EN 573-3 Grade AW-5050 H18

Want to keep this datasheet? Save it now in your required format

Description

Material EN AW-Al Mg1,5(C) is produced for sheet metal, strip and plates. It is food-safe and it is used for prematerial for cans, caps and stoppers.

Related Standards

Equivalent Materials

This material data has been provided by WIAM,AluKey,Aludium.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueTemperature

Density

2.68 - 2.69 g/cm³

Show Material materials with Density of 2.68 - 2.69 g/cm³ at 23.0 °C

23.0 °C

Dimension

PropertyValue

Thickness

0.2 - 6 mm

Show Material materials with Thickness of 0.2 - 6 mm

Mechanical

PropertyValueTemperatureComment

Bending angle 180°

0 °/t

Show Material materials with Bending angle 180° of 0 °/t at 23.0 °C

23.0 °C

Bending angle 90°

0 - 2.5 °/t

Show Material materials with Bending angle 90° of 0 - 2.5 °/t at 23.0 °C

23.0 °C

Elastic modulus

68.6 - 70 GPa

Show Material materials with Elastic modulus of 68.6 - 70 GPa at 23.0 °C

23.0 °C

Elongation A50

1 - 2 %

Show Material materials with Elongation A50 of 1 - 2 % at 20.0 °C

20.0 °C

1 - 2 %

Show Material materials with Elongation A50 of 1 - 2 % at 23.0 °C

23.0 °C

Elongation A50, transverse

1 - 2 %

Show Material materials with Elongation A50, transverse of 1 - 2 % at 20.0 °C

20.0 °C

Hardness, Brinell

68 [-]

Show Material materials with Hardness, Brinell of 68 [-] at 20.0 °C

20.0 °C

68 [-]

Show Material materials with Hardness, Brinell of 68 [-] at 23.0 °C

23.0 °C

Unlock all property charts

Hardness, HBW

68 [-]

Show Material materials with Hardness, HBW of 68 [-] at 23.0 °C

23.0 °C

Plane-Strain Fracture Toughnes

22 - 35 MPa·√m

Show Material materials with Plane-Strain Fracture Toughnes of 22 - 35 MPa·√m at 23.0 °C

23.0 °C

Typical for Wrought 5000 Series Aluminium

Poisson's ratio

0.33 [-]

Show Material materials with Poisson's ratio of 0.33 [-] at 23.0 °C

23.0 °C

Typical for Wrought 5000 Series Aluminium

Shear modulus

26.5 GPa

Show Material materials with Shear modulus of 26.5 GPa at 23.0 °C

23.0 °C

Tensile strength

220 MPa

Show Material materials with Tensile strength of 220 MPa at 20.0 °C

20.0 °C

220 MPa

Show Material materials with Tensile strength of 220 MPa at 23.0 °C

23.0 °C

Unlock all property charts

Tensile strength, transverse

220 MPa

Show Material materials with Tensile strength, transverse of 220 MPa at 20.0 °C

20.0 °C

Yield strength

190 MPa

Show Material materials with Yield strength of 190 MPa at 23.0 °C

23.0 °C

Yield strength Rp0.2

190 MPa

Show Material materials with Yield strength Rp0.2 of 190 MPa at 20.0 °C

20.0 °C

190 MPa

Show Material materials with Yield strength Rp0.2 of 190 MPa at 23.0 °C

23.0 °C

Unlock all property charts

Yield strength Rp0.2, transverse

190 MPa

Show Material materials with Yield strength Rp0.2, transverse of 190 MPa at 20.0 °C

20.0 °C

Thermal

PropertyValueTemperatureComment

Coefficient of thermal expansion

2.38E-5 1/K

Show Material materials with Coefficient of thermal expansion of 2.38E-5 1/K at 20.0 °C

20.0 °C

20-100°C

2.38E-5 - 2.4E-5 1/K

Show Material materials with Coefficient of thermal expansion of 2.38E-5 - 2.4E-5 1/K at 100.0 °C

100.0 °C

20-100°C

Unlock all property charts

Max service temperature

150 °C

Show Material materials with Max service temperature of 150 °C

Typical for Wrought 5000 Series Aluminium

Melting point

620 - 650 °C

Show Material materials with Melting point of 620 - 650 °C

Specific heat capacity

879 - 963 J/(kg·K)

Show Material materials with Specific heat capacity of 879 - 963 J/(kg·K) at 23.0 °C

23.0 °C

Typical for Wrought 5000 Series Aluminium

Thermal conductivity

170 - 193 W/(m·K)

Show Material materials with Thermal conductivity of 170 - 193 W/(m·K) at 23.0 °C

23.0 °C

Electrical

PropertyValueTemperature

Electrical conductivity

2.30E+7 - 2.90E+7 S/m

Show Material materials with Electrical conductivity of 2.30E+7 - 2.90E+7 S/m at 23.0 °C

23.0 °C

Electrical resistivity

3.4E-8 - 4.35E-8 Ω·m

Show Material materials with Electrical resistivity of 3.4E-8 - 4.35E-8 Ω·m at 23.0 °C

23.0 °C

Chemical properties

Property

Chromium

0.1 %

Copper

0.2 %

Iron

0.7 %

Magnesium

1.1 - 1.8 %

Manganese

0.1 - 0.3 %

Other

each 0.05, total 0.10, Rest Al

Silicon

0.4 %

Zinc

0.25 %

Technological properties

Property
Anodizing

Very Good (anodizing quality)

Application areas

Roofing: Single sheet, Sheets for composites/ sandwich Panels; Interiors and ceilings: Single sheet, Sheets for composites/ sandwich Panels, Sheets for mechanized panels, Decoration; Anodizing quality; Tubes: Industrial tubes, Pipes; Food can: Body, Lids

Brazing

Good

Corrosion properties

Excellent

General machinability

Fair

Welding

Excellent

Workability

Very Good