTM B316, ASTM B345, ASTM B483, ASTM B547 | ||
4e-08 Ω·m Show Material materials with Electrical resistivity of 4e-08 Ω·m | T6 | Typical value | |||
4e-08 Ω·m Show Material materials with Electrical resistivity of 4e-08 Ω·m | T6 | BS EN 573-3, BS EN 755-2 | Extrusion | ||
Specific Electrical conductivity | 43.0 % IACS Show Material materials with Specific Electrical conductivity of 43.0 % IACS | T6 | Typical value |
Chemical properties
Property | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|
Aluminium | 95.9 - 98.6 % Show Material materials with Aluminium of 95.9 - 98.6 % | T6 | |||
Chromium | 0.04 - 0.35 % Show Material materials with Chromium of 0.04 - 0.35 % | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B247, ASTM B313, ASTM B316, ASTM B345, ASTM B483, ASTM B547, BS EN 573-3, BS EN 755-2 | Extrusion | |
Copper | 0.15 - 0.4 % Show Material materials with Copper of 0.15 - 0.4 % | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B247, ASTM B313, ASTM B316, ASTM B345, ASTM B483, ASTM B547, BS EN 573-3, BS EN 755-2 | Extrusion | |
Iron | 0.70 % Show Material materials with Iron of 0.70 % | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B247, ASTM B313, ASTM B316, ASTM B345, ASTM B483, ASTM B547 | ||
0.7 % Show Material materials with Iron of 0.7 % | T6 | BS EN 573-3, BS EN 755-2 | Extrusion | ||
Magnesium | 0.8 - 1.2 % Show Material materials with Magnesium of 0.8 - 1.2 % | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B247, ASTM B313, ASTM B316, ASTM B345, ASTM B483, ASTM B547, BS EN 573-3, BS EN 755-2 | Extrusion | |
Manganese | 0.15 % Show Material materials with Manganese of 0.15 % | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B247, ASTM B313, ASTM B316, ASTM B345, ASTM B483, ASTM B547, BS EN 573-3, BS EN 755-2 | Extrusion | |
Other | 0.05 % Show Material materials with Other of 0.05 % | T6 | BS EN 573-3, BS EN 755-2 | Extrusion | Total |
0.15 % Show Material materials with Other of 0.15 % | T6 | ||||
Silicon | 0.4 - 0.8 % Show Material materials with Silicon of 0.4 - 0.8 % | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B247, ASTM B313, ASTM B316, ASTM B345, ASTM B483, ASTM B547, BS EN 573-3, BS EN 755-2 | Extrusion | |
Titanium | 0.15 % Show Material materials with Titanium of 0.15 % | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B247, ASTM B313, ASTM B316, ASTM B345, ASTM B483, ASTM B547, BS EN 573-3, BS EN 755-2 | Extrusion | |
Zinc | 0.25 % Show Material materials with Zinc of 0.25 % | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B247, ASTM B313, ASTM B316, ASTM B345, ASTM B483, ASTM B547, BS EN 573-3, BS EN 755-2 | Extrusion |
Technological properties
Property | ||
---|---|---|
Application areas | Heavy duty structures (Rail coaches, Truck frames, Ship building, Bridges and Military bridges, Aerospace applications including helicopter rotor), Skins (Tube, Pylons and Towers, Transport, Boilermaking, Motorboats, Rivets). | |
Brazing | general: possible with commercial processes and methods | |
Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests (O, T6, T651, T652, T6510, T6511), no damage during operation, limited damage during laboratory tests (T4, T451, T4510, T4511), general: good, without protection in industrial or seawater atmosphere | |
General machinability | General: poor (O), sufficient (T4, T451, T4510, T4511, T6, T651, T652, T6510, T6511) | |
Soldering general | Good | |
Welding | Gas: Good; Arc: Very Good; Resistance: Good | |
Workability | general (condition): good (O), acceptable (T4, T451, T4510, T4511), poor(T6, T651, T652, T6510, T6511) |