General
Property | Temperature | Value |
---|---|---|
Density | 23.0 °C | 5.5 g/cm³ Show Supplier Material materials with Density of 5.5 g/cm³ |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 275 GPa Show Supplier Material materials with Elastic modulus of 275 GPa | |
Flexural strength | 23.0 °C | 1550 MPa Show Supplier Material materials with Flexural strength of 1550 MPa | after HIP |
Hardness, Vickers | 23.0 °C | 1400 [-] Show Supplier Material materials with Hardness, Vickers of 1400 [-] | |
Plane-Strain Fracture Toughnes | 23.0 °C | 5 MPa·√m Show Supplier Material materials with Plane-Strain Fracture Toughnes of 5 MPa·√m |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 1000.0 °C | 1E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1E-5 1/K | |
Max service temperature | 1450 °C Show Supplier Material materials with Max service temperature of 1450 °C | no load | |
Thermal conductivity | 23.0 °C | 5.6 W/(m·K) Show Supplier Material materials with Thermal conductivity of 5.6 W/(m·K) |
Electrical
Property | Temperature | Value |
---|---|---|
Electrical resistivity | 23.0 °C | 1.00E+11 Ω·m Show Supplier Material materials with Electrical resistivity of 1.00E+11 Ω·m |
Chemical properties
Property | Value | Comment |
---|---|---|
Aluminium | 20 % Show Supplier Material materials with Aluminium of 20 % | as Al₂O₃ |
Silicon | 0.02 % Show Supplier Material materials with Silicon of 0.02 % | as SiO₂ |
Sodium | 0.04 % Show Supplier Material materials with Sodium of 0.04 % | as Na₂O |
Yttrium | 3.9 % Show Supplier Material materials with Yttrium of 3.9 % | as Y₂O₃ |
Zirconium | 76 % Show Supplier Material materials with Zirconium of 76 % | as ZrO₂ |
Technological properties
Property | ||
---|---|---|
Application areas | Typical application areas include: Pump & compressor industry, seal & gasket industry, wear parts, grinding media, bio applications (implants) |