General
Property | Temperature | Value | Condition | Related Standards |
---|---|---|---|---|
Density | 20.0 °C | 2.7 g/cm³ Show Material materials with Density of 2.7 g/cm³ | H3x | WL 3.2134 |
Mechanical
Property | Temperature | Value | Condition | Related Standards | Comment |
---|---|---|---|---|---|
Elastic modulus | 20.0 °C | 71.0 GPa Show Material materials with Elastic modulus of 71.0 GPa | H3x | WL 3.2134 | |
Elongation | 20.0 °C | 0.5 % Show Material materials with Elongation of 0.5 % | H3x | WL 3.2134 | |
20.0 °C | 1.0 % Show Material materials with Elongation of 1.0 % | H3x | WL 3.2134 | ||
20.0 °C | 1.5 % Show Material materials with Elongation of 1.5 % | H3x | WL 3.2134 | ||
20.0 °C | 2.0 % Show Material materials with Elongation of 2.0 % | H3x | WL 3.2134 | ||
Hardness, Brinell | 20.0 °C | 60.0 [-] Show Material materials with Hardness, Brinell of 60.0 [-] | H3x | WL 3.2134 | |
20.0 °C | 65.0 [-] Show Material materials with Hardness, Brinell of 65.0 [-] | H3x | WL 3.2134 | ||
20.0 °C | 70.0 [-] Show Material materials with Hardness, Brinell of 70.0 [-] | H3x | WL 3.2134 | ||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Cast 3xx.x Series Aluminium | |||
Shear modulus | 2.8 GPa Show Material materials with Shear modulus of 2.8 GPa | Typical for Cast 3xx.x Series Aluminium | |||
Shear strength | 20.0 °C | 120.0 MPa Show Material materials with Shear strength of 120.0 MPa | H3x | WL 3.2134 | |
20.0 °C | 160.0 MPa Show Material materials with Shear strength of 160.0 MPa | H3x | WL 3.2134 | ||
Tensile strength | 20.0 °C | 150.0 MPa Show Material materials with Tensile strength of 150.0 MPa | H3x | WL 3.2134 | |
20.0 °C | 160.0 MPa Show Material materials with Tensile strength of 160.0 MPa | H3x | WL 3.2134 | ||
20.0 °C | 180.0 MPa Show Material materials with Tensile strength of 180.0 MPa | H3x | WL 3.2134 | ||
20.0 °C | 190.0 MPa Show Material materials with Tensile strength of 190.0 MPa | H3x | WL 3.2134 |
Thermal
Property | Value | Comment |
---|---|---|
Coefficient of thermal expansion | 1.6e-05 - 2.3e-05 1/K Show Material materials with Coefficient of thermal expansion of 1.6e-05 - 2.3e-05 1/K | Typical for Cast 3xx.x Series Aluminium |
Melting point | 505.0 - 770.0 °C Show Material materials with Melting point of 505.0 - 770.0 °C | Typical for Cast 3xx.x Series Aluminium |
Specific heat capacity | 960.0 - 963.0 J/(kg·K) Show Material materials with Specific heat capacity of 960.0 - 963.0 J/(kg·K) | Typical for Cast 3xx.x Series Aluminium |
Thermal conductivity | 130.0 - 180.0 W/(m·K) Show Material materials with Thermal conductivity of 130.0 - 180.0 W/(m·K) | Typical for Cast 3xx.x Series Aluminium |
Chemical properties
Property | Value | Condition | Related Standards |
---|---|---|---|
Chromium | 0.25 Show Material materials with Chromium of 0.25 | H3x | WL 3.2134 |
Copper | 1.0 - 1.5 % Show Material materials with Copper of 1.0 - 1.5 % | H3x | WL 3.2134 |
Iron | 0.6 Show Material materials with Iron of 0.6 | H3x | WL 3.2134 |
Magnesium | 0.4 - 0.6 % Show Material materials with Magnesium of 0.4 - 0.6 % | H3x | WL 3.2134 |
Manganese | 0.5 Show Material materials with Manganese of 0.5 | H3x | WL 3.2134 |
Silicon | 4.5 - 5.5 % Show Material materials with Silicon of 4.5 - 5.5 % | H3x | WL 3.2134 |
Titanium | 0.25 Show Material materials with Titanium of 0.25 | H3x | WL 3.2134 |
Zinc | 0.3 Show Material materials with Zinc of 0.3 | H3x | WL 3.2134 |
Technological properties
Property | ||
---|---|---|
Processing methods | permanent mould casting |