General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 3.94 g/cm³ Show Supplier Material materials with Density of 3.94 g/cm³ | |
Porosity | 0 % Show Supplier Material materials with Porosity of 0 % | open porositiy |
Mechanical
Property | Temperature | Value |
---|---|---|
Elastic modulus | 23.0 °C | 380 GPa Show Supplier Material materials with Elastic modulus of 380 GPa |
Flexural strength | 23.0 °C | 420 MPa Show Supplier Material materials with Flexural strength of 420 MPa |
Plane-Strain Fracture Toughnes | 23.0 °C | 3.8 MPa·√m Show Supplier Material materials with Plane-Strain Fracture Toughnes of 3.8 MPa·√m |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 1000.0 °C | 8.5E-6 1/K Show Supplier Material materials with Coefficient of thermal expansion of 8.5E-6 1/K | |
Max service temperature | 1750 °C Show Supplier Material materials with Max service temperature of 1750 °C | no load | |
Thermal conductivity | 23.0 °C | 29 W/(m·K) Show Supplier Material materials with Thermal conductivity of 29 W/(m·K) |
Electrical
Property | Temperature | Value |
---|---|---|
Electrical resistivity | 23.0 °C | 1.00E+11 Ω·m Show Supplier Material materials with Electrical resistivity of 1.00E+11 Ω·m |
Chemical properties
Property | Value | Comment |
---|---|---|
Aluminium | 99.96 % Show Supplier Material materials with Aluminium of 99.96 % | as Al₂O₃ |
Calcium | 1E-3 % Show Supplier Material materials with Calcium of 1E-3 % | as CaO |
Chromium | 1E-3 % Show Supplier Material materials with Chromium of 1E-3 % | |
Iron | 0.01 % Show Supplier Material materials with Iron of 0.01 % | as Fe₂O₃ |
Magnesium | 3E-3 % Show Supplier Material materials with Magnesium of 3E-3 % | as MgO |
Silicon | 0.01 % Show Supplier Material materials with Silicon of 0.01 % | as SiO₂ |
Titanium | 3E-3 % Show Supplier Material materials with Titanium of 3E-3 % | as TiO₂ |
Zinc | 5E-3 % Show Supplier Material materials with Zinc of 5E-3 % |
Technological properties
Property | ||
---|---|---|
Application areas | Typical application areas include: High temperature labware, furnace construction, abrasives industry, pump & compressor industry, chemical & pharma industry |