Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 23.0 °C | 2.68 g/cm³ Show Material materials with Density of 2.68 g/cm³ |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Bending angle 90° | 23.0 °C | 1.5 - 2 °/t Show Material materials with Bending angle 90° of 1.5 - 2 °/t | |
Elastic modulus | 23.0 °C | 70 GPa Show Material materials with Elastic modulus of 70 GPa | |
Elongation A100 | 23.0 °C | 10 % Show Material materials with Elongation A100 of 10 % | |
Elongation A50 | 23.0 °C | 4 - 9 % Show Material materials with Elongation A50 of 4 - 9 % | |
Plane-Strain Fracture Toughnes | 23.0 °C | 22 - 35 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22 - 35 MPa·√m | Typical for Wrought 5000 Series Aluminium |
Poisson's ratio | 23.0 °C | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 5000 Series Aluminium |
Shear modulus | 23.0 °C | 26.3 GPa Show Material materials with Shear modulus of 26.3 GPa | |
Tensile strength | 23.0 °C | 210 - 270 MPa Show Material materials with Tensile strength of 210 - 270 MPa | |
Yield strength Rp0.2 | 23.0 °C | 130 MPa Show Material materials with Yield strength Rp0.2 of 130 MPa |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | -50.0 °C | 2.21E-5 1/K Show Material materials with Coefficient of thermal expansion of 2.21E-5 1/K | |
20.0 °C | 2.21E-5 - 2.57E-5 1/K Show Material materials with Coefficient of thermal expansion of 2.21E-5 - 2.57E-5 1/K | ||
100.0 °C | 2.38E-5 1/K Show Material materials with Coefficient of thermal expansion of 2.38E-5 1/K | ||
200.0 °C | 2.48E-5 1/K Show Material materials with Coefficient of thermal expansion of 2.48E-5 1/K | ||
300.0 °C | 2.57E-5 1/K Show Material materials with Coefficient of thermal expansion of 2.57E-5 1/K | ||
Max service temperature | 150 °C Show Material materials with Max service temperature of 150 °C | Typical for Wrought 5000 Series Aluminium | |
Melting point | 605 - 650 °C Show Material materials with Melting point of 605 - 650 °C | ||
Specific heat capacity | 23.0 °C | 900 J/(kg·K) Show Material materials with Specific heat capacity of 900 J/(kg·K) | |
Thermal conductivity | 23.0 °C | 130 - 150 W/(m·K) Show Material materials with Thermal conductivity of 130 - 150 W/(m·K) | |
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical conductivity | 23.0 °C | 1.90E+7 - 2.10E+7 S/m Show Material materials with Electrical conductivity of 1.90E+7 - 2.10E+7 S/m |
Electrical resistivity | 23.0 °C | 4.76E-8 - 5.26E-8 Ω·m Show Material materials with Electrical resistivity of 4.76E-8 - 5.26E-8 Ω·m |
Chemical properties
| Property | Value |
|---|---|
Chromium | 0.15 - 0.35 % Show Material materials with Chromium of 0.15 - 0.35 % |
Copper | 0.1 % Show Material materials with Copper of 0.1 % |
Iron | 0.4 % Show Material materials with Iron of 0.4 % |
Magnesium | 2.2 - 2.8 % Show Material materials with Magnesium of 2.2 - 2.8 % |
Manganese | 0.1 % Show Material materials with Manganese of 0.1 % |
Other | each 0.05, total 0.15, Rest Al |
Silicon | 0.25 % Show Material materials with Silicon of 0.25 % |
Zinc | 0.1 % Show Material materials with Zinc of 0.1 % |
Technological properties
| Property | ||
|---|---|---|
| Anodizing | decorative: good, Protective: very good | |
| Corrosion properties | Seawater: very good to good, weathering: good | |
| Workability | Bending / Spinning (cold): very good / acceptable, Impact extrusion (cold): acceptable, Deep drawing / upsetting (Condition) good (O) / good (H12) | |