Epoxy RT500X - Tube

Alternative and trade names
NEMA GRADE: G-10, U.L. LISTED: N
Want to keep this datasheet? Save it now in your required format

Description

The RT500X has excellent electrical properties under humid conditions and very good heat resistance and mechanical properties. RT500X is used when NEMA recognition is needed and fine machining is required. This version is made with an extra-fine weave fabric. RT500X also complies with MIL-I-24768/2, Type GEE and ASTM D709 Type IV Grade G-10.

This material data has been provided by Norplex Micarta.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.9 g/cm³

Show Supplier Material materials with Density of 1.9 g/cm³

ASTM D792

Moisture absorption

23.0 °C

0.07 %

Show Supplier Material materials with Moisture absorption of 0.07 %

ASTM D570, Condition D₁-24/23

Mechanical

PropertyTemperatureValueComment

Compressive modulus

23.0 °C

7.34 MPa

Show Supplier Material materials with Compressive modulus of 7.34 MPa

ASTM D695, Condition A

Compressive strength

23.0 °C

303.37 MPa

Show Supplier Material materials with Compressive strength of 303.37 MPa

ASTM D695, Condition A

Hardness, Rockwell M

23.0 °C

110 [-]

Show Supplier Material materials with Hardness, Rockwell M of 110 [-]

ASTM D785

Tensile strength

23.0 °C

344.74 MPa

Show Supplier Material materials with Tensile strength of 344.74 MPa

ASTM D638, Condition A

Thermal

PropertyValueComment

Glass transition temperature

170 °C

Show Supplier Material materials with Glass transition temperature of 170 °C

Min., DMA

Relative temperature index, electrical

200 °C

Show Supplier Material materials with Relative temperature index, electrical of 200 °C

¹

Relative temperature index, mechanical strength

200 °C

Show Supplier Material materials with Relative temperature index, mechanical strength of 200 °C

¹

Flammability

UL Bulletin 94, Class HB

Electrical

PropertyTemperatureValueComment

Breakdown voltage

23.0 °C

65 - 75 kV

Show Supplier Material materials with Breakdown voltage of 65 - 75 kV

ASTM D149, Condition A (Min.) & D-48/50 (Max.)

Dielectric constant, 1MHz

23.0 °C

4.39 - 4.46 [-]

Show Supplier Material materials with Dielectric constant, 1MHz of 4.39 - 4.46 [-]

ASTM D150, Condition A (Min.) & D-24/23 (Max.)

Dielectric strength

23.0 °C

19.48 - 19.68 kV/mm

Show Supplier Material materials with Dielectric strength of 19.48 - 19.68 kV/mm

ASTM D149, Condition D-48/50 (Min.) & A (Max.)

Dissipation factor, 1MHz

23.0 °C

0.02 - 0.03 [-]

Show Supplier Material materials with Dissipation factor, 1MHz of 0.02 - 0.03 [-]

ASTM D150, Condition A (Min.) & D-24/23 (Max.)

Technological properties

Property
Fillers

Glass Fabric

Other

1.This temperature is a recommendation only, and based upon experience in various applications. The maximum operating temperature is dependent upon the application and should be investigated prior to use


2.The mechanical properties are converted from American unit system to International unit system.

Supplier Disclaimer

This data, while believed to be accurate and based on reliable analytical methods, is for informational purposes only. The terms and conditions of the agreement under which it is sold will govern any sales of this product. Data supplied above are "typical values"; not to be considered "specification values".


To assure the material's performance is adequate for a specific application; customers should verify, independent of Norplex-Micarta, performance characteristics of interest.


It is the responsibility of the users of this information to make sure that they have the latest version of this TDB, and are urged to check with Customer Service or, preferably our web site, www.norplex-micarta.com, to determine if the information is the most current available.