Properties
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Density | 2.64 g/cm³ Show Material materials with Density of 2.64 g/cm³ | H38 | AA Standards, ASTM B211 |
Mechanical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Bending Fatigue Strength | 150.0 MPa Show Material materials with Bending Fatigue Strength of 150.0 MPa | H38 | AA Standards | |
Elastic modulus | 71.0 GPa Show Material materials with Elastic modulus of 71.0 GPa | H38 | AA Standards, ASTM B211 | |
Hardness, Brinell | 100.0 [-] Show Material materials with Hardness, Brinell of 100.0 [-] | H38 | AA Standards | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 5000 Series Aluminium | ||
Shear modulus | 26.0 - 26.5 GPa Show Material materials with Shear modulus of 26.0 - 26.5 GPa | Typical for Wrought 5000 Series Aluminium | ||
Tensile strength | 380.0 MPa Show Material materials with Tensile strength of 380.0 MPa | H38 | AA Standards, ASTM B211 | |
415.0 MPa Show Material materials with Tensile strength of 415.0 MPa | H38 | AA Standards |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.41e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.41e-05 1/K | H38 | AA Standards, ASTM B211 | |
100 °C | 2.41e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.41e-05 1/K | H38 | AA Standards, ASTM B211 | ||
Max service temperature | 150.0 °C Show Material materials with Max service temperature of 150.0 °C | Typical for Wrought 5000 Series Aluminium | |||
Melting point | 565.0 - 640.0 °C Show Material materials with Melting point of 565.0 - 640.0 °C | H38 | AA Standards, ASTM B211 | ||
Specific heat capacity | 879.0 - 963.0 J/(kg·K) Show Material materials with Specific heat capacity of 879.0 - 963.0 J/(kg·K) | Typical for Wrought 5000 Series Aluminium | |||
Thermal conductivity | 109.0 - 117.0 W/(m·K) Show Material materials with Thermal conductivity of 109.0 - 117.0 W/(m·K) | H38 | AA Standards, ASTM B211 | ||
Electrical
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Electrical conductivity | 16000000.0 - 17000000.0 S/m Show Material materials with Electrical conductivity of 16000000.0 - 17000000.0 S/m | H38 | AA Standards, ASTM B211 |
Electrical resistivity | 5.88e-08 - 6.25e-08 Ω·m Show Material materials with Electrical resistivity of 5.88e-08 - 6.25e-08 Ω·m | H38 | AA Standards, ASTM B211 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Chromium | 0.05 - 0.2 % Show Material materials with Chromium of 0.05 - 0.2 % | H38 | AA Standards, ASTM B211 |
Copper | 0.1 % Show Material materials with Copper of 0.1 % | H38 | AA Standards, ASTM B211 |
Iron | 0.40 % Show Material materials with Iron of 0.40 % | H38 | AA Standards, ASTM B211 |
Magnesium | 4.5 - 5.6 % Show Material materials with Magnesium of 4.5 - 5.6 % | H38 | AA Standards, ASTM B211 |
Manganese | 0.05 - 0.2 % Show Material materials with Manganese of 0.05 - 0.2 % | H38 | AA Standards, ASTM B211 |
Silicon | 0.3 % Show Material materials with Silicon of 0.3 % | H38 | AA Standards, ASTM B211 |
Zinc | 0.1 % Show Material materials with Zinc of 0.1 % | H38 | AA Standards, ASTM B211 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: no brazing is known or developed | |
| Corrosion properties | Stress corrosion cracking: kein Schadensfall im Betrieb, eingeschränkte Schäden bei den Labortests (O, H111, H12, H32, H14, H34), c (H18, H38), d (H192, H392), general: sehr gut, ohne Schutz in industrieller oder Seewasser-Atmosphäre (O, H111, H12, H32, H14, H34, H18, H38), b (H192, H392) | |
| General machinability | General: poor (O, H111, H12, H32), sufficient (H14, H34, H18, H38), good to acceptable (H192, H392) | |
| Workability | general (condition): good (O, H111), acceptable (H12, H32, H14, H34), poor(H18, H38), d (H192, H392) | |