EN 573-3 Grade AW-5052 H16

Want to keep this datasheet? Save it now in your required format

Description

Material EN AW-Al Mg2,5 is produced for sheet metals, strip and plates, for extruded and drawn components, for wire and prewire for mechanical applications, as well as for prematerial for cans, caps and stoppers. The material is food-safe and is used for HF-welded tubes. To the comparable mark AlMg2,5, material No. 3.3523 acc. to DIN 1725-1 : 1983-02 applies: The alloy has a high resistance to corrosion, seawater and salted atmosphere. Strength increases and cold workability decreases according to the Mg-content. It is naturally hard, i.e. a strength increase can only be achieved by cold forming, not by controlled heat treatment. It is well brightenable and anodizable. Machinability and weldability are enhanced by increasing Mg-content. The material is used for staticly not overly loaded components. The weldability is enhanced due to the available Mg-content (>=2,5 %), but the extrusion is more complicated. Application: in packaging industry for tear open lids, stopper of all kind, beverage cans. For transport container , for signs (esp. in traffic), in construction trade for load-carrying constructions, for shutter, roll-up doors, for roofs and facade lining. In apparatus engineering for tanks (tanks for temp. up to 250°C) and pipelines, in vehicle manufacturing for coachbuilding, in aircraft construction for tanks, Honeycomb-constructions and tubes as well as for connecting elements (blind rivets, clinch nuts). Material comparison for US grades (sequel to the material recoding): 5052: ASTM B 275, ASTM B 404, ASTM B 548, ASTM B 745, ASTM B 746, ASTM B 864, ASTM F 626, ASTM F 782, ASTM F 993 UNS A 95052: AMS 4114, AMS 4178, AMS 4348, AMS-A-81596, AMS-QQ-A-225/7, AMS-QQ-A-250/8, MIL-G-18014

Related Standards

Equivalent Materials

This material data has been provided by WIAM,AluKey,Aludium.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Properties

General

Property	Value	Temperature
Density	2.68 - 2.69 g/cm³ Show Material materials with Density of 2.68 - 2.69 g/cm³ at 20.0 °C	20.0 °C
	2.68 g/cm³ Show Material materials with Density of 2.68 g/cm³ at 23.0 °C	23.0 °C

Dimension

Property	Value
Thickness	0.2 - 6 mm Show Material materials with Thickness of 0.2 - 6 mm

Mechanical

Property	Value	Temperature	Comment
Bending Fatigue Strength	125 MPa Show Material materials with Bending Fatigue Strength of 125 MPa at 23.0 °C	23.0 °C
Elastic modulus	70 GPa Show Material materials with Elastic modulus of 70 GPa at 20.0 °C	20.0 °C
	70 GPa Show Material materials with Elastic modulus of 70 GPa at 23.0 °C	23.0 °C
	Unlock all property charts
Elongation	3 % Show Material materials with Elongation of 3 % at 20.0 °C	20.0 °C
Elongation A100	3 % Show Material materials with Elongation A100 of 3 % at 23.0 °C	23.0 °C
Elongation A50	2 - 6 % Show Material materials with Elongation A50 of 2 - 6 % at 20.0 °C	20.0 °C
	2 - 3 % Show Material materials with Elongation A50 of 2 - 3 % at 23.0 °C	23.0 °C
	Unlock all property charts
Elongation A50, transverse	2 - 3 % Show Material materials with Elongation A50, transverse of 2 - 3 % at 20.0 °C	20.0 °C
Hardness, Brinell	73 - 76 [-] Show Material materials with Hardness, Brinell of 73 - 76 [-] at 20.0 °C	20.0 °C
	76 [-] Show Material materials with Hardness, Brinell of 76 [-] at 23.0 °C	23.0 °C
	Unlock all property charts
Hardness, HBW	76 [-] Show Material materials with Hardness, HBW of 76 [-] at 23.0 °C	23.0 °C
Plane-Strain Fracture Toughnes	22 - 35 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22 - 35 MPa·√m at 23.0 °C	23.0 °C	Typical for Wrought 5000 Series Aluminium
Poisson's ratio	0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] at 20.0 °C	20.0 °C
Shear modulus	26.3 - 27 GPa Show Material materials with Shear modulus of 26.3 - 27 GPa at 20.0 °C	20.0 °C
	26.3 - 26.5 GPa Show Material materials with Shear modulus of 26.3 - 26.5 GPa at 23.0 °C	23.0 °C
	Unlock all property charts
Tensile strength	240 - 300 MPa Show Material materials with Tensile strength of 240 - 300 MPa at 20.0 °C	20.0 °C
	250 - 300 MPa Show Material materials with Tensile strength of 250 - 300 MPa at 23.0 °C	23.0 °C
	Unlock all property charts
Tensile strength, transverse	250 - 300 MPa Show Material materials with Tensile strength, transverse of 250 - 300 MPa at 20.0 °C	20.0 °C
Yield strength	210 MPa Show Material materials with Yield strength of 210 MPa at 23.0 °C	23.0 °C
Yield strength Rp0.2	190 - 270 MPa Show Material materials with Yield strength Rp0.2 of 190 - 270 MPa at 20.0 °C	20.0 °C
	200 - 270 MPa Show Material materials with Yield strength Rp0.2 of 200 - 270 MPa at 23.0 °C	23.0 °C
	Unlock all property charts
Yield strength Rp0.2, transverse	210 MPa Show Material materials with Yield strength Rp0.2, transverse of 210 MPa at 20.0 °C	20.0 °C

Thermal

Property	Value	Temperature	Comment
Coefficient of thermal expansion	2.21E-5 1/K Show Material materials with Coefficient of thermal expansion of 2.21E-5 1/K at -50.0 °C	-50.0 °C	20-100°C
	2.21E-5 - 2.57E-5 1/K Show Material materials with Coefficient of thermal expansion of 2.21E-5 - 2.57E-5 1/K at 20.0 °C	20.0 °C	20-100°C
	2.38E-5 - 2.4E-5 1/K Show Material materials with Coefficient of thermal expansion of 2.38E-5 - 2.4E-5 1/K at 100.0 °C	100.0 °C	20-100°C
	2.48E-5 1/K Show Material materials with Coefficient of thermal expansion of 2.48E-5 1/K at 200.0 °C	200.0 °C	20-100°C
	2.57E-5 1/K Show Material materials with Coefficient of thermal expansion of 2.57E-5 1/K at 300.0 °C	300.0 °C	20-100°C
	Unlock all property charts
Max service temperature	150 °C Show Material materials with Max service temperature of 150 °C		Typical for Wrought 5000 Series Aluminium
Melting point	605 - 650 °C Show Material materials with Melting point of 605 - 650 °C
Specific heat capacity	900 - 901 J/(kg·K) Show Material materials with Specific heat capacity of 900 - 901 J/(kg·K) at 20.0 °C	20.0 °C
	900 J/(kg·K) Show Material materials with Specific heat capacity of 900 J/(kg·K) at 23.0 °C	23.0 °C
	Unlock all property charts
Thermal conductivity	130 - 150 W/(m·K) Show Material materials with Thermal conductivity of 130 - 150 W/(m·K) at 20.0 °C	20.0 °C
	130 - 150 W/(m·K) Show Material materials with Thermal conductivity of 130 - 150 W/(m·K) at 23.0 °C	23.0 °C
	Unlock all property charts

Electrical

Property	Value	Temperature
Electrical conductivity	1.90E+7 - 2.10E+7 S/m Show Material materials with Electrical conductivity of 1.90E+7 - 2.10E+7 S/m at 20.0 °C	20.0 °C
	1.90E+7 - 2.10E+7 S/m Show Material materials with Electrical conductivity of 1.90E+7 - 2.10E+7 S/m at 23.0 °C	23.0 °C
	Unlock all property charts
Electrical resistivity	4.7E-8 - 5.2E-8 Ω·m Show Material materials with Electrical resistivity of 4.7E-8 - 5.2E-8 Ω·m at 20.0 °C	20.0 °C
	4.76E-8 - 5.26E-8 Ω·m Show Material materials with Electrical resistivity of 4.76E-8 - 5.26E-8 Ω·m at 23.0 °C	23.0 °C
	Unlock all property charts

Chemical properties

Property
Chromium	0.15 - 0.35 %
Copper	0.1 %
Iron	0.4 %
Magnesium	2.2 - 2.8 %
Manganese	0.1 %
Other	0.15 %	each 0.05, total 0.15, Rest Al
Silicon	0.25 %
Zinc	0.1 %

Technological properties

Property
Anodizing	decorative: good, Protective: very good
Application areas	Facades: Single sheet, Sheets for composites/ sandwich Panels, Sheets for mechanized panels; Doors: Sheets for composites/ sandwich Panels, Sheets for mechanized panels; Interiors and ceilings: Single sheet, Sheets for composites/ sandwich Panels, Sheets for mechanized panels; Furniture, Plinths, Blinds: Single sheet, Intermediate transformation/interior use; Anodizing quality; Electronic devices: Housing devices; Closures: Easy open; Food can: Body, Lids; Components: Heat shields, Access hatches, Spoilers, General trasportation
Corrosion properties	Seawater: very good to good, weathering: good
Welding	Very Good
Workability	Bending / Spinning (cold): very good / acceptable, Impact extrusion (cold): acceptable, Deep drawing / upsetting (Condition) good (O) / good (H12)