General
Property | Temperature | Value | Condition | Related Standards | Shape |
---|---|---|---|---|---|
Density | 2.84 g/cm³ Show Material materials with Density of 2.84 g/cm³ | T6 | WL 3.1754 | Casting | |
20.0 °C | 2.84 g/cm³ Show Material materials with Density of 2.84 g/cm³ | T6 | WL 3.1854, WL 3.1754 |
Mechanical
Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|---|
Elastic modulus | 70.0 GPa Show Material materials with Elastic modulus of 70.0 GPa | T6 | WL 3.1754 | Casting | ||
20.0 °C | 70.0 GPa Show Material materials with Elastic modulus of 70.0 GPa | T6 | WL 3.1854, WL 3.1754 | |||
Elongation | 1.0 % Show Material materials with Elongation of 1.0 % | T6 | WL 3.1754 | Casting | A50 | |
20.0 °C | 1.0 % Show Material materials with Elongation of 1.0 % | T6 | WL 3.1854, WL 3.1754 | |||
Hardness, Brinell | 80.0 [-] Show Material materials with Hardness, Brinell of 80.0 [-] | T6 | WL 3.1754 | Casting | ||
20.0 °C | 80.0 [-] Show Material materials with Hardness, Brinell of 80.0 [-] | T6 | WL 3.1854, WL 3.1754 | |||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Cast 2xx.x Series Aluminium | ||||
Tensile strength | 180.0 MPa Show Material materials with Tensile strength of 180.0 MPa | T6 | WL 3.1754 | Casting | ||
190.0 MPa Show Material materials with Tensile strength of 190.0 MPa | T6 | WL 3.1754 | Casting | |||
20.0 °C | 180.0 MPa Show Material materials with Tensile strength of 180.0 MPa | T6 | WL 3.1854, WL 3.1754 | |||
20.0 °C | 185.0 MPa Show Material materials with Tensile strength of 185.0 MPa | T6 | WL 3.1854, WL 3.1754 | |||
20.0 °C | 190.0 MPa Show Material materials with Tensile strength of 190.0 MPa | T6 | WL 3.1854, WL 3.1754 | |||
20.0 °C | 200.0 MPa Show Material materials with Tensile strength of 200.0 MPa | T6 | WL 3.1854, WL 3.1754 | |||
20.0 °C | 215.0 MPa Show Material materials with Tensile strength of 215.0 MPa | T6 | WL 3.1854, WL 3.1754 |
Thermal
Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 1.9999999999999998e-05 1/K Show Material materials with Coefficient of thermal expansion of 1.9999999999999998e-05 1/K | T6 | WL 3.1754 | Casting | |
100 °C | 1.9999999999999998e-05 1/K Show Material materials with Coefficient of thermal expansion of 1.9999999999999998e-05 1/K | T6 | WL 3.1754 | Casting | ||
Melting point | 510.0 - 790.0 °C Show Material materials with Melting point of 510.0 - 790.0 °C | Typical for Cast 2xx.x Series Aluminium | ||||
Specific heat capacity | 875.0 - 963.0 J/(kg·K) Show Material materials with Specific heat capacity of 875.0 - 963.0 J/(kg·K) | Typical for Cast 2xx.x Series Aluminium | ||||
Thermal conductivity | 155 W/(m·K) Show Material materials with Thermal conductivity of 155 W/(m·K) | T6 | WL 3.1754 | Casting | ||
20.0 °C | 155.0 W/(m·K) Show Material materials with Thermal conductivity of 155.0 W/(m·K) | T6 | WL 3.1854, WL 3.1754 |
Electrical
Property | Temperature | Value | Condition | Related Standards | Shape |
---|---|---|---|---|---|
Electrical conductivity | 21000000.0 S/m Show Material materials with Electrical conductivity of 21000000.0 S/m | T6 | WL 3.1754 | Casting | |
20.0 °C | 21000000.0 S/m Show Material materials with Electrical conductivity of 21000000.0 S/m | T6 | WL 3.1854, WL 3.1754 | ||
Electrical resistivity | 4.76e-08 Ω·m Show Material materials with Electrical resistivity of 4.76e-08 Ω·m | T6 | WL 3.1754 | Casting |
Chemical properties
Property | Value | Condition | Related Standards | Shape |
---|---|---|---|---|
Aluminium | 93.4 % Show Material materials with Aluminium of 93.4 % | T6 | WL 3.1854, WL 3.1754 | |
Copper | 4.2 - 5.0 % Show Material materials with Copper of 4.2 - 5.0 % | T6 | WL 3.1854, WL 3.1754 | |
4.5 - 5.5 % Show Material materials with Copper of 4.5 - 5.5 % | T6 | WL 3.1754 | Casting | |
Iron | 0.35 % Show Material materials with Iron of 0.35 % | T6 | WL 3.1854, WL 3.1754 | |
0.50 % Show Material materials with Iron of 0.50 % | T6 | WL 3.1754 | Casting | |
Magnesium | 0.15 - 0.35 % Show Material materials with Magnesium of 0.15 - 0.35 % | T6 | WL 3.1854, WL 3.1754 | |
Manganese | 0.1 % Show Material materials with Manganese of 0.1 % | T6 | WL 3.1854, WL 3.1754 | |
0.2 - 0.3 % Show Material materials with Manganese of 0.2 - 0.3 % | T6 | WL 3.1754 | Casting | |
Nickel | 0.03 % Show Material materials with Nickel of 0.03 % | T6 | WL 3.1854, WL 3.1754 | |
1.3 - 1.8 % Show Material materials with Nickel of 1.3 - 1.8 % | T6 | WL 3.1754 | Casting | |
Silicon | 0.3 % Show Material materials with Silicon of 0.3 % | T6 | WL 3.1854, WL 3.1754 | Casting |
Titanium | 0.15 - 0.25 % Show Material materials with Titanium of 0.15 - 0.25 % | T6 | WL 3.1854, WL 3.1754 | Casting |
Zinc | 0.1 Show Material materials with Zinc of 0.1 | T6 | WL 3.1854, WL 3.1754 | |
Zirconium | 0.1 - 0.3 % Show Material materials with Zirconium of 0.1 - 0.3 % | T6 | WL 3.1754 | Casting |
Technological properties
Property | ||
---|---|---|
Processing methods | investment casting, sample taken from casting |