Phenolic NP101 - Sheet

Alternative and trade names
NEMA GRADE: N-1, U.L. LISTED: N
Want to keep this datasheet? Save it now in your required format

Description

Phenolic resin combined with spun nylon fabric. Good impact strength and excellent electrical properties under high humidity conditions.

Properties

General

Bonding strength

Fbond

816.5 Kg at 23 °C

ASTM D229, Condition A

Density

ρ

1.15 g/cm³ at 23 °C

ASTM D792

Moisture absorption

cmoisture

0.3 % at 23 °C

ASTM D570, Condition D₁-24/23

Mechanical

Compressive strength

Rmc

172.4 MPa at 23 °C

Show Thermoset Polymer Matrix Composite materials with Compressive strength of 172.4 MPa at 23 °C

ASTM D695, Condition A, Flatwise

Flexural modulus

Ebend

4.8 GPa at 23 °C

Show Thermoset Polymer Matrix Composite materials with Flexural modulus of 4.8 GPa at 23 °C

ASTM D790, Condition A

Flexural modulus, transverse

Ebend,trans

3.8 GPa at 23 °C

Show Thermoset Polymer Matrix Composite materials with Flexural modulus, transverse of 3.8 GPa at 23 °C

ASTM D790, Condition A

Flexural strength

σbend

124.1 MPa at 23 °C

Show Thermoset Polymer Matrix Composite materials with Flexural strength of 124.1 MPa at 23 °C

ASTM D790, Condition A

Flexural strength, transverse

σbendT

89.6 MPa at 23 °C

Show Thermoset Polymer Matrix Composite materials with Flexural strength, transverse of 89.6 MPa at 23 °C

ASTM D790, Condition A

Hardness, Rockwell M

HRM

90 [-] at 23 °C

Show Thermoset Polymer Matrix Composite materials with Hardness, Rockwell M of 90 [-] at 23 °C

ASTM D785

Impact strength, Izod unnotched, ASTM

IIzod,unnot,astm

480 J/m at 23 °C

Show Thermoset Polymer Matrix Composite materials with Impact strength, Izod unnotched, ASTM of 480 J/m at 23 °C

ASTM D256, Condition E-48/50

Impact strength, Izod unnotched, ASTM, Transversal

IIzod,unnot,astm,trans

320 J/m at 23 °C

Show Thermoset Polymer Matrix Composite materials with Impact strength, Izod unnotched, ASTM, Transversal of 320 J/m at 23 °C

ASTM D256, Condition E-48/50

Shear strength, transverse

τtrans

96.5 MPa at 23 °C

Show Thermoset Polymer Matrix Composite materials with Shear strength, transverse of 96.5 MPa at 23 °C

ASTM D732, Condition A

Tensile strength

Rm

55.2 MPa at 23 °C

Show Thermoset Polymer Matrix Composite materials with Tensile strength of 55.2 MPa at 23 °C

ASTM D638, Condition A

Tensile strength, transverse

Rm,trans

55.2 MPa at 23 °C

Show Thermoset Polymer Matrix Composite materials with Tensile strength, transverse of 55.2 MPa at 23 °C

ASTM D638, Condition A

Thermal

Arc resistance

80 seconds, ASTM D495, Condition A

Flammability

UL Bulletin 94, Class HB, Condition A

Relative temperature index, mechanical strength

RTIstr

105 °C

UL Bulletin 746b¹

Electrical

Breakdown voltage

Ubreak

45 - 65 kV at 23 °C

ASTM D149, Condition D48/50 (Min.) & A (Max.)

Comparative tracking index

CTI

150 V at 23 °C

ASTM D3638

Dielectric constant, 1MHz

εr,1MHz

3.75 [-] at 23 °C

ASTM D150, Condition D-24/23

Dielectric strength

EDS

19.69 - 25.59 kV/mm at 23 °C

ASTM D149, Condition D-48/50 (Min.) & A (Max.)

Dissipation factor, 1MHz

ε''1MHz

0.04 [-] at 23 °C

ASTM D150, Condition D-24/23

Technological properties

Fillers

Nylon

Other

1.This temperature is a recommendation only, and based upon experience in various applications. The maximum operating temperature is dependent upon the application and should be investigated prior to use

Primary Phase

Secondary Phase

Supplier Disclaimer

This data, while believed to be accurate and based on reliable analytical methods, is for informational purposes only. The terms and conditions of the agreement under which it is sold will govern any sales of this product. Data supplied above are "typical values"; not to be considered "specification values".


To assure the material's performance is adequate for a specific application; customers should verify, independent of Norplex-Micarta, performance characteristics of interest.


It is the responsibility of the users of this information to make sure that they have the latest version of this TDB, and are urged to check with Customer Service or, preferably our web site, www.norplex-micarta.com, to determine if the information is the most current available.

This material data has been provided by Norplex Micarta.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.