Phenolic MC330 - Sheet

Alternative and trade names
U.L. LISTED: N
Want to keep this datasheet? Save it now in your required format

Description

Grade MC330 is a cotton cloth/phenolic resin composite which is specially processed to be used in cryogenic applications.

This material data has been provided by Norplex Micarta.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyTemperatureValueComment

Bonding strength

23.0 °C

1043 - 1133 Kg

Show Supplier Material materials with Bonding strength of 1043 - 1133 Kg

ASTM D229, Condition D-48/50 (Min.) & A (Max.)

Density

23.0 °C

1.37 g/cm³

Show Supplier Material materials with Density of 1.37 g/cm³

Moisture absorption

23.0 °C

3.5 %

Show Supplier Material materials with Moisture absorption of 3.5 %

Condition D₁-24/23

Mechanical

PropertyTemperatureValueComment

Compressive strength

23.0 °C

234.42 MPa

Show Supplier Material materials with Compressive strength of 234.42 MPa

Condition A

Flexural modulus

23.0 °C

11.03 GPa

Show Supplier Material materials with Flexural modulus of 11.03 GPa

Condition A

Flexural modulus, transverse

23.0 °C

10.34 GPa

Show Supplier Material materials with Flexural modulus, transverse of 10.34 GPa

Condition A

Flexural strength

23.0 °C

126.86 MPa

Show Supplier Material materials with Flexural strength of 126.86 MPa

Condition A

Flexural strength, transverse

23.0 °C

117.21 MPa

Show Supplier Material materials with Flexural strength, transverse of 117.21 MPa

Condition A

Hardness, Rockwell M

23.0 °C

100 [-]

Show Supplier Material materials with Hardness, Rockwell M of 100 [-]

Impact strength, Izod unnotched, ASTM

23.0 °C

195 J/m

Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 195 J/m

Condition E-48/50

Impact strength, Izod unnotched, ASTM, Transversal

23.0 °C

175 J/m

Show Supplier Material materials with Impact strength, Izod unnotched, ASTM, Transversal of 175 J/m

Condition E-48/50

Shear strength, transverse

23.0 °C

96.5 MPa

Show Supplier Material materials with Shear strength, transverse of 96.5 MPa

Tensile strength

23.0 °C

82.74 MPa

Show Supplier Material materials with Tensile strength of 82.74 MPa

Condition A

Tensile strength, transverse

23.0 °C

66.88 MPa

Show Supplier Material materials with Tensile strength, transverse of 66.88 MPa

Condition A

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

2E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 2E-5 1/K

IPC-TM 650-2.4.24

Coefficient of thermal expansion, transverse

23.0 °C

2.2E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion, transverse of 2.2E-5 1/K

IPC-TM 650-2.4.24

Relative temperature index, mechanical strength

125 °C

Show Supplier Material materials with Relative temperature index, mechanical strength of 125 °C

¹

Arc resistance

15 seconds, ASTM D495, Condition A

Flammability

UL 94, Class HB, Condition A

Electrical

PropertyTemperatureValueComment

Breakdown voltage

23.0 °C

5 - 20 kV

Show Supplier Material materials with Breakdown voltage of 5 - 20 kV

Condition D48/50 (Min.) & A (Max.)

Comparative tracking index

23.0 °C

155 V

Show Supplier Material materials with Comparative tracking index of 155 V

ASTM D3638

Dielectric strength

23.0 °C

5.91 - 15.75 kV/mm

Show Supplier Material materials with Dielectric strength of 5.91 - 15.75 kV/mm

Condition D48/50 (Min.) & A (Max.)

Technological properties

Property
Application areas

Applications include spacers for installation of liquid oxygen apparatus where temperatures are as low as minus 320 F.

Fillers

Cotton Fabric

Other

1.This temperature is a recommendation only, and based upon experience in various applications. The maximum operating temperature is dependent upon the application and should be investigated prior to use


2.The mechanical properties are converted from American unit system to International unit system.

Supplier Disclaimer

This data, while believed to be accurate and based on reliable analytical methods, is for informational purposes only. The terms and conditions of the agreement under which it is sold will govern any sales of this product. Data supplied above are "typical values"; not to be considered "specification values".