AA Standards Grade 5056 H32

Want to keep this datasheet? Save it now in your required format

Related Standards

Equivalent Materials

This material data has been provided by AluKey.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueConditionRelated Standards

Density

2.64 g/cm³

Show Material materials with Density of 2.64 g/cm³

H32

AA Standards, ASTM B211, ASTM B316

Mechanical

PropertyValueConditionRelated StandardsComment

Elastic modulus

71.0 GPa

Show Material materials with Elastic modulus of 71.0 GPa

H32

AA Standards, ASTM B211, ASTM B316

Unlock all property charts

Plane-Strain Fracture Toughnes

22.0 - 35.0 MPa·√m

Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m

Typical for Wrought 5000 Series Aluminium

Unlock all property charts

Poisson's ratio

0.33 [-]

Show Material materials with Poisson's ratio of 0.33 [-]

Typical for Wrought 5000 Series Aluminium

Unlock all property charts

Shear modulus

26.0 - 26.5 GPa

Show Material materials with Shear modulus of 26.0 - 26.5 GPa

Typical for Wrought 5000 Series Aluminium

Unlock all property charts

Tensile strength

300.0 MPa

Show Material materials with Tensile strength of 300.0 MPa

H32

AA Standards, ASTM B211

300.0 - 360.0 MPa

Show Material materials with Tensile strength of 300.0 - 360.0 MPa

H32

AA Standards, ASTM B316

Unlock all property charts

Thermal

PropertyTemperatureValueConditionRelated StandardsComment

Coefficient of thermal expansion

100 °C, 20 °C

2.41e-05 1/K

Show Material materials with Coefficient of thermal expansion of 2.41e-05 1/K

H32

AA Standards, ASTM B211, ASTM B316

Unlock all property charts

Max service temperature

150.0 °C

Show Material materials with Max service temperature of 150.0 °C

Typical for Wrought 5000 Series Aluminium

Melting point

565.0 - 640.0 °C

Show Material materials with Melting point of 565.0 - 640.0 °C

H32

AA Standards, ASTM B211, ASTM B316

Specific heat capacity

879.0 - 963.0 J/(kg·K)

Show Material materials with Specific heat capacity of 879.0 - 963.0 J/(kg·K)

Typical for Wrought 5000 Series Aluminium

Unlock all property charts

Thermal conductivity

109.0 - 117.0 W/(m·K)

Show Material materials with Thermal conductivity of 109.0 - 117.0 W/(m·K)

H32

AA Standards, ASTM B211, ASTM B316

Unlock all property charts

Electrical

PropertyValueConditionRelated Standards

Electrical conductivity

16000000.0 - 17000000.0 S/m

Show Material materials with Electrical conductivity of 16000000.0 - 17000000.0 S/m

H32

AA Standards, ASTM B211, ASTM B316

Unlock all property charts

Electrical resistivity

5.88e-08 - 6.25e-08 Ω·m

Show Material materials with Electrical resistivity of 5.88e-08 - 6.25e-08 Ω·m

H32

AA Standards, ASTM B211, ASTM B316

Unlock all property charts

Chemical properties

PropertyValueConditionRelated Standards

Chromium

0.05 - 0.2 %

Show Material materials with Chromium of 0.05 - 0.2 %

H32

AA Standards, ASTM B211, ASTM B316

Copper

0.1 %

Show Material materials with Copper of 0.1 %

H32

AA Standards, ASTM B211, ASTM B316

Iron

0.40 %

Show Material materials with Iron of 0.40 %

H32

AA Standards, ASTM B211, ASTM B316

Magnesium

4.5 - 5.6 %

Show Material materials with Magnesium of 4.5 - 5.6 %

H32

AA Standards, ASTM B211, ASTM B316

Manganese

0.05 - 0.2 %

Show Material materials with Manganese of 0.05 - 0.2 %

H32

AA Standards, ASTM B211, ASTM B316

Other

each 0.05, total 0.15, Rest Al

Silicon

0.3 %

Show Material materials with Silicon of 0.3 %

H32

AA Standards, ASTM B211, ASTM B316

Zinc

0.1 %

Show Material materials with Zinc of 0.1 %

H32

AA Standards, ASTM B211, ASTM B316

Technological properties

Property
Brazing

general: no brazing is known or developed

Corrosion properties

Stress corrosion cracking: kein Schadensfall im Betrieb, eingeschränkte Schäden bei den Labortests (O, H111, H12, H32, H14, H34), c (H18, H38), d (H192, H392), general: sehr gut, ohne Schutz in industrieller oder Seewasser-Atmosphäre (O, H111, H12, H32, H14, H34, H18, H38), b (H192, H392)

General machinability

General: poor (O, H111, H12, H32), sufficient (H14, H34, H18, H38), good to acceptable (H192, H392)

Workability

general (condition): good (O, H111), acceptable (H12, H32, H14, H34), poor(H18, H38), d (H192, H392)