Properties
General
| Property | Value | Comment |
|---|---|---|
Density | 2.65 - 2.7 g/cm³ Show Material materials with Density of 2.65 - 2.7 g/cm³ | Typical for Wrought 5000 Series Aluminium |
Mechanical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Elastic modulus | 69.0 - 70.0 GPa Show Material materials with Elastic modulus of 69.0 - 70.0 GPa | Typical for Wrought 5000 Series Aluminium | ||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 5000 Series Aluminium | ||
Shear modulus | 26.0 - 26.5 GPa Show Material materials with Shear modulus of 26.0 - 26.5 GPa | Typical for Wrought 5000 Series Aluminium | ||
Tensile strength | 270.0 MPa Show Material materials with Tensile strength of 270.0 MPa | H111 | AA Standards, ASTM B247 | |
275.0 MPa Show Material materials with Tensile strength of 275.0 MPa | H111 | AA Standards, ASTM B221, ASTM B241, ASTM B345 | ||
290.0 MPa Show Material materials with Tensile strength of 290.0 MPa | H111 | AA Standards, ASTM B247 |
Thermal
| Property | Value | Comment |
|---|---|---|
Coefficient of thermal expansion | 2.2e-05 - 2.5e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.2e-05 - 2.5e-05 1/K | Typical for Wrought 5000 Series Aluminium |
Max service temperature | 150.0 °C Show Material materials with Max service temperature of 150.0 °C | Typical for Wrought 5000 Series Aluminium |
Melting point | 560.0 - 655.0 °C Show Material materials with Melting point of 560.0 - 655.0 °C | Typical for Wrought 5000 Series Aluminium |
Specific heat capacity | 879.0 - 963.0 J/(kg·K) Show Material materials with Specific heat capacity of 879.0 - 963.0 J/(kg·K) | Typical for Wrought 5000 Series Aluminium |
Thermal conductivity | 112.0 - 205.0 W/(m·K) Show Material materials with Thermal conductivity of 112.0 - 205.0 W/(m·K) | Typical for Wrought 5000 Series Aluminium |
Electrical
| Property | Value | Comment |
|---|---|---|
Electrical conductivity | 18000000.0 - 31000000.0 S/m Show Material materials with Electrical conductivity of 18000000.0 - 31000000.0 S/m | Typical for Wrought 5000 Series Aluminium |
Electrical resistivity | 3.3e-08 - 5e-08 Ω·m Show Material materials with Electrical resistivity of 3.3e-08 - 5e-08 Ω·m | Typical for Wrought 5000 Series Aluminium |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Chromium | 0.05 - 0.25 % Show Material materials with Chromium of 0.05 - 0.25 % | H111 | AA Standards, ASTM B221, ASTM B241, ASTM B247, ASTM B345 |
Copper | 0.1 % Show Material materials with Copper of 0.1 % | H111 | AA Standards, ASTM B221, ASTM B241, ASTM B247, ASTM B345 |
Iron | 0.40 % Show Material materials with Iron of 0.40 % | H111 | AA Standards, ASTM B221, ASTM B241, ASTM B247, ASTM B345 |
Magnesium | 4.0 - 4.9 % Show Material materials with Magnesium of 4.0 - 4.9 % | H111 | AA Standards, ASTM B221, ASTM B241, ASTM B247, ASTM B345 |
Manganese | 0.4 - 1.0 % Show Material materials with Manganese of 0.4 - 1.0 % | H111 | AA Standards, ASTM B221, ASTM B241, ASTM B247, ASTM B345 |
Silicon | 0.4 % Show Material materials with Silicon of 0.4 % | H111 | AA Standards, ASTM B221, ASTM B241, ASTM B247, ASTM B345 |
Titanium | 0.15 % Show Material materials with Titanium of 0.15 % | H111 | AA Standards, ASTM B221, ASTM B241, ASTM B247, ASTM B345 |
Zinc | 0.25 % Show Material materials with Zinc of 0.25 % | H111 | AA Standards, ASTM B221, ASTM B241, ASTM B247, ASTM B345 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: no brazing is known or developed | |
| Corrosion properties | Stress corrosion cracking: kein Schadensfall im Betrieb und bei Labortests (O, H321, H116), kein Schadensfall im Betrieb, eingeschränkte Schäden bei den Labortests (H111), general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: poor | |
| Workability | general (condition): acceptable (O), poor(H321, H116, H111) | |