Epoxy NP130 - Sheet

Alternative and trade names
NEMA GRADE: FR-4, U.L. LISTED: N
Want to keep this datasheet? Save it now in your required format

Description

NP130 is a woven glass fabric combined with halogenated epoxy resin system. NP130 is produced to printed circuit board quality standards. It is flame retardant, and meets the requirements of MIL-I-24768/27, Type GEE-F and IEC-60893-3-2 EP GC 202.

Properties

General

Bonding strength

Fbond

997.9 Kg at 23 °C

ASTM D229, Condition A

Density

ρ

1.8 g/cm³ at 23 °C

ASTM D792

Moisture absorption

cmoisture

0.1 % at 23 °C

ASTM D570, Condition D₁-24/23

Mechanical

Compressive strength

Rmc

482.6 MPa at 23 °C

Show Thermoset Polymer Matrix Composite materials with Compressive strength of 482.6 MPa at 23 °C

ASTM D695, Condition A, Flatwise

Flexural modulus

Ebend

18.6 GPa at 23 °C

Show Thermoset Polymer Matrix Composite materials with Flexural modulus of 18.6 GPa at 23 °C

ASTM D790, Condition A

Flexural modulus, transverse

Ebend,trans

16.5 GPa at 23 °C

Show Thermoset Polymer Matrix Composite materials with Flexural modulus, transverse of 16.5 GPa at 23 °C

ASTM D790, Condition A

Flexural strength

σbend

551.6 MPa at 23 °C

Show Thermoset Polymer Matrix Composite materials with Flexural strength of 551.6 MPa at 23 °C

ASTM D790, Condition A

Flexural strength, transverse

σbendT

413.7 MPa at 23 °C

Show Thermoset Polymer Matrix Composite materials with Flexural strength, transverse of 413.7 MPa at 23 °C

ASTM D790, Condition A

Hardness, Rockwell M

HRM

100 [-] at 23 °C

Show Thermoset Polymer Matrix Composite materials with Hardness, Rockwell M of 100 [-] at 23 °C

ASTM D785

Impact strength, Izod unnotched, ASTM

IIzod,unnot,astm

801 J/m at 23 °C

Show Thermoset Polymer Matrix Composite materials with Impact strength, Izod unnotched, ASTM of 801 J/m at 23 °C

ASTM D256, Condition E-48/50

Impact strength, Izod unnotched, ASTM, Transversal

IIzod,unnot,astm,trans

641 J/m at 23 °C

Show Thermoset Polymer Matrix Composite materials with Impact strength, Izod unnotched, ASTM, Transversal of 641 J/m at 23 °C

ASTM D256, Condition E-48/50

Shear strength, transverse

τtrans

151.7 MPa at 23 °C

Show Thermoset Polymer Matrix Composite materials with Shear strength, transverse of 151.7 MPa at 23 °C

ASTM D732, Condition A

Tensile strength

Rm

344.7 MPa at 23 °C

Show Thermoset Polymer Matrix Composite materials with Tensile strength of 344.7 MPa at 23 °C

ASTM D638, Condition A

Tensile strength, transverse

Rm,trans

275.8 MPa at 23 °C

Show Thermoset Polymer Matrix Composite materials with Tensile strength, transverse of 275.8 MPa at 23 °C

ASTM D638, Condition A

Thermal

Arc resistance

120 seconds, ASTM D495, Condition A

Coefficient of thermal expansion

α

1E-5 1/K at 23 °C

IPC-TM 650-2.4.24

Coefficient of thermal expansion, transverse

αtrans

1.2E-5 1/K at 23 °C

IPC-TM 650-2.4.24

Flammability

UL Bulletin 94, Class V-0

Glass transition temperature

Tg

127 °C

DMA

Relative temperature index, electrical

RTIel

130 °C

UL Bulletin 746b¹

Relative temperature index, mechanical strength

RTIstr

140 °C

UL Bulletin 746b¹

Electrical

Breakdown voltage

Ubreak

54 - 65 kV at 23 °C

ASTM D149, Condition D-48/50 (Min.) & A (Max.)

Comparative tracking index

CTI

150 V at 23 °C

ASTM D3638

Dielectric constant, 1MHz

εr,1MHz

4.8 [-] at 23 °C

ASTM D150, Condition D-24/23

Dielectric strength

EDS

25.59 - 26.38 kV/mm at 23 °C

ASTM D149, Condition D-48/50 (Min.) & A (Max.)

Dissipation factor, 1MHz

ε''1MHz

0.03 [-] at 23 °C

ASTM D150, Condition D-24/23

Technological properties

Fillers

Glass Fabric

Modifications

Other

1.This temperature is a recommendation only, and based upon experience in various applications. The maximum operating temperature is dependent upon the application and should be investigated prior to use.

Primary Phase

Secondary Phase

Supplier Disclaimer

This data, while believed to be accurate and based on reliable analytical methods, is for informational purposes only. The terms and conditions of the agreement under which it is sold will govern any sales of this product. Data supplied above are "typical values"; not to be considered "specification values".


To assure the material's performance is adequate for a specific application; customers should verify, independent of Norplex-Micarta, performance characteristics of interest.


It is the responsibility of the users of this information to make sure that they have the latest version of this TDB, and are urged to check with Customer Service or, preferably our web site, www.norplex-micarta.com, to determine if the information is the most current available.

This material data has been provided by Norplex Micarta.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.