Phenolic BP13NPM - Sheet

Alternative and trade names
U.L. LISTED: N
Want to keep this datasheet? Save it now in your required format

Description

Canvas phenolic laminate with molybdenum disulfide lubricant. The mechanical properties are slightly lower than BP11NPN. BP13NPM is used for lubricity in the composite when carbon (graphite) cannot be used because of conductivity.

Properties

General

Bonding strength

Fbond

861.8 Kg at 23 °C

ASTM D229, Condition A

Density

ρ

1.4 g/cm³ at 23 °C

ASTM D792

Moisture absorption

cmoisture

1.95 % at 23 °C

ASTM D570, Condition Dᵢ-24/23

Mechanical

Compressive strength

Rmc

248.2 MPa at 23 °C

Show Thermoset Polymer Matrix Composite materials with Compressive strength of 248.2 MPa at 23 °C

ASTM D695, Condition A, Flatwise

Flexural modulus

Ebend

8.3 GPa at 23 °C

Show Thermoset Polymer Matrix Composite materials with Flexural modulus of 8.3 GPa at 23 °C

ASTM D790, Condition A

Flexural modulus, transverse

Ebend,trans

6.9 GPa at 23 °C

Show Thermoset Polymer Matrix Composite materials with Flexural modulus, transverse of 6.9 GPa at 23 °C

ASTM D790, Condition A

Flexural strength

σbend

131 MPa at 23 °C

Show Thermoset Polymer Matrix Composite materials with Flexural strength of 131 MPa at 23 °C

ASTM D790, Condition A

Flexural strength, transverse

σbendT

117.2 MPa at 23 °C

Show Thermoset Polymer Matrix Composite materials with Flexural strength, transverse of 117.2 MPa at 23 °C

ASTM D790, Condition A

Hardness, Rockwell M

HRM

100 [-] at 23 °C

Show Thermoset Polymer Matrix Composite materials with Hardness, Rockwell M of 100 [-] at 23 °C

ASTM D785

Impact strength, Izod unnotched, ASTM

IIzod,unnot,astm

91 J/m at 23 °C

Show Thermoset Polymer Matrix Composite materials with Impact strength, Izod unnotched, ASTM of 91 J/m at 23 °C

ASTM D256, Condition E-48/50

Impact strength, Izod unnotched, ASTM, Transversal

IIzod,unnot,astm,trans

75 J/m at 23 °C

Show Thermoset Polymer Matrix Composite materials with Impact strength, Izod unnotched, ASTM, Transversal of 75 J/m at 23 °C

ASTM D256, Condition E-48/50

Shear strength, transverse

τtrans

93.1 MPa at 23 °C

Show Thermoset Polymer Matrix Composite materials with Shear strength, transverse of 93.1 MPa at 23 °C

ASTM D732, Condition A

Tensile strength

Rm

75.8 MPa at 23 °C

Show Thermoset Polymer Matrix Composite materials with Tensile strength of 75.8 MPa at 23 °C

ASTM D638, Condition A

Tensile strength, transverse

Rm,trans

62.1 MPa at 23 °C

Show Thermoset Polymer Matrix Composite materials with Tensile strength, transverse of 62.1 MPa at 23 °C

ASTM D638, Condition A

Thermal

Coefficient of thermal expansion

α

1.8E-5 1/K at 23 °C

IPC-TM 650-2.4.24

Coefficient of thermal expansion, transverse

αtrans

2.4E-5 1/K at 23 °C

IPC-TM 650-2.4.24

Flammability

UL Bulletin 94, Class HB, Condition A

Relative temperature index, mechanical strength

RTIstr

145 °C

UL Bulletin 746b¹

Technological properties

Fillers

Cotton Fabric and MoS2

Modifications

Other

1.This temperature is a recommendation only, and based upon experience in various applications. The maximum operating temperature is dependent upon the application and should be investigated prior to use

Primary Phase

Secondary Phase

Supplier Disclaimer

This data, while believed to be accurate and based on reliable analytical methods, is for informational purposes only. The terms and conditions of the agreement under which it is sold will govern any sales of this product. Data supplied above are "typical values"; not to be considered "specification values".


To assure the material's performance is adequate for a specific application; customers should verify, independent of Norplex-Micarta, performance characteristics of interest.


It is the responsibility of the users of this information to make sure that they have the latest version of this TDB, and are urged to check with Customer Service or, preferably our web site, www.norplex-micarta.com, to determine if the information is the most current available.

This material data has been provided by Norplex Micarta.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.