Properties
General
| Property | Value | Testing Standard | Comment |
|---|---|---|---|
Bonding strength | 816.5 Kg Show Supplier Material materials with Bonding strength of 816.5 Kg | ASTM D229 | Condition A |
Density | 1.35 g/cm³ Show Supplier Material materials with Density of 1.35 g/cm³ | ASTM D792 | |
Moisture absorption | 4.2 % Show Supplier Material materials with Moisture absorption of 4.2 % | ASTM D570 | Condition A |
Mechanical
| Property | Value | Testing Standard | Comment |
|---|---|---|---|
Compressive strength | 172.4 MPa Show Supplier Material materials with Compressive strength of 172.4 MPa | ASTM D695 | Condition A | Flatwise |
Flexural modulus | 6.2 GPa Show Supplier Material materials with Flexural modulus of 6.2 GPa | ASTM D790 | Condition A, Transverse |
7.6 GPa Show Supplier Material materials with Flexural modulus of 7.6 GPa | ASTM D790 | Condition A | |
Flexural strength | 96.5 MPa Show Supplier Material materials with Flexural strength of 96.5 MPa | ASTM D790 | Condition A, Transverse |
117.2 MPa Show Supplier Material materials with Flexural strength of 117.2 MPa | ASTM D790 | Condition A | |
Hardness, Rockwell M | 90 [-] Show Supplier Material materials with Hardness, Rockwell M of 90 [-] | ASTM D785 | |
Impact strength, Izod unnotched, ASTM | 107 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 107 J/m | ASTM D256 | Condition E-48/50, Transverse |
133 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 133 J/m | ASTM D256 | Condition E-48/50 | |
Shear strength | 82.7 MPa Show Supplier Material materials with Shear strength of 82.7 MPa | ASTM D732 | Condition A, Transverse |
Tensile strength | 68.9 MPa Show Supplier Material materials with Tensile strength of 68.9 MPa | ASTM D638 | Condition A |
Thermal
| Property | Value | Comment | |
|---|---|---|---|
Relative temperature index, electrical | 125 °C Show Supplier Material materials with Relative temperature index, electrical of 125 °C | UL Bulletin 746b¹ | |
Relative temperature index, mechanical strength | 125 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 125 °C | UL Bulletin 746b¹ | |
Arc resistance | 10 seconds, ASTM D495, Condition A | ||
Flammability | UL Bulletin 94, Class HB, Condition A | ||
Electrical
| Property | Value | Testing Standard | Comment |
|---|---|---|---|
Breakdown voltage | 4 kV Show Supplier Material materials with Breakdown voltage of 4 kV | ASTM D149 | Condition D48/50 |
65 kV Show Supplier Material materials with Breakdown voltage of 65 kV | ASTM D149 | Condition A | |
Comparative tracking index | 150 V Show Supplier Material materials with Comparative tracking index of 150 V | ASTM D3638 | |
Dielectric strength | 13.78 kV/mm Show Supplier Material materials with Dielectric strength of 13.78 kV/mm | ASTM D149 | Condition D-48/50 |
18.9 kV/mm Show Supplier Material materials with Dielectric strength of 18.9 kV/mm | ASTM D149 | Condition A |
Technological properties
| Property | ||
|---|---|---|
| Fillers | Cotton Fabric | |
| Other | 1.This temperature is a recommendation only, and based upon experience in various applications. The maximum operating temperature is dependent upon the application and should be investigated prior to use | |
| Supplier Disclaimer | This data, while believed to be accurate and based on reliable analytical methods, is for informational purposes only. The terms and conditions of the agreement under which it is sold will govern any sales of this product. Data supplied above are "typical values"; not to be considered "specification values". To assure the material's performance is adequate for a specific application; customers should verify, independent of Norplex-Micarta, performance characteristics of interest. It is the responsibility of the users of this information to make sure that they have the latest version of this TDB, and are urged to check with Customer Service or, preferably our web site, www.norplex-micarta.com, to determine if the information is the most current available. | |