EN 573-3 Grade AW-5050 H28

Want to keep this datasheet? Save it now in your required format

Description

Material EN AW-Al Mg1,5(C) is produced for sheet metal, strip and plates. It is food-safe and it is used for prematerial for cans, caps and stoppers.

Related Standards

Equivalent Materials

This material data has been provided by WIAM,AluKey.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueTemperature

Density

2.68 - 2.69 g/cm³

Show Material materials with Density of 2.68 - 2.69 g/cm³ at 23.0 °C

23.0 °C

Mechanical

PropertyValueTemperatureComment

Bending angle 90°

1.5 - 2.5 °/t

Show Material materials with Bending angle 90° of 1.5 - 2.5 °/t at 23.0 °C

23.0 °C

Elastic modulus

69 - 70 GPa

Show Material materials with Elastic modulus of 69 - 70 GPa at 23.0 °C

23.0 °C

Elongation A50

1 - 3 %

Show Material materials with Elongation A50 of 1 - 3 % at 20.0 °C

20.0 °C

1 - 3 %

Show Material materials with Elongation A50 of 1 - 3 % at 23.0 °C

23.0 °C

Elongation A50, transverse

1 - 3 %

Show Material materials with Elongation A50, transverse of 1 - 3 % at 20.0 °C

20.0 °C

Hardness, Brinell

58 - 67 [-]

Show Material materials with Hardness, Brinell of 58 - 67 [-] at 20.0 °C

20.0 °C

67 [-]

Show Material materials with Hardness, Brinell of 67 [-] at 23.0 °C

23.0 °C

Unlock all property charts

Plane-Strain Fracture Toughnes

22 - 35 MPa·√m

Show Material materials with Plane-Strain Fracture Toughnes of 22 - 35 MPa·√m at 23.0 °C

23.0 °C

Typical for Wrought 5000 Series Aluminium

Poisson's ratio

0.33 [-]

Show Material materials with Poisson's ratio of 0.33 [-] at 23.0 °C

23.0 °C

Typical for Wrought 5000 Series Aluminium

Shear modulus

26 - 26.5 GPa

Show Material materials with Shear modulus of 26 - 26.5 GPa at 23.0 °C

23.0 °C

Typical for Wrought 5000 Series Aluminium

Tensile strength

185 - 220 MPa

Show Material materials with Tensile strength of 185 - 220 MPa at 20.0 °C

20.0 °C

220 MPa

Show Material materials with Tensile strength of 220 MPa at 23.0 °C

23.0 °C

Unlock all property charts

Tensile strength, transverse

220 MPa

Show Material materials with Tensile strength, transverse of 220 MPa at 20.0 °C

20.0 °C

Yield strength Rp0.2

160 - 180 MPa

Show Material materials with Yield strength Rp0.2 of 160 - 180 MPa at 20.0 °C

20.0 °C

180 MPa

Show Material materials with Yield strength Rp0.2 of 180 MPa at 23.0 °C

23.0 °C

Unlock all property charts

Yield strength Rp0.2, transverse

180 MPa

Show Material materials with Yield strength Rp0.2, transverse of 180 MPa at 20.0 °C

20.0 °C

Thermal

PropertyValueTemperatureComment

Coefficient of thermal expansion

2.38E-5 1/K

Show Material materials with Coefficient of thermal expansion of 2.38E-5 1/K at 20.0 °C

20.0 °C

2.38E-5 1/K

Show Material materials with Coefficient of thermal expansion of 2.38E-5 1/K at 100.0 °C

100.0 °C

Unlock all property charts

Max service temperature

150 °C

Show Material materials with Max service temperature of 150 °C

Typical for Wrought 5000 Series Aluminium

Melting point

620 - 650 °C

Show Material materials with Melting point of 620 - 650 °C

Specific heat capacity

879 - 963 J/(kg·K)

Show Material materials with Specific heat capacity of 879 - 963 J/(kg·K) at 23.0 °C

23.0 °C

Typical for Wrought 5000 Series Aluminium

Thermal conductivity

170 - 193 W/(m·K)

Show Material materials with Thermal conductivity of 170 - 193 W/(m·K) at 23.0 °C

23.0 °C

Electrical

PropertyValueTemperature

Electrical conductivity

2.30E+7 - 2.90E+7 S/m

Show Material materials with Electrical conductivity of 2.30E+7 - 2.90E+7 S/m at 23.0 °C

23.0 °C

Electrical resistivity

3.45E-8 - 4.35E-8 Ω·m

Show Material materials with Electrical resistivity of 3.45E-8 - 4.35E-8 Ω·m at 23.0 °C

23.0 °C

Chemical properties

Property

Chromium

0.1 %

Copper

0.2 %

Iron

0.7 %

Magnesium

1.1 - 1.8 %

Manganese

0.1 - 0.3 %

Other

each 0.05, total 0.10, Rest Al

Silicon

0.4 %

Zinc

0.25 %

Technological properties

Property
Workability

Good workability.