General
Mechanical
Property | Value | Temperature | Comment |
---|---|---|---|
Elastic modulus | 70 GPa Show Material materials with Elastic modulus of 70 GPa at -270.0 °C | -270.0 °C | |
70 - 72 GPa Show Material materials with Elastic modulus of 70 - 72 GPa at 20.0 °C | 20.0 °C | ||
70 GPa Show Material materials with Elastic modulus of 70 GPa at 23.0 °C | 23.0 °C | ||
69 GPa Show Material materials with Elastic modulus of 69 GPa at 50.0 °C | 50.0 °C | ||
68 GPa Show Material materials with Elastic modulus of 68 GPa at 100.0 °C | 100.0 °C | ||
66 GPa Show Material materials with Elastic modulus of 66 GPa at 150.0 °C | 150.0 °C | ||
63 GPa Show Material materials with Elastic modulus of 63 GPa at 200.0 °C | 200.0 °C | ||
57 GPa Show Material materials with Elastic modulus of 57 GPa at 250.0 °C | 250.0 °C | ||
50 GPa Show Material materials with Elastic modulus of 50 GPa at 300.0 °C | 300.0 °C | ||
Elongation | 2 % Show Material materials with Elongation of 2 % at 23.0 °C | 23.0 °C | |
Elongation A100 | 2 % Show Material materials with Elongation A100 of 2 % at 20.0 °C | 20.0 °C | |
Plane-Strain Fracture Toughnes | 22 - 35 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22 - 35 MPa·√m at 23.0 °C | 23.0 °C | Typical for Wrought 1000 Series Aluminium |
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] at 23.0 °C | 23.0 °C | Typical for Wrought 1000 Series Aluminium |
Shear modulus | 25 - 26.5 GPa Show Material materials with Shear modulus of 25 - 26.5 GPa at 20.0 °C | 20.0 °C | |
Tensile strength | 115 MPa Show Material materials with Tensile strength of 115 MPa at 20.0 °C | 20.0 °C | |
115 MPa Show Material materials with Tensile strength of 115 MPa at 23.0 °C | 23.0 °C | ||
Yield strength Rp0.2 | 110 MPa Show Material materials with Yield strength Rp0.2 of 110 MPa at 20.0 °C | 20.0 °C | |
110 MPa Show Material materials with Yield strength Rp0.2 of 110 MPa at 23.0 °C | 23.0 °C | ||
Thermal
Property | Value | Temperature |
---|---|---|
Coefficient of thermal expansion | 2.18E-5 1/K Show Material materials with Coefficient of thermal expansion of 2.18E-5 1/K at -50.0 °C | -50.0 °C |
2.18E-5 - 2.55E-5 1/K Show Material materials with Coefficient of thermal expansion of 2.18E-5 - 2.55E-5 1/K at 20.0 °C | 20.0 °C | |
2.35E-5 - 2.36E-5 1/K Show Material materials with Coefficient of thermal expansion of 2.35E-5 - 2.36E-5 1/K at 100.0 °C | 100.0 °C | |
2.45E-5 1/K Show Material materials with Coefficient of thermal expansion of 2.45E-5 1/K at 200.0 °C | 200.0 °C | |
2.55E-5 1/K Show Material materials with Coefficient of thermal expansion of 2.55E-5 1/K at 300.0 °C | 300.0 °C | |
Melting point | 660 °C Show Material materials with Melting point of 660 °C | |
Specific heat capacity | 900 J/(kg·K) Show Material materials with Specific heat capacity of 900 J/(kg·K) at 20.0 °C | 20.0 °C |
900 J/(kg·K) Show Material materials with Specific heat capacity of 900 J/(kg·K) at 23.0 °C | 23.0 °C | |
Thermal conductivity | 215 - 227 W/(m·K) Show Material materials with Thermal conductivity of 215 - 227 W/(m·K) at 20.0 °C | 20.0 °C |
232 W/(m·K) Show Material materials with Thermal conductivity of 232 W/(m·K) at 23.0 °C | 23.0 °C | |
Electrical
Property | Value | Temperature |
---|---|---|
Electrical conductivity | 3.76E+7 - 3.78E+7 S/m Show Material materials with Electrical conductivity of 3.76E+7 - 3.78E+7 S/m at 20.0 °C | 20.0 °C |
3.75E+7 - 3.77E+7 S/m Show Material materials with Electrical conductivity of 3.75E+7 - 3.77E+7 S/m at 23.0 °C | 23.0 °C | |
Electrical resistivity | 2.65E-8 - 2.67E-8 Ω·m Show Material materials with Electrical resistivity of 2.65E-8 - 2.67E-8 Ω·m at 23.0 °C | 23.0 °C |
Chemical properties
Property | ||
---|---|---|
Aluminium | 99.98 % | |
Copper | 3E-3 % | |
Iron | 6E-3 % | |
Other | each 0.003 | |
Silicon | 0.01 % | |
Titanium | 3E-3 % | |
Zinc | 0.02 % |
Technological properties
Property | ||
---|---|---|
Brazing | hard brazing (with flux/ without flux): very good / very good, friction soldering: very good, soft brazing with flux: very good, general: very good | |
Corrosion properties | Seawater: acceptable, weathering: good | |
Workability | Bending / Spinning (cold): very good |