WL 3.2364 Grade 3.2364 H3x

Want to keep this datasheet? Save it now in your required format

Description

Very good weldable cast material with very good casting properties. Castings are sensitive to impact loads. Application: fittings

Related Standards

WL 3.2364

Equivalent Materials

This material data has been provided by WIAM.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Properties

General

Property	Temperature	Value	Condition	Related Standards
Density	20.0 °C	2.7 g/cm³ Show Material materials with Density of 2.7 g/cm³	H3x	WL 3.2364

Mechanical

Property	Temperature	Value	Condition	Related Standards	Comment
Elastic modulus	20.0 °C	70.6 GPa Show Material materials with Elastic modulus of 70.6 GPa	H3x	WL 3.2364
Elongation	20.0 °C	2.0 % Show Material materials with Elongation of 2.0 %	H3x	WL 3.2364
Hardness, Brinell	20.0 °C	60.0 [-] Show Material materials with Hardness, Brinell of 60.0 [-]	H3x	WL 3.2364
	20.0 °C	65.0 [-] Show Material materials with Hardness, Brinell of 65.0 [-]	H3x	WL 3.2364
	20.0 °C	70.0 [-] Show Material materials with Hardness, Brinell of 70.0 [-]	H3x	WL 3.2364
Poisson's ratio		0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-]			Typical for Cast 3xx.x Series Aluminium
Shear modulus		2.8 GPa Show Material materials with Shear modulus of 2.8 GPa			Typical for Cast 3xx.x Series Aluminium
Shear strength	20.0 °C	137.0 MPa Show Material materials with Shear strength of 137.0 MPa	H3x	WL 3.2364
Tensile strength	20.0 °C	118.0 MPa Show Material materials with Tensile strength of 118.0 MPa	H3x	WL 3.2364
	20.0 °C	137.0 MPa Show Material materials with Tensile strength of 137.0 MPa	H3x	WL 3.2364
	20.0 °C	157.0 MPa Show Material materials with Tensile strength of 157.0 MPa	H3x	WL 3.2364
	20.0 °C	186.0 MPa Show Material materials with Tensile strength of 186.0 MPa	H3x	WL 3.2364

Thermal

Property	Value	Comment
Coefficient of thermal expansion	1.6e-05 - 2.3e-05 1/K Show Material materials with Coefficient of thermal expansion of 1.6e-05 - 2.3e-05 1/K	Typical for Cast 3xx.x Series Aluminium
Melting point	505.0 - 770.0 °C Show Material materials with Melting point of 505.0 - 770.0 °C	Typical for Cast 3xx.x Series Aluminium
Specific heat capacity	960.0 - 963.0 J/(kg·K) Show Material materials with Specific heat capacity of 960.0 - 963.0 J/(kg·K)	Typical for Cast 3xx.x Series Aluminium
Thermal conductivity	130.0 - 180.0 W/(m·K) Show Material materials with Thermal conductivity of 130.0 - 180.0 W/(m·K)	Typical for Cast 3xx.x Series Aluminium

Chemical properties

Property	Value	Condition	Related Standards
Copper	0.2 Show Material materials with Copper of 0.2	H3x	WL 3.2364
Iron	0.6 Show Material materials with Iron of 0.6	H3x	WL 3.2364
Magnesium	0.2 - 0.4 % Show Material materials with Magnesium of 0.2 - 0.4 %	H3x	WL 3.2364
Manganese	0.35 Show Material materials with Manganese of 0.35	H3x	WL 3.2364
Silicon	6.5 - 7.5 % Show Material materials with Silicon of 6.5 - 7.5 %	H3x	WL 3.2364
Titanium	0.25 Show Material materials with Titanium of 0.25	H3x	WL 3.2364
Zinc	0.3 Show Material materials with Zinc of 0.3	H3x	WL 3.2364

Technological properties

Property

Processing methods

permanent mould casting, sample taken from casting