Properties
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Bonding strength | 23.0 °C | 1088 Kg Show Supplier Material materials with Bonding strength of 1088 Kg | ASTM D229, Condition A |
Density | 23.0 °C | 1.54 g/cm³ Show Supplier Material materials with Density of 1.54 g/cm³ | ASTM D792 |
Moisture absorption | 23.0 °C | 1.94 % Show Supplier Material materials with Moisture absorption of 1.94 % | ASTM D570, Condition Dᵢ-24/23 |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Compressive strength | 23.0 °C | 280.6 MPa Show Supplier Material materials with Compressive strength of 280.6 MPa | ASTM D695, Condition A, Flatwise |
Flexural strength | 23.0 °C | 201.3 - 253 MPa Show Supplier Material materials with Flexural strength of 201.3 - 253 MPa | ASTM D790, Condition E-1/150 (Min.) & A (Max.) |
Flexural strength, transverse | 23.0 °C | 106.9 - 120.7 MPa Show Supplier Material materials with Flexural strength, transverse of 106.9 - 120.7 MPa | ASTM D790, Condition E-1/150 (Min.) & A (Max.) |
Hardness, Rockwell M | 23.0 °C | 95 [-] Show Supplier Material materials with Hardness, Rockwell M of 95 [-] | ASTM D785 |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 1222 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 1222 J/m | ASTM D256, Condition E-48/50 |
Impact strength, Izod unnotched, ASTM, Transversal | 23.0 °C | 390 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM, Transversal of 390 J/m | ASTM D256, Condition E-48/50 |
Tensile strength | 23.0 °C | 176.5 MPa Show Supplier Material materials with Tensile strength of 176.5 MPa | ASTM D638, Condition A |
Tensile strength, transverse | 23.0 °C | 66.9 MPa Show Supplier Material materials with Tensile strength, transverse of 66.9 MPa | ASTM D638, Condition A |
Thermal
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 2.7E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 2.7E-5 1/K | IPC-TM 650-2.4.24 | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 3.98E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 3.98E-5 1/K | IPC-TM 650-2.4.24 | ||
Relative temperature index, mechanical strength | 165 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 165 °C | UL Bulletin 746b¹ | |||
Flammability | UL Bulletin 94, Class HB, Condition A | ||||
Technological properties
| Property | ||
|---|---|---|
| Application areas | Applications include wear plates for conveyor systems, valve plates, and compressor and pump vanes | |
| Fillers | Cotton Fabric | |
| Other | 1.This temperature is a recommendation only, and based upon experience in various applications. The maximum operating temperature is dependent upon the application and should be investigated prior to use | |
| Supplier Disclaimer | This data, while believed to be accurate and based on reliable analytical methods, is for informational purposes only. The terms and conditions of the agreement under which it is sold will govern any sales of this product. Data supplied above are "typical values"; not to be considered "specification values". To assure the material's performance is adequate for a specific application; customers should verify, independent of Norplex-Micarta, performance characteristics of interest. It is the responsibility of the users of this information to make sure that they have the latest version of this TDB, and are urged to check with Customer Service or, preferably our web site, www.norplex-micarta.com, to determine if the information is the most current available. | |