Properties
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Density | 23.0 °C | 1.2 g/cm³ Show Supplier Material materials with Density of 1.2 g/cm³ | ISO 1183 |
Mechanical
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Elastic modulus | 23.0 °C | 2.4 GPa Show Supplier Material materials with Elastic modulus of 2.4 GPa | ISO 527-2/1 | ||
Elongation | 23.0 °C | 50 % Show Supplier Material materials with Elongation of 50 % | ISO 527-2/50 | ||
Elongation at yield | 23.0 °C | 6 % Show Supplier Material materials with Elongation at yield of 6 % | ISO 527-2/50 | ||
Flexural modulus | 23.0 °C | 2.4 GPa Show Supplier Material materials with Flexural modulus of 2.4 GPa | ISO 178 | ||
Flexural strength | 23.0 °C | 94 MPa Show Supplier Material materials with Flexural strength of 94 MPa | ISO 178 | ||
Impact strength, Charpy notched | 23.0 °C | 71 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 71 kJ/m² | ISO 179 | ||
Yield strength | 23.0 °C | 61 MPa Show Supplier Material materials with Yield strength of 61 MPa | ISO 527-2/50 | ||
Impact strength, Charpy unnotched | ISO 179, no break | ||||
Thermal
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 7.5E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 7.5E-5 1/K | ISO 11359-2 | ||
Heat deflection temperature, 0.45 MPa | 141 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 141 °C | ISO 75-2/B | |||
Heat deflection temperature, 1.80 MPa | 128 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 128 °C | ISO 75-2/A | |||
Relative temperature index, electrical | 125 °C Show Supplier Material materials with Relative temperature index, electrical of 125 °C | UL 746 | |||
Relative temperature index, mechanical impact | 115 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 115 °C | UL 746 | |||
Relative temperature index, mechanical strength | 125 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 125 °C | UL 746 | |||
Vicat softening temperature | 148 °C Show Supplier Material materials with Vicat softening temperature of 148 °C | ISO 306/B50 | |||
Flammability | HB for 1.9mm and V-2 for 0.4mm UL94 | ||||
Electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Comparative tracking index | 23.0 °C | 250 V Show Supplier Material materials with Comparative tracking index of 250 V | IEC 60112 |
Dielectric constant, 100Hz | 23.0 °C | 3.1 [-] Show Supplier Material materials with Dielectric constant, 100Hz of 3.1 [-] | IEC 60250 |
Dielectric constant, 1MHz | 23.0 °C | 3 [-] Show Supplier Material materials with Dielectric constant, 1MHz of 3 [-] | IEC 60250 |
Dielectric strength | 23.0 °C | 30 kV/mm Show Supplier Material materials with Dielectric strength of 30 kV/mm | IEC 60243-1 |
Dissipation factor, 100Hz | 23.0 °C | 1E-3 [-] Show Supplier Material materials with Dissipation factor, 100Hz of 1E-3 [-] | IEC 60250 |
Dissipation factor, 1MHz | 23.0 °C | 9E-3 [-] Show Supplier Material materials with Dissipation factor, 1MHz of 9E-3 [-] | IEC 60250 |
Electrical resistivity | 23.0 °C | 1.00E+13 Ω·m Show Supplier Material materials with Electrical resistivity of 1.00E+13 Ω·m | IEC 60093 |
Surface resistivity | 23.0 °C | 1.00E+15 Ω/sq Show Supplier Material materials with Surface resistivity of 1.00E+15 Ω/sq | IEC 60093 |
Optical
Rheological Properties
| Property | Value | Comment |
|---|---|---|
Melt mass-flow rate | 12 g/10min Show Supplier Material materials with Melt mass-flow rate of 12 g/10min | ISO 1133 |
Technological properties
| Property | ||
|---|---|---|
| Application areas | AUTOMOTIVE APPLICATIONS, GENERAL PURPOSE, LEDS | |