EN 573-3 Grade AW-5086 H14

Want to keep this datasheet? Save it now in your required format

Description

The food-safe material EN AW-Al Mg4,5Mn0,4 is produced for sheet metal, strip and plates, HF-welded tubes, for wire and prewire for mechanical applications and as extruded and drawn components. To the comparable mark AlMg4Mn, material No. 3.4545, acc. to DIN 1725-1 :1983-02 applies: The alloy AlMg4Mn is a naturally hard aluminium forgeable material. A strength increase is achieved only by cold forming not by controlled heat treatment. It has a high corrosion resistance. It is resistant to seawater and salted atmosphere. Increasing Mg- and Mn-content complicates extrusion but strength and low-temperature behaviour enhances. Application: shutters and roll-up gates (sheet metal sections), in apparatus engineering for reservoirs (low-temperature tanks), heat exchanger, air decomposer and pipelines. In vehicle manufacturing for superstructures as well as for bulk and tank vehicles, motor busses, shock absorber, body and safety parts. In shipbuilding for hull, superstructure, radar system.

Related Standards

Equivalent Materials

This material data has been provided by WIAM,Aludium,AluKey.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueTemperature

Density

2.66 - 2.67 g/cm³

Show Material materials with Density of 2.66 - 2.67 g/cm³ at 20.0 °C

20.0 °C

2.66 g/cm³

Show Material materials with Density of 2.66 g/cm³ at 23.0 °C

23.0 °C

Dimension

PropertyValue

Thickness

0.2 - 6 mm

Show Material materials with Thickness of 0.2 - 6 mm

Mechanical

PropertyValueTemperatureComment

Bending Fatigue Strength

135 MPa

Show Material materials with Bending Fatigue Strength of 135 MPa at 23.0 °C

23.0 °C

Elastic modulus

71 GPa

Show Material materials with Elastic modulus of 71 GPa at 20.0 °C

20.0 °C

71 GPa

Show Material materials with Elastic modulus of 71 GPa at 23.0 °C

23.0 °C

Unlock all property charts

Elongation

3 - 7 %

Show Material materials with Elongation of 3 - 7 % at 20.0 °C

20.0 °C

Elongation A100

3 - 7 %

Show Material materials with Elongation A100 of 3 - 7 % at 23.0 °C

23.0 °C

Elongation A50

2 - 4 %

Show Material materials with Elongation A50 of 2 - 4 % at 20.0 °C

20.0 °C

2 - 4 %

Show Material materials with Elongation A50 of 2 - 4 % at 23.0 °C

23.0 °C

Unlock all property charts

Elongation A50, transverse

2 - 4 %

Show Material materials with Elongation A50, transverse of 2 - 4 % at 20.0 °C

20.0 °C

Elongation, transverse

3 %

Show Material materials with Elongation, transverse of 3 % at 20.0 °C

20.0 °C

Hardness, Brinell

90 - 95 [-]

Show Material materials with Hardness, Brinell of 90 - 95 [-] at 20.0 °C

20.0 °C

90 [-]

Show Material materials with Hardness, Brinell of 90 [-] at 23.0 °C

23.0 °C

Unlock all property charts

Hardness, HBW

90 [-]

Show Material materials with Hardness, HBW of 90 [-] at 23.0 °C

23.0 °C

Plane-Strain Fracture Toughnes

22 - 35 MPa·√m

Show Material materials with Plane-Strain Fracture Toughnes of 22 - 35 MPa·√m at 23.0 °C

23.0 °C

Typical for Wrought 5000 Series Aluminium

Poisson's ratio

0.33 [-]

Show Material materials with Poisson's ratio of 0.33 [-] at 20.0 °C

20.0 °C

Shear modulus

26.7 - 27 GPa

Show Material materials with Shear modulus of 26.7 - 27 GPa at 20.0 °C

20.0 °C

26.7 - 27 GPa

Show Material materials with Shear modulus of 26.7 - 27 GPa at 23.0 °C

23.0 °C

Unlock all property charts

Tensile strength

295 - 360 MPa

Show Material materials with Tensile strength of 295 - 360 MPa at 20.0 °C

20.0 °C

295 - 360 MPa

Show Material materials with Tensile strength of 295 - 360 MPa at 23.0 °C

23.0 °C

Unlock all property charts

Tensile strength, transverse

300 - 360 MPa

Show Material materials with Tensile strength, transverse of 300 - 360 MPa at 20.0 °C

20.0 °C

Yield strength

240 MPa

Show Material materials with Yield strength of 240 MPa at 23.0 °C

23.0 °C

Yield strength Rp0.2

220 - 240 MPa

Show Material materials with Yield strength Rp0.2 of 220 - 240 MPa at 20.0 °C

20.0 °C

220 - 240 MPa

Show Material materials with Yield strength Rp0.2 of 220 - 240 MPa at 23.0 °C

23.0 °C

Unlock all property charts

Yield strength Rp0.2, transverse

240 MPa

Show Material materials with Yield strength Rp0.2, transverse of 240 MPa at 20.0 °C

20.0 °C

Thermal

PropertyValueTemperatureComment

Coefficient of thermal expansion

2.2E-5 1/K

Show Material materials with Coefficient of thermal expansion of 2.2E-5 1/K at -50.0 °C

-50.0 °C

20-100°C

2.2E-5 - 2.58E-5 1/K

Show Material materials with Coefficient of thermal expansion of 2.2E-5 - 2.58E-5 1/K at 20.0 °C

20.0 °C

20-100°C

2.38E-5 - 2.4E-5 1/K

Show Material materials with Coefficient of thermal expansion of 2.38E-5 - 2.4E-5 1/K at 100.0 °C

100.0 °C

20-100°C

2.47E-5 1/K

Show Material materials with Coefficient of thermal expansion of 2.47E-5 1/K at 200.0 °C

200.0 °C

20-100°C

2.58E-5 1/K

Show Material materials with Coefficient of thermal expansion of 2.58E-5 1/K at 300.0 °C

300.0 °C

20-100°C

Unlock all property charts

Max service temperature

150 °C

Show Material materials with Max service temperature of 150 °C

Typical for Wrought 5000 Series Aluminium

Melting point

585 - 641 °C

Show Material materials with Melting point of 585 - 641 °C

Specific heat capacity

900 J/(kg·K)

Show Material materials with Specific heat capacity of 900 J/(kg·K) at 20.0 °C

20.0 °C

900 J/(kg·K)

Show Material materials with Specific heat capacity of 900 J/(kg·K) at 23.0 °C

23.0 °C

Unlock all property charts

Thermal conductivity

120 - 140 W/(m·K)

Show Material materials with Thermal conductivity of 120 - 140 W/(m·K) at 20.0 °C

20.0 °C

120 - 140 W/(m·K)

Show Material materials with Thermal conductivity of 120 - 140 W/(m·K) at 23.0 °C

23.0 °C

Unlock all property charts

Electrical

PropertyValueTemperature

Electrical conductivity

1.70E+7 - 1.90E+7 S/m

Show Material materials with Electrical conductivity of 1.70E+7 - 1.90E+7 S/m at 20.0 °C

20.0 °C

1.70E+7 - 1.90E+7 S/m

Show Material materials with Electrical conductivity of 1.70E+7 - 1.90E+7 S/m at 23.0 °C

23.0 °C

Unlock all property charts

Electrical resistivity

5.2E-8 - 5.8E-8 Ω·m

Show Material materials with Electrical resistivity of 5.2E-8 - 5.8E-8 Ω·m at 20.0 °C

20.0 °C

5.26E-8 - 5.88E-8 Ω·m

Show Material materials with Electrical resistivity of 5.26E-8 - 5.88E-8 Ω·m at 23.0 °C

23.0 °C

Unlock all property charts

Chemical properties

Property

Chromium

0.05 - 0.25 %

Copper

0.1 %

Iron

0.5 %

Magnesium

3.5 - 4.5 %

Manganese

0.2 - 0.7 %

Other

0.05 - 0.15 %

each 0.05, total 0.15, Rest Al

Silicon

0.4 %

Titanium

0.15 %

Zinc

0.25 %

Technological properties

Property
Anodizing

Excellent (anodizing quality)

Application areas

Vessels: Pressure, Cryogenics; Components: Access hatches, Spoilers, General tranportation

Brazing

hard brazing (with flux/ without flux): poor / sufficient, friction soldering: acceptable, soft brazing with flux: poor

Corrosion properties

Excellent

Welding

Good

Workability

Good (in O temper)