Property | Value | Testing Standard | Comment |
---|---|---|---|
Compressive strength | 234.4 MPa Show Supplier Material materials with Compressive strength of 234.4 MPa | ASTM D695 | Condition A | Flatwise |
Flexural modulus | 5.6 GPa Show Supplier Material materials with Flexural modulus of 5.6 GPa | ASTM D790 | Condition A, Transverse |
6.5 GPa Show Supplier Material materials with Flexural modulus of 6.5 GPa | ASTM D790 | Condition A | |
Flexural strength | 87.6 MPa Show Supplier Material materials with Flexural strength of 87.6 MPa | ASTM D790 | Condition A, Transverse |
111.7 MPa Show Supplier Material materials with Flexural strength of 111.7 MPa | ASTM D790 | Condition A | |
Hardness, Rockwell M | 80 [-] Show Supplier Material materials with Hardness, Rockwell M of 80 [-] | ASTM D785 | |
Impact strength, Izod unnotched, ASTM | 124 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 124 J/m | ASTM D256 | Condition E-48/50, Transverse |
320 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 320 J/m | ASTM D256 | Condition E-48/50 | |
Shear strength | 84.1 MPa Show Supplier Material materials with Shear strength of 84.1 MPa | ASTM D732 | Condition A, Transverse |
Tensile strength | 70.3 MPa Show Supplier Material materials with Tensile strength of 70.3 MPa | ASTM D638 | Condition A |
Thermal
Property | Value | Testing Standard | Comment |
---|---|---|---|
Coefficient of thermal expansion | 2.64e-05 1/K Show Supplier Material materials with Coefficient of thermal expansion of 2.64e-05 1/K | IPC-TM 650-2.4.24 | |
3.94e-05 1/K Show Supplier Material materials with Coefficient of thermal expansion of 3.94e-05 1/K | IPC-TM 650-2.4.24 | Transverse | |
Relative temperature index, mechanical strength | 125 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 125 °C | UL Bulletin 746b¹ |
Technological properties
Property | ||
---|---|---|
Application areas | BR60 is specifically designed for highly loaded bearing applications, where the lubrication is provided by the molybdenum disulfide. It may have a slightly greenish tint in the finished laminate. | |
Fillers | Cotton Fabric and MoS2 | |
Other | 1.This temperature is a recommendation only, and based upon experience in various applications. The maximum operating temperature is dependent upon the application and should be investigated prior to use. | |
Supplier Disclaimer | This data, while believed to be accurate and based on reliable analytical methods, is for informational purposes only. The terms and conditions of the agreement under which it is sold will govern any sales of this product. Data supplied above are "typical values"; not to be considered "specification values". To assure the material's performance is adequate for a specific application; customers should verify, independent of Norplex-Micarta, performance characteristics of interest. It is the responsibility of the users of this information to make sure that they have the latest version of this TDB, and are urged to check with Customer Service or, preferably our web site, www.norplex-micarta.com, to determine if the information is the most current available. |