EN 573-3 Grade AW-5049 H34

Want to keep this datasheet? Save it now in your required format

Description

Material EN AW-Al Mg2Mn0,8 is produced for sheet metal, strip and plates, for HF-welded tubes as well as for rolled billets. The material is food-safe. To the comparable mark AlMg2Mn0,8, material No. 3.0527 acc. to DIN 1725-1 : 1983-02 applies: The alloy AlMg2Mn0,8 is similar to alloy AlMg3. Mn-addition (above 0,6 %) causes an increase of high-temperature strength (up to approx. 150°C) and recrystallization barrier. As a result of this considerably increases strength of extrusion products in longitudinal direction. The material has a high resistance to corrosion, seawater and salted atmospere. Strength increases and cold workability decreases according to the Mg-content. It is naturally hard, i.e. a strength increase can only be achieved by cold forming, not by controlled heat treatment. Machinability and weldability are enhanced by increasing Mg-content. Application: In apparatus engineering for pressure tanks, for pressure gas tanks (pipelines), for low-temperature tanks and for temperatures up to 250°C. In car manufacturing for coachbuilding, in shipbuilding for hull and superstructure. In construction trade for roofing, facade lining, for load-carrying constructions and sun protection facilities as well as for furniture (incl. camping furniture).

Related Standards

Equivalent Materials

This material data has been provided by WIAM,Aludium,AluKey.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

2.71 g/cm³

Show Material materials with Density of 2.71 g/cm³

23.0 °C

2.7 - 2.71 g/cm³

Show Material materials with Density of 2.7 - 2.71 g/cm³

Dimension

PropertyValue

Thickness

0.2 - 6 mm

Show Material materials with Thickness of 0.2 - 6 mm

Mechanical

PropertyTemperatureValueComment

Bending angle 180°

23.0 °C

2.5 °/t

Show Material materials with Bending angle 180° of 2.5 °/t

Bending angle 90°

23.0 °C

1 - 3 °/t

Show Material materials with Bending angle 90° of 1 - 3 °/t

Elastic modulus

-270.0 °C

70 GPa

Show Material materials with Elastic modulus of 70 GPa

20.0 °C

70 GPa

Show Material materials with Elastic modulus of 70 GPa

23.0 °C

70 GPa

Show Material materials with Elastic modulus of 70 GPa

50.0 °C

69 GPa

Show Material materials with Elastic modulus of 69 GPa

100.0 °C

68 GPa

Show Material materials with Elastic modulus of 68 GPa

150.0 °C

66 GPa

Show Material materials with Elastic modulus of 66 GPa

200.0 °C

63 GPa

Show Material materials with Elastic modulus of 63 GPa

250.0 °C

57 GPa

Show Material materials with Elastic modulus of 57 GPa

300.0 °C

50 GPa

Show Material materials with Elastic modulus of 50 GPa

Unlock all property charts

Elongation

20.0 °C

8 %

Show Material materials with Elongation of 8 %

Elongation A100

23.0 °C

7 - 8 %

Show Material materials with Elongation A100 of 7 - 8 %

Elongation A50

20.0 °C

6 - 10 %

Show Material materials with Elongation A50 of 6 - 10 %

23.0 °C

6 - 10 %

Show Material materials with Elongation A50 of 6 - 10 %

Unlock all property charts

Elongation A50, transverse

20.0 °C

6 - 10 %

Show Material materials with Elongation A50, transverse of 6 - 10 %

Elongation, transverse

20.0 °C

8 %

Show Material materials with Elongation, transverse of 8 %

Hardness, Brinell

20.0 °C

63 - 70 [-]

Show Material materials with Hardness, Brinell of 63 - 70 [-]

23.0 °C

70 [-]

Show Material materials with Hardness, Brinell of 70 [-]

Unlock all property charts

Hardness, HBW

23.0 °C

70 [-]

Show Material materials with Hardness, HBW of 70 [-]

Plane-Strain Fracture Toughnes

23.0 °C

22 - 35 MPa·√m

Show Material materials with Plane-Strain Fracture Toughnes of 22 - 35 MPa·√m

Typical for Wrought 5000 Series Aluminium

Poisson's ratio

23.0 °C

0.33 [-]

Show Material materials with Poisson's ratio of 0.33 [-]

Typical for Wrought 5000 Series Aluminium

Shear modulus

20.0 °C

26.5 GPa

Show Material materials with Shear modulus of 26.5 GPa

23.0 °C

26.5 GPa

Show Material materials with Shear modulus of 26.5 GPa

Unlock all property charts

Tensile strength

20.0 °C

240 - 280 MPa

Show Material materials with Tensile strength of 240 - 280 MPa

23.0 °C

220 - 280 MPa

Show Material materials with Tensile strength of 220 - 280 MPa

Unlock all property charts

Tensile strength, transverse

20.0 °C

240 - 280 MPa

Show Material materials with Tensile strength, transverse of 240 - 280 MPa

Yield strength

23.0 °C

160 MPa

Show Material materials with Yield strength of 160 MPa

Yield strength Rp0.2

20.0 °C

160 MPa

Show Material materials with Yield strength Rp0.2 of 160 MPa

23.0 °C

160 - 170 MPa

Show Material materials with Yield strength Rp0.2 of 160 - 170 MPa

Unlock all property charts

Yield strength Rp0.2, transverse

20.0 °C

160 MPa

Show Material materials with Yield strength Rp0.2, transverse of 160 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

20.0 °C

2.37E-5 1/K

Show Material materials with Coefficient of thermal expansion of 2.37E-5 1/K

20-100°C

100.0 °C

2.37E-5 - 2.4E-5 1/K

Show Material materials with Coefficient of thermal expansion of 2.37E-5 - 2.4E-5 1/K

20-100°C

Unlock all property charts

Max service temperature

150 °C

Show Material materials with Max service temperature of 150 °C

Typical for Wrought 5000 Series Aluminium

Max service temperature, long

0 - 150 °C

Show Material materials with Max service temperature, long of 0 - 150 °C

Melting point

620 - 650 °C

Show Material materials with Melting point of 620 - 650 °C

Specific heat capacity

23.0 °C

879 - 963 J/(kg·K)

Show Material materials with Specific heat capacity of 879 - 963 J/(kg·K)

Typical for Wrought 5000 Series Aluminium

Thermal conductivity

20.0 °C

140 - 180 W/(m·K)

Show Material materials with Thermal conductivity of 140 - 180 W/(m·K)

23.0 °C

140 - 180 W/(m·K)

Show Material materials with Thermal conductivity of 140 - 180 W/(m·K)

Unlock all property charts

Electrical

PropertyTemperatureValue

Electrical conductivity

20.0 °C

2.00E+7 - 2.50E+7 S/m

Show Material materials with Electrical conductivity of 2.00E+7 - 2.50E+7 S/m

23.0 °C

2.00E+7 - 2.50E+7 S/m

Show Material materials with Electrical conductivity of 2.00E+7 - 2.50E+7 S/m

Unlock all property charts

Electrical resistivity

23.0 °C

4E-8 - 5E-8 Ω·m

Show Material materials with Electrical resistivity of 4E-8 - 5E-8 Ω·m

Chemical properties

PropertyValueComment

Chromium

0.3 %

Show Material materials with Chromium of 0.3 %

Copper

0.1 %

Show Material materials with Copper of 0.1 %

Iron

0.5 %

Show Material materials with Iron of 0.5 %

Magnesium

1.6 - 2.5 %

Show Material materials with Magnesium of 1.6 - 2.5 %

Manganese

0.5 - 1.1 %

Show Material materials with Manganese of 0.5 - 1.1 %

Other

0.05 - 0.15 %

Show Material materials with Other of 0.05 - 0.15 %

each 0.05, total 0.15, Rest Al

Silicon

0.4 %

Show Material materials with Silicon of 0.4 %

Titanium

0.1 %

Show Material materials with Titanium of 0.1 %

Zinc

0.2 %

Show Material materials with Zinc of 0.2 %

Technological properties

Property
Anodizing

Excellent (anodizing quality)

Application areas

Components: General trasportation

Brazing

Poor

Corrosion properties

Excellent

Welding

Very Good

Workability

Very Good (in O temper)