EN 573-3 Grade AW-1080A H18

Want to keep this datasheet? Save it now in your required format

Description

Material EN AW-Al 99,8(A) is produced in large quantities for sheets, strips, plates, scraps, rolled bars and wire and prewire for mechanical resp. welding application. It is used in limited quantities for pressed bars as well as for presswork components. It is food-safe. The material is comparable to trademark Al99,8, material number 3.0285, acc. to DIN 1712-3 : 1976-12. EN AW-Al 99,8(A) is well anodizable and shows favorable electrical and thermal conductivity. Smearing may occur on machining. Low mechanical strength, high strain. Formability as well as chemical and weathering resistance are excellent. Application: apparatus engineering, roll bond, Z-bond, household appliances, storage and transport equipment for chemical, pharmaceutical and food industry. Furthermore for roofings, facings, arts-and-crafts, packagings, extruded parts, e.g. collapsible tubes, tubes, cans, bottles.

Related Standards

Equivalent Materials

This material data has been provided by WIAM,AluKey,Aludium.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueTemperature

Density

2.7 g/cm³

Show Material materials with Density of 2.7 g/cm³ at 20.0 °C

20.0 °C

2.69 - 2.7 g/cm³

Show Material materials with Density of 2.69 - 2.7 g/cm³ at 23.0 °C

23.0 °C

Dimension

PropertyValue

Thickness

0.2 - 3 mm

Show Material materials with Thickness of 0.2 - 3 mm

Mechanical

PropertyValueTemperatureComment

Bending angle 90°

1 - 2.5 °/t

Show Material materials with Bending angle 90° of 1 - 2.5 °/t at 23.0 °C

23.0 °C

according to EN 485-2

Elastic modulus

70 GPa

Show Material materials with Elastic modulus of 70 GPa at -270.0 °C

-270.0 °C

60 - 70 GPa

Show Material materials with Elastic modulus of 60 - 70 GPa at 20.0 °C

20.0 °C

70 GPa

Show Material materials with Elastic modulus of 70 GPa at 23.0 °C

23.0 °C

69 GPa

Show Material materials with Elastic modulus of 69 GPa at 50.0 °C

50.0 °C

68 GPa

Show Material materials with Elastic modulus of 68 GPa at 100.0 °C

100.0 °C

66 GPa

Show Material materials with Elastic modulus of 66 GPa at 150.0 °C

150.0 °C

63 GPa

Show Material materials with Elastic modulus of 63 GPa at 200.0 °C

200.0 °C

57 GPa

Show Material materials with Elastic modulus of 57 GPa at 250.0 °C

250.0 °C

50 GPa

Show Material materials with Elastic modulus of 50 GPa at 300.0 °C

300.0 °C

Unlock all property charts

Elongation

3 %

Show Material materials with Elongation of 3 % at 23.0 °C

23.0 °C

Elongation A100

3 %

Show Material materials with Elongation A100 of 3 % at 20.0 °C

20.0 °C

Elongation A50

2 %

Show Material materials with Elongation A50 of 2 % at 20.0 °C

20.0 °C

according to EN 485-2

2 %

Show Material materials with Elongation A50 of 2 % at 23.0 °C

23.0 °C

according to EN 485-2

Unlock all property charts

Elongation A50, transverse

2 %

Show Material materials with Elongation A50, transverse of 2 % at 20.0 °C

20.0 °C

Hardness, Brinell

40 [-]

Show Material materials with Hardness, Brinell of 40 [-] at 20.0 °C

20.0 °C

40 [-]

Show Material materials with Hardness, Brinell of 40 [-] at 23.0 °C

23.0 °C

Unlock all property charts

Hardness, HBW

40 [-]

Show Material materials with Hardness, HBW of 40 [-] at 23.0 °C

23.0 °C

according to EN 485-2

Plane-Strain Fracture Toughnes

22 - 35 MPa·√m

Show Material materials with Plane-Strain Fracture Toughnes of 22 - 35 MPa·√m at 23.0 °C

23.0 °C

Typical for Wrought 1000 Series Aluminium

Poisson's ratio

0.33 [-]

Show Material materials with Poisson's ratio of 0.33 [-] at 23.0 °C

23.0 °C

Typical for Wrought 1000 Series Aluminium

Shear modulus

25 GPa

Show Material materials with Shear modulus of 25 GPa at 20.0 °C

20.0 °C

26.5 GPa

Show Material materials with Shear modulus of 26.5 GPa at 23.0 °C

23.0 °C

Unlock all property charts

Tensile strength

120 - 125 MPa

Show Material materials with Tensile strength of 120 - 125 MPa at 20.0 °C

20.0 °C

according to EN 485-2

120 - 125 MPa

Show Material materials with Tensile strength of 120 - 125 MPa at 23.0 °C

23.0 °C

according to EN 485-2

Unlock all property charts

Tensile strength, transverse

125 MPa

Show Material materials with Tensile strength, transverse of 125 MPa at 20.0 °C

20.0 °C

Yield strength

105 MPa

Show Material materials with Yield strength of 105 MPa at 23.0 °C

23.0 °C

according to EN 485-2

Yield strength Rp0.2

105 - 115 MPa

Show Material materials with Yield strength Rp0.2 of 105 - 115 MPa at 20.0 °C

20.0 °C

105 - 115 MPa

Show Material materials with Yield strength Rp0.2 of 105 - 115 MPa at 23.0 °C

23.0 °C

Unlock all property charts

Yield strength Rp0.2, transverse

105 MPa

Show Material materials with Yield strength Rp0.2, transverse of 105 MPa at 20.0 °C

20.0 °C

Thermal

PropertyValueTemperatureComment

Coefficient of thermal expansion

2.35E-5 1/K

Show Material materials with Coefficient of thermal expansion of 2.35E-5 1/K at 20.0 °C

20.0 °C

20-100°C

2.3E-5 - 2.35E-5 1/K

Show Material materials with Coefficient of thermal expansion of 2.3E-5 - 2.35E-5 1/K at 100.0 °C

100.0 °C

20-100°C

Unlock all property charts

Melting point

659 °C

Show Material materials with Melting point of 659 °C

Specific heat capacity

921 J/(kg·K)

Show Material materials with Specific heat capacity of 921 J/(kg·K) at 20.0 °C

20.0 °C

Thermal conductivity

215 W/(m·K)

Show Material materials with Thermal conductivity of 215 W/(m·K) at 20.0 °C

20.0 °C

138 - 225 W/(m·K)

Show Material materials with Thermal conductivity of 138 - 225 W/(m·K) at 23.0 °C

23.0 °C

Unlock all property charts

Electrical

PropertyValueTemperature

Electrical conductivity

3.64E+7 - 3.70E+7 S/m

Show Material materials with Electrical conductivity of 3.64E+7 - 3.70E+7 S/m at 20.0 °C

20.0 °C

3.45E+7 - 3.50E+7 S/m

Show Material materials with Electrical conductivity of 3.45E+7 - 3.50E+7 S/m at 23.0 °C

23.0 °C

Unlock all property charts

Electrical resistivity

2.86E-8 - 4.9E-8 Ω·m

Show Material materials with Electrical resistivity of 2.86E-8 - 4.9E-8 Ω·m at 23.0 °C

23.0 °C

Chemical properties

Property

Aluminium

99.8 %

Copper

0.03 %

Gallium

0.03 %

Iron

0.15 %

Magnesium

0.02 %

Manganese

0.02 %

Other

0.02 %

each 0.02,Min.

Silicon

0.15 %

Titanium

0.02 %

Zinc

0.06 %

Technological properties

Property
Anodizing

decorative: very good, Protective: very good

Application areas

Facades: Single sheet, Sheets for composites/ sandwich Panels, Sheets for mechanized panels; Roofing: Single sheet, Sheets for composites/ sandwich Panels, Foil for bituminous coating; Doors: Sheets for composites/ sandwich Panels, Sheets for mechanized panels; Sun Protection Systems: Single sheet (covering, sun breakers and gutters); Interiors and ceilings: Single sheet, Sheets for composites/ sandwich Panels, Sheets for mechanized panels, Decoration; Furniture, Plinths, Blinds: Single sheet, Intermediate transformation/interior use; Lighting: Anodizing Quality, Lacquering quality; Electronic devices: Housing of devices; Tubes: Industrial tubes, Flexible tube, Pipes; Insulation; Solar: Solar collectors, Photovoltaic panels; Wind energy: Nacelle coverings, Rotor, Hub, Stairs; Cosmetics: Cosmetic pieces; Automotive trim: Interior trim, Windows frame, Marque badges

Brazing

hard brazing (with flux/ without flux): very good / very good, friction soldering: very good, soft brazing with flux: very good

Corrosion properties

Excellent

Welding

Excellent

Workability

Bending / Spinning (cold): very good / very good, Impact extrusion (cold): very good, Deep drawing / upsetting (Condition) very good (H14) / very good (H12)